A kind of water-based transparent ancient building wood fireproof coating and preparation method thereof

A technology for fire retardant coatings and ancient buildings, applied in fire retardant coatings, antifouling/underwater coatings, coatings, etc. Good preparation and other issues, to achieve the effect of high productivity, effortless painting, and easy construction and operation

A technology for fire retardant coatings and ancient buildings, applied in fire retardant coatings, antifouling/underwater coatings, coatings, etc. Good preparation and other issues, to achieve the effect of high productivity, effortless painting, and easy construction and operation

CN107652740BActive Publication Date: 2019-08-16NINGBO INST OF TECH ZHEJIANG UNIV ZHEJIANG
2 Cites 0 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based transparent ancient building wood fireproof coating and preparation method thereof
  • A kind of water-based transparent ancient building wood fireproof coating and preparation method thereof
  • A kind of water-based transparent ancient building wood fireproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A water-based transparent ancient building wood fireproof coating, made of the following weighed materials in parts by weight: 10 parts of diammonium hydrogen phosphate, 9 parts of dicyandiamide, 9 parts of ethylene glycol, 72 parts of water, and 2 parts of synergist , 15 parts of ACQ, 1 part of UV-531 anti-aging agent; the synergist is hydroxyethyl cellulose and zinc chloride in parts by weight of 3:1.

[0042] A preparation method of water-based transparent ancient building wood fireproof coating, comprising the following steps:

[0043] 1) Weigh the materials according to the following parts by weight: 10 parts of diammonium hydrogen phosphate, 9 parts of dicyandiamide, 9 parts of ethylene glycol, 72 parts of water, 2 parts of synergist, 15 parts of ACQ, 1 part of UV-531 anti-aging agent Part; Described synergist is hydroxyethyl cellulose and zinc chloride that parts by weight are 3:1;

[0044] 2) React the air blowing agent and the carbonization catalyst at 170°C f...

Embodiment 2

[0048] A water-based transparent ancient building wood fireproof coating is made of the following weighed materials in parts by weight: 4 parts of ammonium dihydrogen phosphate, 6 parts of dicyandiamide, 9 parts of ethylene glycol, 81 parts of water, 30 parts of ACQ, UV- 2 parts of 531 anti-aging agent, 4 parts of synergist; the synergist is hydroxyethyl cellulose and zinc chloride in parts by weight of 5:1.

[0049] A preparation method of water-based transparent ancient building wood fireproof coating, comprising the following steps:

[0050] 1) Weigh the materials according to the following parts by weight: 4 parts of ammonium dihydrogen phosphate, 6 parts of dicyandiamide, 9 parts of ethylene glycol, 81 parts of water, 30 parts of ACQ, 2 parts of UV-531 anti-aging agent, 4 parts of synergist Part; Described synergist is the hydroxyethyl cellulose and zinc chloride that parts by weight are 5:1;

[0051] 2) React the air blowing agent and the carbonization catalyst at 170°C...

Embodiment 3

[0055] A water-based transparent ancient building wood fireproof coating, made of the following weighed materials in parts by weight: 10 parts of ammonium polyphosphate, 9 parts of urea, 9 parts of pentaerythritol, 72 parts of water, 20 parts of ACQ, 1 part of UV-531 anti-aging agent Parts, 2 parts of synergists; Said synergists are hydroxyethyl cellulose and zinc chloride in parts by weight of 4:1.

[0056] A preparation method of water-based transparent ancient building wood fireproof coating, comprising the following steps:

[0057] 1) Weigh materials according to the following parts by weight: 10 parts of ammonium polyphosphate, 9 parts of urea, 9 parts of pentaerythritol, 72 parts of water, 20 parts of ACQ, 1 part of UV-531 anti-aging agent, 2 parts of synergist; Efficacy agent is the hydroxyethyl cellulose and zinc chloride that parts by weight are 4:1;

[0058] 2) React the air blowing agent and the carbonization catalyst at 180°C for 50 minutes, cool to 100°C, add hot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The application of the invention discloses waterborne transparent fireproof coating for ancient building wood, made from, by weight, 3-15 parts of a carbided catalyst, 2-10 parts of a purging agent, 2-10 parts of a carbonizing substance, 15-30 parts of ammoniacal copper quaternary, 1-2 parts of UV-531 antiaging agent, 2-4 parts of a synergist, and 65-93 parts of water; a preparation method of thewaterborne transparent fireproof coating for ancient building wood comprises the steps of 1) weighing; 2) preparing guanidine phosphate crystal; 3) grinding the guanidine phosphate crystal, and dryingin vacuum to obtain guanidine phosphate powder; 4) adding the carbonizing substance, ammoniacal copper quaternary and antiaging agent to the guanidine phosphate powder, adding water, and stirring fordissolving to obtain the coating. The waterborne transparent fireproof coating for ancient building wood can keep excellent fireproof performance in ancient building wood in a severe environment.

Description

technical field [0001] The invention relates to the field of architectural coatings, in particular to a water-based transparent ancient building wood fireproof coating and a preparation method thereof. Background technique [0002] Wood is a combustible material and presents a high fire hazard. Wood fire retardant paint is a special paint that is applied on the surface of wood substrates to reduce the flammability of the wood surface, retard the rapid spread of fire, and improve the fire resistance limit of wood. The buildings of traditional wooden structure relics are important historical and cultural heritage, and also the precious wealth of all mankind. However, due to the limitation of historical conditions, the fire prevention infrastructure of wooden structures is weak, and it is extremely easy to be destroyed by fire. It is self-evident that transparent fireproof coatings are ideal for fire protection of ancient buildings. For those ancient buildings that have a str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine