Green glaze for ceramics and preparation method thereof

A green glaze and ceramic technology, applied in the field of ceramic glaze production, can solve the problems of uneven color, not bright enough, and the glaze surface is not bright enough, and achieve the effect of uniform color, bright color and moist glaze.

Inactive Publication Date: 2018-02-06
长沙市峰云陶艺有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramics are widely used in various fields because of their smoothness, compactness and many other advantages. During the preparation of ceramics, various low-temperature colors are often applied to pure black glazes, and black glazes become various beautiful colors. High-profile and elegant ceramic glaze can be obtained, but the glaze surface of green-glazed ceramic handicrafts is not bright enough, the color is not uniform enough, and the color is not bright enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A green glaze for ceramics, comprising 10 parts of albite, 65 parts of glass powder, 8 parts of kaolin, 5 parts of copper oxide, and 12 parts of apple green material.

[0017] A preparation method for ceramic green glaze, the steps are as follows:

[0018] a. Accurately weigh the above components by weight and mix them uniformly to form a mixed solid raw material;

[0019] B, according to mixing solid ball stone: raw material: the ratio of water=2: 1: 0.9 is counted respectively into ball mill mixing ball mill, forms slurry;

[0020] c. After 14-16 hours of ball milling, check the fineness of the slurry;

[0021] d. Sieve the qualified slurry to obtain a green glaze.

[0022] The glaze surface of the green-glazed ceramic handicraft prepared by the invention is moist and bright, and has the advantages of easy dispersion, strong tinting power, bright color, high brightness, uniform color and the like.

Embodiment 2

[0024] A green glaze for ceramics, comprising 12 parts of albite, 63 parts of glass powder, 10 parts of kaolin, 5 parts of copper oxide, and 10 parts of apple green material.

[0025] A preparation method for ceramic green glaze, the steps are as follows:

[0026] a. Accurately weigh the above components by weight and mix them uniformly to form a mixed solid raw material;

[0027] B, according to mixing solid ball stone: raw material: the ratio of water=2: 1: 0.8 is counted respectively into ball mill mixing ball mill, forms slurry;

[0028] c. After 14-16 hours of ball milling, check the fineness of the slurry;

[0029] d. Sieve the qualified slurry to obtain a green glaze.

[0030] The glaze surface of the green-glazed ceramic handicraft prepared by the invention is moist and bright, and has the advantages of easy dispersion, strong tinting power, bright color, high brightness, uniform color and the like.

Embodiment 3

[0032] A green glaze for ceramics, comprising 13 parts of albite, 62 parts of glass powder, 9 parts of kaolin, 5 parts of copper oxide, and 11 parts of apple green material.

[0033] A preparation method for ceramic green glaze, the steps are as follows:

[0034] a. Accurately weigh the above components by weight and mix them uniformly to form a mixed solid raw material;

[0035] B, according to mixing solid ball stone: raw material: the ratio of water=2: 1: 0.8 is counted respectively into ball mill mixing ball mill, forms slurry;

[0036] c. After 14-16 hours of ball milling, check the fineness of the slurry;

[0037] d. Sieve the qualified slurry to obtain a green glaze.

[0038] The glaze surface of the green-glazed ceramic handicraft prepared by the invention is moist and bright, and has the advantages of easy dispersion, strong tinting power, bright color, high brightness, uniform color and luster.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a green glaze for ceramics and a preparation method thereof. According to parts by weight, the composition is: 10-15 parts of albite, 50-65 parts of glass powder, 8-10 parts of kaolin, 3.5-5 parts of copper oxide, apple 8‑12 servings of green ingredients. a. Accurately weigh each component in the above parts by weight and mix them uniformly to form mixed solid raw materials; b. According to the ratio of mixed solid ball stone: raw material: water = 2: 1-1.1: 0.8-0.9, they are respectively included in the ball mill and mixed Ball milling to form a slurry; c. After ball milling for 14-16 hours, detect the fineness of the slurry; d. Sieve the qualified slurry to obtain a green glaze. Compared with the prior art, the preparation and operation of the present invention are simple, and the prepared green-glazed ceramic handicraft has a moist and bright glaze surface, and has the advantages of easy dispersion, strong tinting power, bright color, high brightness, uniform color and luster.

Description

technical field [0001] The invention belongs to the technical field of ceramic glaze production, and in particular relates to a green glaze for ceramics and a preparation method thereof. Background technique [0002] Ceramics are widely used in various fields because of their smoothness, compactness and many other advantages. During the preparation of ceramics, various low-temperature colors are often applied to pure black glazes, and black glazes become various beautiful colors. High-profile and elegant ceramic glaze can be obtained, but the glaze surface of green-glazed ceramic handicrafts is not bright enough, and the color is not uniform enough and not bright. Contents of the invention [0003] The object of the present invention is to provide a kind of scarlet glaze for ceramics and a preparation method thereof in order to solve the problems mentioned in the above-mentioned background technology. [0004] In order to achieve the above object, the technical scheme of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C04B41/86
CPCC03C8/14C04B41/5022C04B41/86
Inventor 文志祥金健康
Owner 长沙市峰云陶艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap