Reinforcing liquid for paper cultural relic protection

A technology of paper cultural relics and reinforcement liquid, which is applied in the post-processing of waste paper, post-processing of printing, printing, etc., can solve the problems of poor permeability, low anti-ultraviolet light performance, and poor use effect, and achieve easy production and preparation. The formula is scientific and reasonable, and the effect of rich raw materials

Inactive Publication Date: 2018-06-29
郑州博物馆 +1
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the above situation, in order to overcome the defects of the prior art, the purpose of the present invention is to provide a reinforcement solution for the protection of paper cultural relics, which can effectively solve the problem of poor permeability and anti-ultraviolet light performance of the existing reinforcement solutions for the protection of paper cultural relics. Low, poor use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforcing liquid for paper cultural relic protection
  • Reinforcing liquid for paper cultural relic protection
  • Reinforcing liquid for paper cultural relic protection

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: A kind of reinforcing liquid that is used for the protection of paper cultural relics is made of the following raw materials by weight percentage: 40g of hexamethylene diisocyanate trimer, 0.5g of nano silicon dioxide, 0.1g of dibutyltin dilaurate g and N,N-dimethylformamide (DMF) 30g, wherein, put the nano-silica in a vacuum drying oven, dry for 10-24h, and remove the moisture to obtain dry nano-silica; Add methylene diisocyanate trimer to N,N-dimethylformamide (DMF), heat to 50°C to dissolve, keep warm for 5~10min to obtain a mixed solution; add dry nano-silica to the mixed solution , and add dibutyltin silicate in February, raise the temperature to 70°C, carry out the reaction, measure the content of isocyanate group (-NCO) every hour, when the weight content of isocyanate group (-NCO) reaches 19%, stop the reaction and depressurize The N,N-dimethylformamide (DMF) is distilled off to obtain the reinforcing solution of the present invention.

Embodiment 2

[0011] Embodiment 2: a kind of reinforcing liquid for the protection of paper cultural relics is made of the following raw materials in weight percent: 30 g of hexamethylene diisocyanate trimer, 1.0 g of nano silicon dioxide, 0.1 g of dibutyltin dilaurate g and N,N-dimethylformamide (DMF) 30g, wherein, put the nano-silica in a vacuum drying oven, dry for 10-24h, and remove the moisture to obtain dry nano-silica; Add methylene diisocyanate trimer to N,N-dimethylformamide (DMF), heat to 50°C to dissolve, keep warm for 5~10min to obtain a mixed solution; add dry nano-silica to the mixed solution , and add dibutyltin silicate in February, raise the temperature to 70°C, carry out the reaction, measure the content of isocyanate group (-NCO) every hour, when the weight content of isocyanate group (-NCO) reaches 16%, stop the reaction and depressurize The N,N-dimethylformamide (DMF) is distilled off to obtain the reinforcing solution of the present invention.

Embodiment 3

[0012] Embodiment 3: A kind of reinforcing liquid that is used for the protection of paper cultural relics is the following raw materials by weight percent: 50g of hexamethylene diisocyanate trimer, 1.5g of nano silicon dioxide, 0.1g of dibutyltin dilaurate g and N,N-dimethylformamide (DMF) 30g, wherein, put the nano-silica in a vacuum drying oven, dry for 10-24h, and remove the moisture to obtain dry nano-silica; Add methylene diisocyanate trimer to N,N-dimethylformamide (DMF), heat to 50°C to dissolve, keep warm for 5~10min to obtain a mixed solution; add dry nano-silica to the mixed solution , and add dibutyltin silicate in February, raise the temperature to 70°C, carry out the reaction, measure the content of isocyanate group (-NCO) every hour, when the weight content of isocyanate group (-NCO) reaches 27%, stop the reaction and depressurize The N,N-dimethylformamide (DMF) is distilled off to obtain the reinforcing solution of the present invention.

[0013] When using th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle size rangeaaaaaaaaaa
Specific surfaceaaaaaaaaaa
Login to View More

Abstract

The invention relates to reinforcing liquid for paper cultural relic protection. The reinforcing liquid for the paper cultural relic protection is prepared from the following raw materials by weight percent: 30% to 75% of hexamethylene diisocyanate trimer, 0.5% to 4% of nano silica, 0.1% to 0.3% of dibutyltin dilaurate and 20.7% to 68.9% of N,N-dimethylformamide, the nano silica is dried to obtaindried nano silica; the hexamethylene diisocyanate trimer is added into the N,N-dimethylformamide, dissolved, and kept warm for 5 to 10 minutes to obtain a mixed solution; the dried nano silica is added into the mixed solution, and the dibutyltin dilaurate is added and heated to 70 DEG C. When an isocyanate group content is up to 15% to 50%, the reinforcing liquid of the invention is obtained; thereinforcing liquid for the paper cultural relic protection is scientific and reasonable in composition, rich in raw materials, easy to produce and prepare, and good in use effect. The reinforcing liquid for the paper cultural relic protection is innovation of the reinforcing liquid for the paper cultural relic protection, and has enormous economic and social benefits.

Description

technical field [0001] The invention relates to the protection of paper cultural relics, in particular to a reinforcement solution for the protection of paper cultural relics. Background technique [0002] Historical relics or unearthed paper relics such as paintings, calligraphy, and scriptures are precious historical materials that record human history, science and technology. However, with changes in internal and external environments, paper relics have become acidified, yellowed, decayed, broken, and broken to varying degrees. Powdery aging, moth-eaten and mildew will greatly reduce its preservation life and ornamental and research value. Therefore, paper cultural relics urgently need to be protected. Currently, the reinforcement solution B72 (an acrylic resin) used for the protection of paper cultural relics has a high Molecular weight, its poor penetration and wettability to fibers, resulting in poor penetration of resin into fibers, causing internal stress in paper, f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H25/18B41M7/00
CPCB41M7/0063D21H25/18
Inventor 齐迎萍申永峰杨扬李萍李华金姗姗
Owner 郑州博物馆
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com