A ppr pipe with copper texture

A technology of texture and pipe material, which is applied in the field of PPR pipe preparation, can solve the problems of single visual effect, poor low-temperature toughness and poor heat resistance of PPR pipe, and achieve good thermal stability, product dimensional stability, and heat-resistant temperature. small effect

Active Publication Date: 2020-09-08
江西陈氏科技集团股份有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is: in order to solve the technical problems of poor low temperature toughness, poor heat resistance and single visual effect of existing PPR pipes, to provide a PPR pipe with copper texture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A ppr pipe with copper texture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment provides a copper-like PPR pipe, comprising the following components by weight: 100 parts of PPR, 15 parts of granular copper powder, 5 parts of scaly copper powder, 12 parts of dispersant, 8 parts of carbon fiber, coupling 1 part of agent, 8 parts of soft core and hard shell type core-shell copolymer toughening agent, 1.5 parts of antioxidant.

[0035] In this embodiment, the carbon fiber is polyacrylonitrile-based carbon fiber, the soft-core hard-shell core-shell copolymer is methyl methacrylate-butyl acrylate core-shell copolymer, and the dispersant is stearic acid , the coupling agent is γ-(2,3-glycidoxy)propyltrimethoxysilane, and the antioxidant is β-(3,5-di-tert-butyl with a mass ratio of 1:0.5 -4-hydroxyphenyl) octadecyl propionate and three [2,4-di-tert-butylphenyl] phosphite, the granular copper powder is 400 mesh, and the flaky copper powder is 700 mesh head.

[0036] The preparation method of the above-mentioned PPR pipe with copper texture...

Embodiment 2

[0044] This embodiment provides a copper-like PPR pipe, comprising the following components by weight: 100 parts of PPR, 30 parts of granular copper powder, 1 part of scaly copper powder, 15 parts of dispersant, 15 parts of carbon fiber, coupling 2 parts of agent, 12 parts of soft core and hard shell type core-shell copolymer toughening agent, 1.3 parts of antioxidant.

[0045] In this embodiment, the carbon fibers are pitch-based carbon fibers, the soft-core hard-shell core-shell copolymer is methyl methacrylate-butadiene-styrene core-shell copolymer, and the dispersant is Lauric acid, the coupling agent is γ-mercaptopropyltrimethoxysilane, and the antioxidant is tetrakis[β-(3,5-di-tert-butyl-4-hydroxybenzene with a mass ratio of 1:1 base) propionic acid] pentaerythritol ester and bis(2,4-di-tert-butylphenol) pentaerythritol diphosphite, the granular copper powder is 500 mesh, and the flaky copper powder is 600 mesh.

[0046] The preparation method of the above-mentioned PPR...

Embodiment 3

[0054] This embodiment provides a copper-like PPR pipe, comprising the following components by weight: 100 parts of PPR, 20 parts of granular copper powder, 2 parts of scaly copper powder, 10 parts of dispersant, 10 parts of carbon fiber, coupling 1.5 parts of agent, 5 parts of soft core and hard shell type core-shell copolymer toughening agent, 2.5 parts of antioxidant.

[0055] In this embodiment, the carbon fiber is viscose-based carbon fiber, the soft-core hard-shell core-shell copolymer is methyl methacrylate-butyl acrylate core-shell copolymer, and the dispersant is tristearic acid Glycerides,

[0056] The coupling agent is tris(dioctylpyrophosphoryloxy) isopropyl titanate, and the antioxidant is 4,6-tris(3,5-di-tert-butyl) with a mass ratio of 1:2 -4-hydroxybenzyl)benzene and tris[2,4-di-tert-butylphenyl]phosphite, the granular copper powder is 800 mesh, and the flaky copper powder is 500 mesh.

[0057] The preparation method of the above-mentioned PPR pipe with coppe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a PPR (polypropylene random copolymer) pipe with copper texture. The PPR pipe comprises, by weight, 100 parts of PPR, 15-30 parts of granular copper powder, 1-5 parts of flakycopper powder, 10-15 parts of dispersing agents, 8-18 parts of carbon fibers, 1-3 parts of coupling agents, 5-15 parts of soft-core hard-shelled core shell copolymer toughening agents and 1.3-3 partsof antioxidants. The PPR pipe has good copper texture and is good in low-temperature toughness, free from embrittlement and good in heat resistance.

Description

technical field [0001] The invention relates to a PPR pipe material with copper texture, belonging to the technical field of PPR pipe preparation. Background technique [0002] PPR is also called random copolymerized polypropylene, which is extruded into pipes by random copolymerized polypropylene, and the pipes are injection molded into pipe fittings. Compared with traditional cast iron pipes, galvanized steel pipes, cement pipes and other pipes, PPR pipe fittings are energy-saving, material-saving, Environmental protection and non-toxic, heat and pressure resistance, light weight and high strength, corrosion resistance, no scaling, good impact resistance and creep resistance, easy installation, firm connection, long service life, recyclable materials, etc., are widely used in construction Water supply and drainage, city gas, electric power and optical cable sheathing, industrial fluid transportation, agricultural irrigation and other construction, municipal, industrial and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14C08L33/12C08K13/06C08K9/06C08K9/04C08K7/06C08K7/00C08K3/08C08K5/134C08K5/526
CPCC08K2003/085C08K2201/003C08L23/14C08L2201/08C08L2203/18C08L2207/53C08L33/12C08K13/06C08K9/06C08K7/06C08K7/00C08K3/08C08K5/1345C08K5/526C08K9/04
Inventor 程东红陈文其
Owner 江西陈氏科技集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products