Aluminum alloy shell, machining method thereof and electronic equipment

A technology of aluminum alloy casing and processing method, which is applied in the direction of electrolytic coating, telephone structure, surface reaction electrolytic coating, etc., can solve the problems of poor appearance integrity and achieve the effects of improving reliability, good appearance integrity, and reducing costs

Inactive Publication Date: 2018-02-27
QIKU INTERNET TECH SHENZHEN CO LTD
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] In order to solve the problem of poor appearance integrity of the existing high-gloss edge same-color anodizing process, reduce production costs, and improve product reliability, the invention provides an oxide film with the same oxide film thickness and color as the high-gloss edge and the non-gloss area. Aluminum alloy casing with film properties, processing method thereof, and electronic equipment including the aluminum alloy casing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy shell, machining method thereof and electronic equipment
  • Aluminum alloy shell, machining method thereof and electronic equipment
  • Aluminum alloy shell, machining method thereof and electronic equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] figure 2 A schematic flow chart of the scheme of the aluminum alloy shell processing method in Example 1 is shown.

[0040] The aluminum alloy shell processing method of embodiment 1 comprises:

[0041] In step S100 , the aluminum alloy material is processed to obtain the outer shell and the inner cavity structure. The shape and related internal cavity structure processing of aluminum alloy materials can be processed in sequence, such as CNC processing, surface grinding, and surface sandblasting. The non-high-gloss area has completed the processing that should be completed before anodizing.

[0042] Sand blasting is the process of cleaning the surface of the substrate by the impact of high-speed sand flow. Compressed air is used as the power to form a high-speed jet beam to spray the spray material (such as alumina, diamond, corundum, quartz sand, etc.) to the surface of the workpiece to be treated at a high speed, so that the appearance or shape of the outer surface...

Embodiment 2

[0064] image 3 A schematic structural view of an aluminum alloy housing according to an embodiment of the present invention is shown. The aluminum alloy shell of the embodiment 2 uses the above-mentioned processing method to obtain an oxide film on the high-gloss side and an oxide film on the non-gloss area through one anodic oxidation process on the aluminum alloy substrate 300 .

[0065] Due to the oxide film on the high-gloss side (including image 3 The second undyed layer 330 and the second dyed layer 340) and the oxide film in the non-high light area (including image 3 The first undyed layer 310 and the first dyed layer 320) are obtained by anodizing at the same time, so they have the same oxide film thickness, color and film properties, and there is no white line that ordinary high-gloss same-color anodizing has, Therefore, the appearance integrity of the highlight edge and the non-highlight area is very good.

[0066] Moreover, the present invention does not need ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum alloy shell, a machining method thereof and electronic equipment. The machining method of the aluminum alloy shell comprises the steps that the shape and an inner cavity structure of an aluminum alloy material are machined, so that a shell workpiece is obtained; protective film is attached to a non-highlight machining area of the shell workpiece; a highlight machining area of the shell workpiece is machined to obtain a highlight side; and after the protective film is removed, the non-highlight machining area and the highlight machining area are subjected tonormal primary anodic oxidation machining at the same time. According to the technology provided by the invention, oxidation film of the highlight side and the oxidation film of the non-highlight areaare the same in thickness, color and film layer property, white line defects existing during ordinary highlight same color anodic oxidation do not exist, and the appearance integrity is very good.

Description

technical field [0001] The invention relates to a metal processing technology, in particular to an aluminum alloy casing, a processing method thereof, and an electronic device. Background technique [0002] Modern daily life has become more and more inseparable from electronic devices, such as tablet computers, smart phones, e-books, portable notebooks, etc. As people have higher and higher requirements for the appearance of electronic products, higher requirements are also put forward for the materials and processing technology of electronic product casings. [0003] Aluminum alloy is the most widely used non-ferrous metal structural material in industry, and has been widely used in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industry. Due to the low density of aluminum alloy, but relatively high strength, which is close to or exceeds that of high-quality steel, it has good plasticity and can be processed into various profiles, so it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D11/04H04M1/18
CPCC25D11/04C25D11/022H04M1/18
Inventor 田振煌刘传钦
Owner QIKU INTERNET TECH SHENZHEN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap