Heat-sealable matte aluminized printed composite packaging film for cigarettes and preparation method thereof

A composite packaging film, printing and packaging technology, applied in packaging, wrapping paper, transportation and packaging, etc., can solve the problem of limited barrier effect, reduce the initial temperature of heat sealing, avoid scratches on the aluminum plating layer, and ensure insulation Effect

Inactive Publication Date: 2018-10-16
SUZHOU KUNLENE FILM IND CO LTD +1
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the barrier effect of this single material is very limited. If the paper is wrapped with aluminized film, it needs to be printed on the surface of the aluminized film. In order to pursue rich colors and beautiful appearance, many cigarette packs often use full-page printing, and finally the surface is coated. A layer of matte ink makes the appearance have a matte color, produces a soft reflective effect, and has a good hand feeling, which improves the texture and grade of the packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-sealable matte aluminized printed composite packaging film for cigarettes and preparation method thereof
  • Heat-sealable matte aluminized printed composite packaging film for cigarettes and preparation method thereof
  • Heat-sealable matte aluminized printed composite packaging film for cigarettes and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The preparation method of the heat-sealable matte printing aluminized composite packaging film for cigarettes of the present invention comprises the following steps:

[0029] A. Preparation of heat-sealable matte printing packaging film: adopt multi-layer co-extrusion polypropylene biaxial stretching preparation process and polypropylene film gravure printing processing process, and use inner printing to prepare, wherein the longitudinal stretching temperature is 60-130 °C, the transverse stretching temperature is 100-175 °C, the temperature of the extruder is 200-250 °C, and the stretching ratio is 4-10;

[0030] B. Preparation of aluminum-coated packaging film: It is prepared by multi-layer co-extrusion polypropylene biaxial stretching preparation process and polypropylene film vacuum aluminum plating process, wherein the longitudinal stretching temperature is 60-130 ° C, and the transverse stretching temperature is 100 ~175℃, extruder temperature 200~250℃, draw ratio...

Embodiment 19

[0040] Select water-based polyurethane glue as the adhesive to carry out composite processing of the printed packaging film obtained in Example 1 and the aluminized packaging film obtained in Example 10 to obtain a composite packaging film for heat-sealable matte printed aluminized cigarettes. The preparation method includes the following steps: step:

[0041] A. Preparation of heat-sealable matte printing packaging film: The preparation process of multi-layer co-extruded polypropylene biaxial stretching and the gravure printing process of polypropylene film are used. The longitudinal stretching temperature is 60 ° C. The transverse stretching temperature is 100°C, the extruder temperature is 200°C, and the draw ratio is 4;

[0042] B. Preparation of aluminum-coated packaging film: It is prepared by multi-layer co-extrusion polypropylene biaxial stretching preparation process and polypropylene film vacuum aluminum plating process, wherein the longitudinal stretching temperatur...

Embodiment 20

[0046] Select vinyl acetate adhesive as the adhesive to carry out composite processing of the printed packaging film obtained in Example 2 and the aluminized packaging film obtained in Example 11 to obtain a printed and aluminized composite packaging film for cigarettes. The preparation method comprises the following steps:

[0047] A. Preparation of heat-sealable matte printing packaging film: the preparation process of multi-layer co-extruded polypropylene biaxial stretching and the processing process of polypropylene film gravure printing are carried out, and the longitudinal stretching temperature is 130 ° C. The transverse stretching temperature is 175°C, the extruder temperature is 250°C, and the draw ratio is 10;

[0048] B. Preparation of aluminum-coated packaging film: It is prepared by multi-layer co-extrusion polypropylene biaxial stretching preparation process and polypropylene film vacuum aluminum plating process, wherein the longitudinal stretching temperature is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Outer layer thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat-sealable matte printed aluminized composite packaging film for cigarettes and a preparation method thereof. The composite packaging film comprises a printed matte film and an aluminized film which are laminated and processed by use of a binder or a hot melt adhesive, wherein the printed layer of the matte film can be laminated with the aluminized layer of the aluminized film to obtain the composite packaging film. The composite packaging film provided by the invention has the following advantages: a heat-sealable matte film is creatively proposed to be adopted asa printed packaging film; after inner printing of the inner surface of the matte film, the printed layer of the matte film is laminated with the surface of the aluminized layer of the aluminized film, so the problem of additional coating of a matting coating on the surface of a conventional cigarette packaging film is solved; meanwhile, the matted layer and the aluminized film have medium-and-low-temperature heat sealability, so a film can be packaged and bonded without the need of using a glue when a cigarette is subsequently packaged on a machine; and the composite packaging film provided by the invention realizes medium-and-low-temperature heat sealability and matte effects on the basis of guaranteeing conventional functions, effectively reduces energy consumption, is friendly to the environment, and has a matte metal texture.

Description

technical field [0001] The invention belongs to the technical field of novel polymer packaging materials, and in particular relates to a composite packaging film for heat-sealable matte printing aluminized cigarettes and a preparation method thereof. Background technique [0002] Traditional cigarette packaging uses paper of a certain grammage, with a designed pattern printed on the surface. After packaging cigarettes online at high speed, the paper is folded into a specific shape, and the inside and outside of the paper are bonded and packaged after the edge is dispensed. Because paper fibers are easy to absorb water vapor in the air, water vapor will affect cigarettes through continuous adsorption and penetration, not only affecting the taste, but also endangering health. Therefore, a layer of transparent film is often wrapped outside the carton, and the film is usually made of polypropylene material, which is not only soft, but also has heat-sealing and heat-shrinking pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/32B32B27/18B32B27/08B32B27/06B32B7/12B32B33/00B32B37/12B32B38/14B65D65/40B29C47/06
Inventor 安德利蔡怀远高伟
Owner SUZHOU KUNLENE FILM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com