Production method of multifunctional plastic
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and multi-functional technology are applied in the production field of multi-functional plastics, which can solve the problems of rising production costs and oily residues, and achieve the effects of improving plasticity, low price and good application prospects.
Inactive Publication Date: 2018-03-20
ZHANGJIAGANG DANENG PLASTIC PROD
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Existing plastic materials, as the structural requirements of plastic materials are getting higher and higher, their production costs are also rising. The appearance, strength, plasticity, heat resistance and other problems of plastics need to be solved. In daily life, oil pollution is more common , stained with oil must be cleaned with a special degreasing detergent, and there are often oily residues in direct water washing; while achieving various properties of plastics, reducing costs is also a problem that needs to be solved
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] A method for making multifunctional plastics is characterized in that it comprises the steps of:
[0019] Mix synthetic resins, fillers, stabilizers, plasticizers, colorants, and lubricants according to a certain mass ratio to obtain a mixture. Fillers account for 5%, stabilizers account for 10%, plasticizers account for 5%, and coloring 5% lubricant, 5% lubricant, 10% oil repellant, 60% synthetic resin;
[0020] heating the mixture at a temperature range of 70° C. for 10 hours;
[0021] The mixture after heating is plasticized and formed on an extruder.
Embodiment 2
[0023] A method for making multifunctional plastics is characterized in that it comprises the steps of:
[0024] Mix synthetic resin, filler, stabilizer, plasticizer, colorant and lubricant according to a certain mass ratio to obtain a mixture. Filler accounts for 10%, stabilizer accounts for 10%, plasticizer accounts for 10%, coloring 2% lubricant, 3% lubricant, 15% oil repellant, 50% synthetic resin;
[0025] heating the mixture at a temperature range of 100° C. for 8 hours;
[0026] The mixture after heating is plasticized and formed on an extruder.
Embodiment 3
[0028] A method for making multifunctional plastics is characterized in that it comprises the steps of:
[0029] Mix synthetic resin, filler, stabilizer, plasticizer, colorant, and lubricant according to a certain mass ratio to obtain a mixture. Filler accounts for 7%, stabilizer accounts for 6%, plasticizer accounts for 7%, coloring 3% lubricants, 4% lubricants, 20% oil repellents, 53% synthetic resins;
[0030] heating the mixture at a temperature range of 130° C. for 7 hours;
[0031] The mixture after heating is plasticized and formed on an extruder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a plastic production method. The plastic production method is characterized by comprising the following steps: mixing synthetic resin, a filling agent, a stabilizer, a plasticizer, a colorant and a lubricant in a certain mass ratio, so as to obtain a mixture, wherein the mixture contains the following components in percentage by weight: 5%-10% of the filling agent, 5%-10% of the stabilizer, 5%-10% of the plasticizer, 2%-5% of the colorant, 10%-20% of the lubricant and the balance of the synthetic resin; heating the mixture at 70-130 DEG C for 7-10 hours; and carrying out plasticization formation on the heated mixture by virtue of an extruder. The method has the advantages that the components of the plastic are relatively cheap in the market and are used for producing the plastic in a reasonable ratio, so that the plasticity, heat resistance, strength, flexibility, appearance, grease resistance and the like of the plastic can be greatly improved, and the plastichas very good application prospect.
Description
technical field [0001] The invention relates to a method for making multifunctional plastics. Background technique [0002] Existing plastic materials, as the structural requirements of plastic materials are getting higher and higher, their production costs are also rising. The appearance, strength, plasticity, heat resistance and other problems of plastics need to be solved. In daily life, oil pollution is more common , Oil stains must be cleaned with a special degreasing detergent, and there are often oil residues in direct water washing; while achieving various properties of plastics, reducing costs is also a problem that needs to be solved. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a multifunctional plastic manufacturing method with good heat resistance, plasticity, strength, oil resistance, etc., and low cost. [0004] In order to solve the above-mentioned tec...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More