Polishing treatment technology for stainless steel packaging box

A processing technology and packaging box technology, which is applied in the field of polishing processing technology of stainless steel packaging boxes, can solve the problems of destroying the color and luster of stainless steel packaging boxes, and achieve the effect of prolonging the service life and ensuring the stability.

Inactive Publication Date: 2018-10-12
JIANGSU GAIZHIBAO PACKAGING TECH CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Purpose of the invention: In order to solve the deficiencies of the prior art, the invention provides a polishing treatment process for stainless steel packaging boxes, which solves the problem in the prior art that the original color of the stainless steel packaging boxes is destroyed due to external factors, and ensures the surface of the parts Achieve the smoothness of the mirror surface, prolong the service life of the electrochemical polishing solution, and ensure the stability of the quality of the stainless steel packaging box

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (a) Degreasing

[0033] Soak the stainless steel packaging box in the degreasing solution for 1 min at a temperature of 30°C. The degreasing agent includes the following raw materials:

[0034] Sodium hydroxide 50g / L, sodium carbonate 20g / L, sodium phosphate 50g / L, sodium silicate 5g / L;

[0035] (b) Running water washing

[0036] Put the stainless steel packaging box after degreasing treatment into flowing water and wash until degreasing is clean;

[0037] (c) pickling

[0038] Put the stainless steel packaging box after water washing into the pickling solution for pickling for 10 minutes at room temperature, and the pickling solution includes the following raw materials:

[0039] 50% hydrochloric acid, 50% water;

[0040] (d) washing

[0041] Put the pickled stainless steel packaging box into clean water for 3 minutes;

[0042] (e) Electrochemical polishing

[0043] Put the cleaned stainless steel packaging box into the electrochemical polishing solution for ele...

Embodiment 2

[0052] (a) Degreasing

[0053] Soak the stainless steel packaging box in the degreasing solution for 2 minutes at a temperature of 35°C. The degreasing agent includes the following raw materials:

[0054] Sodium hydroxide 55g / L, sodium carbonate 25g / L, sodium phosphate 60g / L, sodium silicate 8g / L;

[0055] (b) Running water washing

[0056] Put the stainless steel packaging box after degreasing treatment into flowing water and wash until degreasing is clean;

[0057] (c) pickling

[0058] Put the stainless steel packaging box after water washing into the pickling solution for pickling for 18 minutes at room temperature, and the pickling solution includes the following raw materials:

[0059] 50% hydrochloric acid, 50% water;

[0060] (d) washing

[0061] Put the pickled stainless steel packaging box into clean water for 4 minutes;

[0062] (e) Electrochemical polishing

[0063] Put the cleaned stainless steel packaging box into the electrochemical polishing solution for...

Embodiment 3

[0072] (a) Degreasing

[0073] Soak the stainless steel packaging box in the degreasing solution for 3 minutes at a temperature of 40°C. The degreasing agent includes the following raw materials:

[0074] Sodium hydroxide 60g / L, sodium carbonate 30g / L, sodium phosphate 70g / L, sodium silicate 10g / L;

[0075] (b) Running water washing

[0076] Put the stainless steel packaging box after degreasing treatment into flowing water and wash until degreasing is clean;

[0077] (c) pickling

[0078] Put the stainless steel packaging box after water washing into the pickling solution for pickling at room temperature for 20 minutes. The pickling solution includes the following raw materials:

[0079]50% hydrochloric acid, 50% water;

[0080] (d) washing

[0081] Put the pickled stainless steel packaging box into clean water for 5 minutes;

[0082] (e) Electrochemical polishing

[0083] Put the cleaned stainless steel packaging box into the electrochemical polishing solution for ele...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a polishing treatment technology for a stainless steel packaging box. The polishing treatment technology comprises the following steps of carrying out oil removal; carrying outwashing in flowing water; carrying out acid pickling; carrying out water washing; carrying out electrochemical polishing; carrying out cold water cleaning; carrying out chemical passivation; and carrying out drying. The polishing treatment technology has the advantages that the problem that in the prior art, the original color and lustre of the stainless steel packaging box is damaged due to external reasons can be solved, the surface of a part can be guaranteed to reach the smoothness degree of a mirror plane, the service life of an electrochemical polishing solution can be prolonged, and thequality stability of the stainless steel packing box can be ensured.

Description

technical field [0001] The invention relates to the field of chemical polishing of metal surfaces, in particular to a polishing process for stainless steel packaging boxes. Background technique [0002] Human society is constantly progressing, and there are more aesthetic choices. In some packaging fields, people choose to use various metals to decorate stainless steel packaging boxes or stainless steel packaging boxes to hold some food and cosmetics. Stainless steel packaging boxes are exposed to the atmosphere or are in contact with the atmosphere. After human sweat is in contact, it will gradually change color as time goes by. The degree of corrosion mainly depends on the pollutants, humidity and temperature in the environment, and is also related to the atmosphere, such as the climate in the south or north, industrial atmosphere or marine atmosphere. Etc., the metal discoloration situation is also quite different, and the way to prevent corrosion discoloration is the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25F3/24C23G1/19
CPCC25F3/24C23G1/19
Inventor 罗平潘霞
Owner JIANGSU GAIZHIBAO PACKAGING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap