Wind generating set blade core materials and processing method

A technology for wind turbines and blade cores, which is applied to wind engines, wind engines consistent with the wind direction, and wind power generation. It can solve problems such as waste of raw materials, unreasonable slotting structure of core materials, and impact on blade quality and performance. Achieving improved quality and performance and avoiding poor resin wetting

Pending Publication Date: 2018-02-23
GUODIAN UNITED POWER TECH LIANYUNGANG CO LTD
View PDF8 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the groove structure of the core material is unreasonable, and problems such as waste of raw materials, uneven penetration speed, and poor infiltration are likely to occur during the infusion process, which will have a certain impact on the quality and performance of the blade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wind generating set blade core materials and processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1, with reference to figure 1 , a blade core material of a wind power generating set, comprising a core plate 1, a main resin pouring groove is arranged on the front of the core plate, an auxiliary resin pouring groove is arranged on the back of the core plate, and a tiled resin pouring groove is arranged above the auxiliary resin pouring groove on the core plate The anti-overflow layer 6 on the back, the main resin perfusion groove includes several parallel frontal transverse slits 3 and frontal longitudinal slits 2, the frontal transverse slits 3 and the frontal longitudinal slits 2 are intersected, and the secondary resin perfusion grooves It includes a number of rear transverse grooves 4 parallel to the front transverse grooves 3 and rear longitudinal grooves 5 parallel to the front longitudinal grooves 2, and a back transverse groove 5 is provided between any adjacent two front transverse grooves 3. Cutting groove 4, is provided with a rear longitudinal ...

Embodiment 2

[0020] Embodiment 2, in the blade core material of a wind power generating set described in Embodiment 1: the front transverse groove 3 and the front longitudinal groove 2 perpendicularly intersect, and the rear transverse groove 4 and the rear longitudinal groove 5 also correspond to each other. vertical cross.

Embodiment 3

[0021] Embodiment 3, in a wind turbine blade core material described in Embodiment 1 or 2: the front transverse slots 3 and the front longitudinal slots 2 are evenly spaced, and the two adjacent front transverse slots 3 The distance a between them is set to 20-30 mm, and the distance b between two adjacent front longitudinal grooves 2 is set to 20-30 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides wind generating set blade core materials which comprise a core plate, wherein a main resin pouring groove is formed in the front surface of the core plate. An auxiliary resin pouring groove is formed in the back surface of the core plate, an anti-overflow layer which is laid on the back surface of the core plate is arranged above the auxiliary resin pouring groove, and the main resin pouring groove is communicated with the secondary resin pouring groove. The main resin pouring groove and the secondary resin pouring groove are arranged on the front surface and the back surface of the core plate, and gridding cloth is arranged on the back surface of the core plate, so that resin is more uniformly poured in the core plate, the phenomena of poor resin infiltration, resinwaste and the like are reduced, and the quality and the performance of the core materials is improved.

Description

technical field [0001] The invention relates to the field of wind power generation, in particular to a blade core material of a wind power generating set and a processing method thereof. Background technique [0002] Blades are one of the important components of wind turbines. As the blades of wind turbines are getting longer and longer, the weight of the blades is also increasing. In order to ensure that the blades are light in weight and high in performance, the core material of the blades is made of blades. One of the key materials. In the molding process of wind turbine blades, vacuum infusion molding technology is usually used. The structure of the core material has a certain influence on the flow properties of the resin during the infusion process, which is ultimately related to the quality of the blade after molding. Therefore, the groove structure of the core material is unreasonable, and problems such as waste of raw materials, uneven penetration speed, and poor in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/36B29C70/54B26D3/06B32B37/12B32B38/00B32B5/18F03D1/06
CPCF03D1/0675B26D3/06B29C70/36B29C70/54B32B5/18B32B37/12B32B38/0004Y02E10/72Y02P70/10
Inventor 林涛陈露露袁维瀚任拓
Owner GUODIAN UNITED POWER TECH LIANYUNGANG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap