Fireproof flame-retardant plastic flooring and manufacture method thereof

A technology for plastic floor, fire and flame retardant, applied in the fields of plastic floor and its preparation, polyacrylic acid pentabromo, alkene nitrile copolymer 42-56, can solve problems such as poor fire resistance and flame retardancy, and achieve improved flame retardancy, The effect of low smoke production and high oxygen index

Inactive Publication Date: 2018-01-23
JIANGYIN ZHIYUAN AUTOMOBILE DECORATION PARTS CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional plastic floor still has the shortcomings of poor...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof flame-retardant plastic flooring and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A fire-resistant and flame-retardant plastic floor, made of the following raw materials by weight (kg): polyphenylene sulfide 78, vinyl chloride-acrylonitrile copolymer 42, polyacrylate pentabromobenzyl 22, antimony trisulfide 8, hexasil Magnesium acid 10, polyphenylsulfone diphenyl phosphonate 15, methyl pentachlorostearate 13, expandable graphite 10, tris(2,3-dibromopropyl) isocyanurate 4, boric acid tris 7 isooctyl ester, 5 zirconium oxychloride, 9 sodium tungstate, 14 dicyclohexyl phthalate, 8 dioctyl tetrachlorophthalate, 5 chlorinated paraffin, 13 high alumina fine powder.

[0015] A method for preparing a fire-resistant and flame-retardant plastic floor, comprising the following steps:

[0016] (1) Polyphenylene sulfide, vinyl chloride-acrylonitrile copolymer, pentabromobenzyl polyacrylate, polyphenylsulfone diphenyl phosphonate, methyl pentachlorostearate, dicyclohexyl phthalate , Add chlorinated paraffin into the high-speed mixer, mix at 80-90°C for 4-8 minute...

Embodiment 2

[0021] A fire-resistant and flame-retardant plastic floor, made of the following raw materials in weight (kg): polyphenylene sulfide 84, vinyl chloride-acrylonitrile copolymer 50, polyacrylate pentabromobenzyl 27, antimony trisulfide 11, hexasil Magnesium acid 13, polyphenylsulfone diphenyl phosphonate 20, methyl pentachlorostearate 17, expandable graphite 12, tris(2,3-dibromopropyl) isocyanurate 7, boric acid tris Isooctyl ester 10, zirconium oxychloride 8, sodium tungstate 13, dicyclohexyl phthalate 16, dioctyl tetrachlorophthalate 11, chlorinated paraffin 8, high aluminum fine powder 14.

[0022] The preparation method is the same as in Example 1.

Embodiment 3

[0024] A fire-resistant and flame-retardant plastic floor, made of the following raw materials in weight (kg): polyphenylene sulfide 91, vinyl chloride-acrylonitrile copolymer 56, polyacrylate pentabromobenzyl 34, antimony trisulfide 14, hexasil Magnesium acid 15, polyphenylsulfone diphenyl phosphonate 25, methyl pentachlorostearate 19, expandable graphite 15, tris(2,3-dibromopropyl) isocyanurate 9, boric acid tris Isooctyl 13, zirconium oxychloride 10, sodium tungstate 16, dicyclohexyl phthalate 19, dioctyl tetrachlorophthalate 14, chlorinated paraffin 10, high alumina fine powder 17.

[0025] The preparation method is the same as in Example 1.

[0026] The performance test results of the plastic floor made in the above-mentioned Examples 1-3 are shown in the table below.

[0027]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses fireproof flame-retardant plastic flooring and a manufacture method thereof. The fireproof flame-retardant plastic flooring comprises, by weight part, 78-91 of polyphenylene sulfide, 42-56 of vinyl chloride-acrylonitrile copolymer, 22-34 of polypentabromobenzyl acrylate, 8-14 of antimony trisulfide, 10-15 of magnesium hexasilicate, 15-25 of polysulfonyl diphenylene phenylphosphonate, 13-19 of methyl pentachlorooctadecanoate, 10-15 of expandable graphite, 4-9 of tri(2,3-dibromopropyl) isocyanurate, 7-13 of triisooctyl borate, 5-10 of zirconium oxychloride, 9-16 of sodiumtungstate, 14-19 of dicyclohexyl phthalate, 8-14 of tetrachloro dioctyl phthalate, 5-10 of chlorinated paraffin, and 13-17 of high aluminum fine powder. The manufactured plastic flooring is fireproof, is high in oxygen index, low in smoking amount and excellent in flame retardance, has no drop burning, and is greatly improved in safety coefficient.

Description

Background technique [0001] The invention relates to a plastic floor and a preparation method thereof, in particular to a fireproof and flame-retardant plastic floor and a preparation method thereof. Background technique [0002] In modern society, there are more and more varieties of floor decoration materials, from the traditional cement mortar floor to the generally bare terrazzo floor, to floor tiles, granite, and wooden floors, and new materials emerge in endlessly. Among them, the plastic floor is widely used in kindergartens, hotels, hospitals, office buildings, residences, airports, gymnasiums, railway stations and many other fields due to its advantages of small weight, fast construction speed, good appearance quality, various colors, comfortable walking, and anti-skid. . In recent years, with the rapid development of industrial technology and the continuous improvement of people's living standards, the performance requirements of plastic flooring are getting highe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L81/02C08L27/06C08L33/16C08L91/06C08L85/02C08K13/02C08K3/30C08K3/34C08K5/101C08K3/04C08K5/55C08K5/12C08K3/08C08K3/24
Inventor 刘跃清
Owner JIANGYIN ZHIYUAN AUTOMOBILE DECORATION PARTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap