Melamine foam tooth brush and manufacturing method thereof

A manufacturing method, melamine technology, applied in dentistry, tooth cleaning, carbon preparation/purification, etc., can solve the problems of unable to remove tooth stains, poor adsorption of melamine foam, etc., to improve the fixing effect, increase the adsorption performance, save cost effect

Inactive Publication Date: 2018-03-09
郑州峰泰纳米材料有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Melamine foam, also known as melamine foam, is a high-opening three-dimensional network structure foam made of melamine and formaldehyde resin with additives. It can absorb stains with a little water, and has obvious cleaning effects. It is widely used in cleaning Scale, grease and dirt on any light and hard surface such as tableware, kitchen utensils, bathrooms, tiles, home appliances, household appliances, etc.; due to the good cleaning effect of melamine foam, there are now dental wipes made of melamine foam for cleaning Teeth, remove tooth stains; however, the melamine foam currently used to make tooth wipes has relatively poor adsorption, and cannot effectively remove tooth stains and clean teeth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Melamine foam tooth brush and manufacturing method thereof
  • Melamine foam tooth brush and manufacturing method thereof
  • Melamine foam tooth brush and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A melamine foam toothbrush, comprising a melamine foam cotton wipe 1 and a clamping mechanism for fixing the melamine foam cotton wipe 1;

[0039] The clamping mechanism includes an upper splint 2, a connecting plate 3 and a lower splint 4, and the upper splint 2 and the lower splint 4 are movably connected by the connecting plate 3;

[0040] The upper splint 2 includes a first handle 4 and a first clamping portion 5, the inner surface of the first handle 4 is provided with a first boss 6 along its outer edge, and the inner surface of the first clamping portion 5 is The side is provided with a second boss 8 along its outer edge, and the inner surface of the first clamping part 5 is also provided with a first groove 9, and a third boss 10 is arranged in the first groove 9;

[0041] The lower splint 4 includes a second handle portion 11 and a second clamping portion 12, and the inner surface of the second handle portion 11 is provided with a first card that cooperates wit...

Embodiment 2

[0044] A melamine foam toothbrush, comprising a melamine foam cotton wipe 1 and a clamping mechanism for fixing the melamine foam cotton wipe 1;

[0045] The clamping mechanism includes an upper splint 2, a connecting plate 3 and a lower splint 4, and the upper splint 2 and the lower splint 4 are movably connected by the connecting plate 3;

[0046] The upper splint 2 includes a first handle 4 and a first clamping portion 5, the inner surface of the first handle 4 is provided with a first boss 6 along its outer edge, and the inner surface of the first clamping portion 5 is The side is provided with a second boss 8 along its outer edge, and the inner surface of the first clamping part 5 is also provided with a first groove 9, and a third boss 10 is arranged in the first groove 9;

[0047] The lower splint 4 includes a second handle portion 11 and a second clamping portion 12, and the inner surface of the second handle portion 11 is provided with a first card that cooperates wit...

Embodiment 3

[0050] A kind of manufacture method of melamine foam tooth wipe, the concrete manufacture steps of described melamine foam cotton wipe are as follows:

[0051] 1) Stir and mix ethyl orthosilicate and sulfuric acid solution in proportion to obtain the first solution;

[0052] 2) Take melamine, formaldehyde and water and heat and stir to obtain the second solution;

[0053] 3) After the second solution obtained in step 2) is cooled, quickly add it to the first solution, stir and mix thoroughly, and then stand at 45°C for 12 hours to obtain a mixed solution;

[0054] 4) After the mixed solution obtained in step 3) was stabilized at 180°C for 3 hours in an air atmosphere, it was put into a carbonization furnace, and 2 Under gas protection, the temperature was raised to 800°C, then kept at a constant temperature for 3 hours, then cooled to room temperature naturally, and finally HF was added and stirred at room temperature for 24 hours to obtain a melamine resin-based porous carbo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a melamine foam tooth brush which comprises a melamine foam cotton brush and a clamping mechanism for fixing the melamine foam cotton brush. The clamping mechanism comprises an upper clamping plate, a connecting plate and a lower clamping plate; the upper clamping plate comprises a first handheld part and a first clamping part; a first boss is arranged on the inner side face of the first handheld part, a second boss is arranged on the inner side face of the first clamping art along the outer edge of the first clamping part, a first groove is also formed in the inner side face of the first clamping part, and a third boss is arranged in the first groove; the lower clamping plate comprises a second handheld part and a second clamping part; a first slot is formed in the inner side face of the second handheld part, a second slot is formed in the inner side face of the second handheld part, a second groove is also formed in the second clamping part, a pressure plateis connected to the second groove, and a melamine foam mask brush is arranged between the pressure plate and the second groove. The melamine foam tooth brush provided by the invention has the advantages of being energy-saving and environment-friendly, cost-saving, high in density and good in adsorptive effect.

Description

technical field [0001] The invention belongs to the technical field of cleaning supplies, and in particular relates to a melamine foam tooth wipe and a manufacturing method thereof. Background technique [0002] Melamine foam, also known as melamine foam, is a high-opening three-dimensional network structure foam made of melamine and formaldehyde resin with additives. It can absorb stains with a little water, and has obvious cleaning effects. It is widely used in cleaning Scale, grease and dirt on any light and hard surface such as tableware, kitchen utensils, bathrooms, tiles, home appliances, household appliances, etc.; due to the good cleaning effect of melamine foam, there are now dental wipes made of melamine foam for cleaning teeth, remove tooth stains; yet, the melamine foam currently used to make tooth wipes has relatively poor adsorption, and cannot effectively remove tooth stains and clean teeth. Contents of the invention [0003] The object of the present inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61C17/00C08G12/32C01B32/05B29C44/00
CPCA61C17/00B29C44/00C08G12/32
Inventor 李洋洋樊雪子王永飞李磊磊刘军飞刘振涛左耀卫付超峰方乃竞
Owner 郑州峰泰纳米材料有限公司