Bonding method of PDLC films for vehicles

A vehicle-use, lamination technology, applied in optics, instruments, nonlinear optics, etc., can solve the problems of affecting the appearance, unable to use mechanical film, easy to form a lot of air bubbles, etc., to prolong the service life, prevent electrochemical corrosion, operation simple effect

Inactive Publication Date: 2018-07-13
GUANGZHOU HUAHUI MATERIAL TECH CO LTD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Generally, there are two methods of film application: manual film application and mechanical film application. Since the window glass is a curved glass with a certain radian, the mechanical film application method cannot be used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Embodiment 1 The bonding method of the ultra-thin PDLC film for vehicles of the present invention

[0042] Including the following steps:

[0043] (1) Cleaning the window glass: Spray water evenly on the surface of the window glass from the middle to the outside and from top to bottom to check for large dust particles, and use a straight-handled plastic water scraper to remove the water and water on the glass surface. Dust particles are scraped off without leaving water marks and dust particles;

[0044] (2) Film cutting: According to the shape and size of the window glass, cut the PDLC film for vehicles, and take the metal frame outside the glass as the baseline, and reserve a margin of 1CM outward;

[0045] (3) Edge trimming: cut the film according to the actual size of the glass edge, and reserve the electrode installation position;

[0046] (4) Pre-formed baking film: use wet baking to heat the PDLC film for vehicles with a hot air gun; the temperature is 120°C, a...

Embodiment 2

[0057] Embodiment 2 The bonding method of the ultra-thin PDLC film for vehicles of the present invention

[0058] Including the following steps:

[0059] (1) Cleaning the window glass: Spray water evenly on the surface of the window glass from the middle to the outside and from top to bottom to check for large dust particles, and use a straight-handled plastic water scraper to remove the water and water on the glass surface. Dust particles are scraped off without leaving water marks and dust particles;

[0060] (2) Film cutting: According to the shape and size of the window glass, cut the PDLC film for vehicles, and take the metal frame outside the glass as the baseline, and reserve a margin of 2 cm outward;

[0061] (3) Edge trimming: cut the film according to the actual size of the glass edge, and reserve the electrode installation position;

[0062](4) Pre-shaped baking film: use wet baking to heat the PDLC film for vehicles with a hot air gun; the temperature is 600°C, a...

Embodiment 3

[0070] Embodiment 3 The bonding method of the ultra-thin PDLC film for vehicles of the present invention

[0071] Including the following steps:

[0072] (1) Cleaning the window glass: Spray water evenly on the surface of the window glass from the middle to the outside and from top to bottom to check for large dust particles, and use a straight-handled plastic water scraper to remove the water and water on the glass surface. Dust particles are scraped off without leaving water marks and dust particles;

[0073] (2) Film cutting: according to the shape and size of the window glass, cut the PDLC film for vehicles, and take the metal frame outside the glass as the baseline, and reserve a margin of 1.5CM outward;

[0074] (3) Edge trimming: cut the film according to the actual size of the glass edge, and reserve the electrode installation position;

[0075] (4) Pre-shaped baking film: use wet baking to heat the PDLC film for vehicles with a hot air gun; the temperature is betwee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of glass film bonding, in particular to a bonding method of PDLC films for vehicles. The bonding method of the PDLC films for the vehicles comprises the steps of vehicle window glass cleaning, film cutting, trimming, preshaping and film baking, film bonding on finished products, water and bubble removal, shaping by baking, edge sealing, electrode connection, electrode glue sealing and the like. Films are bonded on the finished products after preshaping and film baking, so that adjustment is convenient due to inaccurate alignment, and the pass percent of the finished products is increased; and the edges of the PDLC films are protected by sealing strips, so that electrochemical corrosion caused by water in air invading into liquid crystal layers is prevented, and the service life of the PDLC films for the vehicles is prolonged. The bonding method of the PDLC films for the vehicles is simple in operation and convenient to use, and can effectively improve the installation speed.

Description

technical field [0001] The invention relates to the technical field of glass film sticking, in particular to a bonding method of a PDLC film for vehicles. Background technique [0002] With the increasingly severe energy problems, energy saving and environmental protection have become the mainstream trend advocated by social development. Many building exterior walls and automobile glass use PDLC intelligent dimming film, which can not only protect the privacy of users, but also have the function of blocking ultraviolet rays and infrared rays. , reduce the radiant heat of sunlight in the interior space, and save electricity for air conditioning. [0003] Traditional car film does not have the function of adjusting transparency, cannot effectively protect user privacy, and is relatively weak in blocking ultraviolet and infrared rays, while smart dimming film has multiple functions of blocking ultraviolet and infrared rays, adjusting transparency, and protecting privacy , with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C63/02G02F1/1334
CPCB29C63/02G02F1/1334
Inventor 张成温奕南来炜刚杨燕妮
Owner GUANGZHOU HUAHUI MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products