Manufacturing method of rustproof anticorrosion milling machine water tank

A technology of anti-rust, anti-corrosion, and manufacturing method, which is applied in the field of water tank anti-rust, can solve problems such as difficult-to-immerse tank pretreatment, and achieve the effects of shortening manufacturing time, ensuring reliability, and enhancing anti-corrosion performance

Inactive Publication Date: 2018-04-20
SHANTUI CONSTR MASCH CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for manufacturing the water tank of an anti-rust and anti-corrosion milling machine, so as to solve the problem that large structural parts such as water tanks are difficult to perform pre-treatment in a dipping tank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of rustproof anticorrosion milling machine water tank

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The technical solutions of the present invention will be further described below in conjunction with the accompanying drawings and through specific implementation methods.

[0032] The invention provides a method for manufacturing an antirust and anticorrosion milling machine water tank, such as figure 1 Shown, the manufacture method of this water tank comprises the following steps:

[0033] S0, perform shot blasting on the plate:

[0034] Before the water tank body is welded, each plate is subjected to shot blasting treatment through a shot blasting machine, including shot blasting cleaning and shot blasting strengthening, to remove impurities such as oxide skin on the surface of the plate to improve the appearance quality, and to use high-speed motion (such as a speed of 60 ~110m / s) projectile flow continuously impacts the surface of the reinforced workpiece, which can improve the fatigue fracture resistance of materials or parts, prevent fatigue failure, plastic def...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of a rustproof anticorrosion milling machine water tank and relates to the technical field of water tank rust prevention. The manufacturing method of therustproof anticorrosion milling machine water tank comprises the steps that oil-resistant primer is sprayed to the surfaces of plates; asphalt paint is brushed and painted on the surfaces of the plates to which the oil-resistant primer is sprayed; and the plates to which the asphalt paint is brushed and painted are welded to form the water tank. According to the method, by adopting the oil-resistant primer and asphalt paint double-coating anticorrosion technology, the oil-resistant primer is sprayed firstly, then the asphalt paint is brushed and painted, the anticorrosion performance is enhanced, the work reliability of the water tank is ensured, and meanwhile, the problem that immersion groove type pretreatment cannot be carried out on large structural members like the water tank easilyis solved.

Description

technical field [0001] The invention relates to the technical field of water tank antirust, in particular to a method for manufacturing an antirust and anticorrosion milling machine water tank. Background technique [0002] During the construction process of the milling machine, the milling cutter head needs to be cooled. The cooling method is that the water pump absorbs water from the water tank and sprays it from the nozzle. In order to ensure the continuity of work, the volume of the water tank of the milling machine is designed to be relatively large. Usually, the milling width is The water tank of the 2000mm milling machine is generally designed at about 3500L, and the water tank of the milling machine is generally welded with the main frame, so it is difficult to prevent rust and corrosion of the water tank. [0003] At present, there is no general technical solution for the anti-rust and anti-corrosion treatment of the water tank of the milling machine. Generally, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00
Inventor 崔冬梅付衍法郭超刘瑞鹏
Owner SHANTUI CONSTR MASCH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap