Anti-corrosive oil-resisting cable and its preparation method

An anti-corrosion and oil-resistant technology, applied in circuits, electrical components, plastic/resin/wax insulators, etc., can solve problems such as corrosion aging, performance and service life reduction

Inactive Publication Date: 2018-03-09
WUHU HANGTIAN SPECIAL CABLE FACTORY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the problem that in the prior art, during the use of the cable, it is often affected by oil pollution, etc., which will lead to corrosion and aging, which will greatly reduce its performance and service life. problem, thereby providing an anti-corrosion and oil-resistant cable with good oil resistance and effective anti-corrosion and aging resistance and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The invention provides a method for preparing an anti-corrosion and oil-resistant cable, wherein the preparation method comprises:

[0016] 1) Mixing silicon dioxide in an acid solution to obtain acid-etched silicon dioxide;

[0017] 2) In the presence of a solvent, the acid-etched silicon dioxide and nano-zinc oxide are mixed and filtered to obtain a mixture M1;

[0018] 3) mixing and melting polypropylene resin, mixture M1, polyurethane resin, mica powder, magnesium oxide, curing agent and accelerator, and extruding to obtain a wire sheath;

[0019] 4) Coating the wire sheath with the wire core to obtain an anti-corrosion and oil-resistant cable.

[0020] In the present invention, silicon dioxide is mixed in acid solution, then mixed with nanometer zinc oxide, filtered, and then polypropylene resin, mixture M1, polyurethane resin, mica powder, magnesium oxide, curing agent and accelerator are mixed and smelted and extruded forming to obtain a wire sheath, and then w...

Embodiment 1

[0031] 1) Put 30 parts by weight of silicon dioxide in 100 parts by weight of an aqueous solution of hydrochloric acid (the content of hydrochloric acid is 35% by weight) and stir and mix at a temperature of 40° C. to prepare silicon dioxide after acid etching;

[0032] 2) In the presence of water, 10 parts by weight of acid-etched silicon dioxide and 3 parts by weight of nano-zinc oxide are mixed and filtered to obtain a mixture M1;

[0033] 3) 100 parts by weight of polypropylene resin, 30 parts by weight of mixture M1, 50 parts by weight of polyurethane resin, 3 parts by weight of mica powder, 5 parts by weight of magnesium oxide, 1 part by weight of curing agent and 1 part by weight of accelerator are placed at a temperature of After mixing and melting at 180°C, extrusion molding is made to obtain the wire sheath;

[0034] 4) Cover the wire core with the wire sheath to prepare the anti-corrosion and oil-resistant cable A1.

Embodiment 2

[0036] 1) Put 50 parts by weight of silicon dioxide in 100 parts by weight of an aqueous solution of hydrochloric acid (the content of hydrochloric acid is 35% by weight) and stir and mix at a temperature of 60° C. to prepare silicon dioxide after acid etching;

[0037] 2) In the presence of water, 10 parts by weight of acid-etched silicon dioxide and 5 parts by weight of nano-zinc oxide are mixed and filtered to obtain a mixture M1;

[0038] 3) 100 parts by weight of polypropylene resin, 60 parts by weight of mixture M1, 60 parts by weight of polyurethane resin, 10 parts by weight of mica powder, 20 parts by weight of magnesium oxide, 5 parts by weight of curing agent and 5 parts by weight of accelerator are placed at a temperature of After mixing and melting at 220°C, extrusion molding is made to obtain the wire sheath;

[0039] 4) Cover the wire core with the wire sheath to prepare the anti-corrosion and oil-resistant cable A2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-corrosive oil-resisting cable and its preparation method. The preparation method includes steps of 1), placing silicon dioxide in acid fluid to mix, and preparing the silicon dioxide after acid erosion; 2), mixing and filtering the silicon dioxide after acid erosion with nano-zinc oxide in the presence of solvent, and preparing a mixture M1; 3), mixing and melting polypropylene resin, the mixture M1, polyurethane resin, mica powder, magnesium oxide, curing agent and accelerant, and then extruding and shaping; preparing a cable skin; 4), coating a cable core by the cable skin, and preparing the anti-corrosive oil-resisting cable. Through the methods of placing silicon dioxide in acid fluid to mix, mixing and filtering the silicon dioxide, and then mixing andmelting polypropylene resin, the mixture M1, polyurethane resin, mica powder, magnesium oxide, curing agent and accelerant, and then extruding and shaping to prepare the cable skin, and coating the cable core by the cable skin, the cable has good oil-resisting and anti-corrosive performances.

Description

technical field [0001] The invention relates to the field of cable materials, in particular to an anti-corrosion and oil-resistant cable and a preparation method thereof. Background technique [0002] As a common power facility, cables are used in all aspects of life and production. In the process of its use, it is often affected by oil pollution and the like, which will lead to corrosion and aging, which will greatly reduce its performance and service life. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide an anti-corrosion and oil-resistant cable with good oil resistance and effective anti-corrosion and aging resistance and its preparation method. Contents of the invention [0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the problem that in the prior art, during the use of the cable, it is often affected by oil pollution, etc., which will lead to corrosion and aging, which w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L75/04C08K13/06C08K9/02C08K3/36C08K3/22C08K3/34H01B3/44
CPCC08L23/12C08K2003/222C08K2003/2296C08K2201/011C08L2203/202H01B3/441C08L75/04C08K13/06C08K9/02C08K3/36C08K3/22C08K3/34
Inventor 赵明哲何想想李倩潘小青
Owner WUHU HANGTIAN SPECIAL CABLE FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com