Method for manufacturing glass fiber reinforced plastic shell through die

A technology of FRP and FRP layers, which is applied in the field of FRP shell production, can solve the problems of difficult molding of FRP shells, affect product quality, and uneven pasting thickness, and achieve the effects of light weight, guaranteed strength, and low cost

Active Publication Date: 2018-07-20
唐山宏正机械设备有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is very difficult to form the FRP shell with smooth inner and outer surfaces, and it is very likely that there will be problems such as uneven paste thickness, paste void, and improper mold clamping, which will affect the final quality of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing glass fiber reinforced plastic shell through die

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the drawings in the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0031] A method of using a mold to make a glass fiber reinforced plastic shell in an embodiment of the present invention includes the following steps:

[0032] (1) Gel coat layer spraying: spray the gel coat layer on the surface of the upper mold and the lower mold of the mold, and the thickness of the gel coat layer is between 0.3-0.5mm;

[0033] Specifically, the upper mold and the lower mold are first waxed with release wax and then the gel coat layer is sprayed. There must b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Smudge thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacturing method of a glass fiber reinforced plastic shell, in particular to a method for manufacturing the glass fiber reinforced plastic shell through a die. The method includes the steps of (1) gel coat layer spraying, (2) glass fiber reinforced plastic layer pasting, (3) foam layer splicing, (4) die assembly grinding, (5) final die assembly, (6) post curing, (7)demolding and (8) product paint spraying. According to the method, the die is used for manufacturing the glass fiber reinforced plastic shell, the technological step is simple, and operation is easy;through an up and down die assembly manner, it is guaranteed that the inner and outer surfaces of a molded product are both flat and smooth; through measurement of the thickness of a die cavity in dieassembly grinding, the problems about uneven pasting thickness, pasting missing and the like of the molded product are avoided, and the final molding quality of the molding product is guaranteed; andin addition, the molded product is the glass fiber reinforced plastic product with a foam sandwich, the strength of a driving cab shell is guaranteed, meanwhile, the weight is smaller, and cost is lower.

Description

technical field [0001] The invention relates to a method for manufacturing a glass steel shell, in particular to a method for making a glass steel shell by using a mold. Background technique [0002] At present, some FRP shell products usually require smooth inner and outer surfaces, especially the driver's cab shell of rail vehicles, which can avoid the need to use interior parts to beautify the inner surface of the shell, and the inner surface of the shell product is the interior surface In this way, on the one hand, the beautification process of the interior surface can be omitted, and the production cycle of the product can be shortened; lighter. However, it is very difficult to form the FRP shell with smooth inner and outer surfaces, and it is very likely that there will be problems such as uneven paste thickness, paste voids, and improper mold closing, which will affect the final quality of the product. Therefore, be badly in need of providing a kind of method that u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C70/30B29C70/54
CPCB29C70/30B29C70/54
Inventor 李忠志李秀连高瑞浦陈阳赵志伟
Owner 唐山宏正机械设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products