Anti-cracking environment-friendly wood paint
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of wood lacquer and environmental protection technology, applied in the field of wood varnish, can solve the problems of cracking and troubles of wood products, and achieve the effect of good anti-cracking, excellent film forming and strong adhesion
Inactive Publication Date: 2018-08-03
长泰惠龙新材料科技有限公司
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] Because solid wood is a natural and environmentally friendly material, it is very popular among people, but in the dry areas of the north, the problem of cracking of wood products often plagues people
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] A kind of anti-cracking environmental protection wood lacquer, each component material and weight percentage thereof are:
[0020]
[0021]
[0022] Preferably, the animal and vegetable oil composition is a mixture of fish oil and tung oil, the weight ratio of fish oil and tung oil is fish oil:tung oil=3:1; the aluminum oxide particles are 5nm.
[0023] Preferably, the bamboo charcoal powder is 4000 mesh.
[0024] Preferably, the defoamer is polyether modified silicone.
[0025] Preferably, the pH regulator is 2-amino-2-methyl-1-propanol.
[0026] Preferably, the minimum film-forming temperature of the aqueous acrylic emulsion is 20°C.
[0027] Preferably, the film-forming aid is dodecyl alcohol ester.
Embodiment 2
[0029] A kind of anti-cracking environmental protection wood lacquer, each component material and weight percentage thereof are:
[0030]
[0031]
[0032] Preferably, the animal and vegetable oil composition is a mixture of fish oil and tung oil, the weight ratio of fish oil and tung oil is fish oil:tung oil=3:1; the aluminum oxide particles are 6nm.
[0033] Preferably, the bamboo charcoal powder is 000 mesh.
[0034] Preferably, the defoamer is polyether modified silicone.
[0035] Preferably, the pH regulator is 2-amino-2-methyl-1-propanol.
[0036] Preferably, the minimum film-forming temperature of the aqueous acrylic emulsion is 25°C.
[0037] Preferably, the film-forming aid is dodecyl alcohol ester.
Embodiment 3
[0039] A kind of anti-cracking environmental protection wood lacquer, each component material and weight percentage thereof are:
[0040]
[0041]
[0042] Preferably, the animal and vegetable oil composition is a mixture of fish oil and tung oil, the weight ratio of fish oil and tung oil is fish oil:tung oil=3:1; the aluminum oxide particles are 4nm.
[0043] Preferably, the bamboo charcoal powder is 5000 mesh.
[0044] Preferably, the defoamer is polyether modified silicone.
[0045] Preferably, the pH regulator is 2-amino-2-methyl-1-propanol.
[0046] Preferably, the minimum film-forming temperature of the aqueous acrylic emulsion is 19°C.
[0047] Preferably, the film-forming aid is dodecyl alcohol ester.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
minimum film forming temperature
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses anti-cracking environment-friendly wood paint. The wood paint comprises the following formula components in parts by mass: 35 to 45 percent of a water-based acrylic emulsion, 13 to 15 percent of methyl methacrylate, 3 to 9 percent of hydroxyethyl acrylate, 5 to 7 percent of nanometer calcium carbonate, 4 to 6 percent of a nanometer silver antimicrobial agent, 3 to 7 percentof nanometer silicon carbide, 1 to 4 percent of aluminum oxide particles, 4 to 6 percent of an animal and vegetable oil combination, 3 to 5 percent of diatomite, 0.1 to 0.4 percent of a wax emulsion,0.4 to 0.8 percent of a defoamer, 0.1 to 0.4percent of a pH regulator, 2.1 to 3.2 percent of an anti-settling agent, 0.3 to 0.6 percent of a dispersing agent, 2 to 4 percent of a coalescing agent, 0.3 to 0.5 percent of an adhesion promoter, 5 to 9 percent of a bamboo charcoal powder, 1 to 3 percent of a glass powder, and water for the surplus. The wood paint has the characteristic of preventing wood products from cracking, has high adhesive force to a wood material, is not easy to fall off and environmentally friendly, and does not have harms to bodies.
Description
[0001] This application is a divisional application of a patent with an application number of 2015110041727 and an application date of December 28, 2015. technical field [0002] The invention relates to a wood varnish, in particular to an anti-cracking and environment-friendly wood varnish. Background technique [0003] Wood paint refers to a type of resin paint used on wood products, including polyester, polyurethane paint, etc., which can be divided into water-based and oil-based. According to gloss, it can be divided into high gloss, semi-matte and matte. According to the application, it can be divided into furniture paint, floor paint and so on. [0004] The production process of water-based wood paint is a simple physical mixing process. Water-based wood paint uses water as a solvent without any harmful volatilization. It is currently the safest and most environmentally friendly furniture paint. However, due to the influence of comprehensive factors such as coating ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More