Novel low-silver-content alloy with blue luster, corrosion resistance and color change resistance for Miao silver jewelry

A technology of corrosion resistance and silver content, applied in the field of alloys, can solve the problems of vulcanization blackening, lack of corrosion resistance, acceleration, etc., and achieve the effect of color and appearance repair, excellent casting performance, and avoiding dendrites

Inactive Publication Date: 2018-11-13
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of alloy does not have sufficient corrosion resistance to discolor after use, or the vulcanization and blackening are accelerated due to wear and tear out of the base alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Miao silver jewelry is a new low-silver content alloy with blue luster and corrosion-resistant discoloration. In terms of weight percentage, the composition of the alloy is B:0.4wt.%, Li:1.8wt.%, Mo:0.4wt.%, W:0.3wt.%, Sc:1.2wt.%, Ni:4.0wt.% , Ag: 40.0wt.%, the balance is copper. The above-mentioned new low-silver content alloy with blue luster and corrosion resistance and discoloration for the above-mentioned Miao silver jewelry comprises the following steps: adding the raw materials in the above ratio into an induction furnace under an argon environment, and using a graphite crucible; melting at 1400 degrees Keep warm for 10 minutes, stir evenly with high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1400 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is rolled at room temperature, and the amount of reduction in...

Embodiment 2

[0022] Miao silver jewelry is a new low-silver content alloy with blue luster and corrosion-resistant discoloration. In terms of weight percentage, the composition of the alloy is B:0.6wt.%, Li:2.5wt.%, Mo:0.6wt.%, W:0.5wt.%, Sc:1.5wt.%, Ni:6.0wt.% , Ag: 50.0wt.%, the balance is copper. The above-mentioned new low-silver content alloy with blue luster and corrosion resistance and discoloration for the above-mentioned Miao silver jewelry comprises the following steps: adding the raw materials in the above ratio into an induction furnace under an argon environment, and using a graphite crucible; melting at 1400 degrees Keep warm for 10 minutes, stir evenly with high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1400 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is rolled at room temperature, and the amount of reduction in...

Embodiment 3

[0025] Miao silver jewelry is a new low-silver content alloy with blue luster and corrosion-resistant discoloration. In terms of weight percentage, the composition of the alloy is B:0.5wt.%, Li:1.9wt.%, Mo:0.5wt.%, W:0.4wt.%, Sc:1.4wt.%, Ni:4.5wt.% , Ag: 45.0wt.%, the balance is copper. The above-mentioned new low-silver content alloy with blue luster and corrosion resistance and discoloration for the above-mentioned Miao silver jewelry comprises the following steps: adding the raw materials in the above ratio into an induction furnace under an argon environment, and using a graphite crucible; melting at 1400 degrees Keep warm for 10 minutes, stir evenly with high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 1400 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is rolled at room temperature, and the amount of reduction in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel low-silver-content alloy with blue luster, corrosion resistance and color change resistance for Miao silver jewelry. The novel low-silver-content alloy comprises, by weight, 0.4%-0.6% of B, 1.8%-2.5% of Li, 0.4%-0.6% of Mo, 0.3%-0.5% of W, 1.2%-1.5% of Sc, 4.0%-6.0% of Ni, 40.0%-50.0% of Ag and the balance copper. The material supplies a materials science solution for a Miao silver alloy in China, therefore, a Miao silver product can have the blue luster after being machined, and the alloy has the excellent corrosion resistance and color change resistance. Through implementation and industrialization of the material, the product updating and industry upgrading requirements in the jewelry industry in China can be effectively met, and the plenteous economic gains and social benefits can be achieved while industry problems are solved.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a silver alloy. Background technique [0002] The price of sterling silver is relatively low among precious metals. Because of its good ductility and soft texture, it can be processed into various forms. It has been loved by people since ancient times and is widely used in the manufacture of jewelry, tableware and various decorations. Sterling silver is soft, although it is convenient for the processing of traditional jewelry, it is not conducive to inlaying gemstones. Moreover, due to the low hardness, after the jewelry is worn, small scratches will be produced on the surface, which will reduce the surface gloss and affect the appearance. In order to overcome these shortcomings of pure silver, people add various alloying elements to silver to improve the mechanical and other properties of silver, which forms a silver alloy. [0003] Adding a very small amount of alloying elemen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C30/02C22C5/08C22C9/00C22C1/02C22F1/08C22F1/14C23C8/12
CPCC22C30/02C22C1/02C22C5/08C22C9/00C22F1/08C22F1/14C23C8/12
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap