High-performance heat preservation building material

A building material and high-performance technology, applied in the field of building materials, can solve the problems of poor weather resistance, low thermal insulation and fire resistance, and not simple preparation methods, and achieve the effect of improving indoor air

Inactive Publication Date: 2018-04-20
江苏赛沃机械设备有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the coatings used for building thermal insulation have poor weather resistance. When the external temperature changes greatly, the coating film will crack and other phenomena. However, the waterproof performance of the e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0008] Example 1

[0009] A high-performance thermal insulation building material, which is composed of the following parts by weight: 22 parts of diatomaceous earth, 30 parts of quartz sand, 8 parts of plant fiber powder, 10 parts of clay, 4 parts of fly ash, and 6 parts of filler , 1 part of carboxyl nitrile rubber, 3 parts of polybutadiene rubber, 10 parts of waterproofing agent, 13 parts of flame retardant.

Example Embodiment

[0010] Example 2

[0011] A high-performance thermal insulation building material, which is composed of the following parts by weight: 32 parts of diatomaceous earth, 36 parts of quartz sand, 12 parts of plant fiber powder, 16 parts of clay, 10 parts of fly ash, and 12 parts of filler , 3 parts of carboxyl nitrile rubber, 7 parts of polybutadiene rubber, 16 parts of waterproofing agent, 17 parts of flame retardant.

Example Embodiment

[0012] Example 3

[0013] A high-performance thermal insulation building material, which is composed of the following parts by weight: 27 parts of diatomaceous earth, 33 parts of quartz sand, 10 parts of plant fiber powder, 13 parts of clay, 7 parts of fly ash, and 9 parts of filler , 2 parts of carboxyl nitrile rubber, 5 parts of polybutadiene rubber, 13 parts of waterproofing agent, 15 parts of flame retardant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-performance thermal insulation building material, which is composed of the following raw materials in parts by weight: 22-32 parts of diatomite, 30-36 parts of quartz sand, 8-12 parts of plant fiber powder, and 10-32 parts of clay 16 parts, 4-10 parts of fly ash, 6-12 parts of filler, 1-3 parts of carboxylated nitrile rubber, 3-7 parts of polybutadiene rubber, 10-16 parts of waterproofing agent, 13-17 parts of flame retardant . The invention adopts a scientific raw material ratio, adopts diatomite, has no pollution to the environment, does not release toxic substances, and can improve indoor air; it solves the problem of energy saving and environmental protection, sound insulation, compressive strength and There are still insufficient problems in buildings with high thermal insulation performance requirements.

Description

Technical field [0001] The invention relates to a high-performance thermal insulation building material, belonging to the field of building materials. Background technique [0002] With the process of urbanization in China, infrastructure construction is not expanding much, so the demand for building materials has become higher and higher in quality. At present, most of the coatings used in building insulation have poor weather resistance. When the external temperature changes greatly, the coating film will crack. However, the existing waterproof materials can only be waterproof in a single layer, and the waterproof performance is not strong enough. The preparation method is not simple enough, and the heat preservation and fire resistance performance is not high. Summary of the invention [0003] In order to solve the above problems, the present invention provides a high-performance thermal insulation building material, which is composed of the following parts by weight: 22-32 pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B111/52C04B111/28
CPCC04B28/001C04B2111/00025C04B2111/28C04B2111/52C04B14/08C04B14/06C04B18/24C04B18/08C04B24/2652C04B24/2611C04B2103/63C04B2103/65
Inventor 刘贵来刘睿先
Owner 江苏赛沃机械设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap