A kind of synthetic method of [60] fullerene cyclopentanone and [60] fullereno 2-cyclohexenone compound

A technology for cyclohexenones and synthesis methods, which is applied in the preparation of organic compounds, the preparation of carbon-based compounds, chemical instruments and methods, etc., can solve the problems of substrate limitations, environmental pollution, etc. The effect of good rate and functional group compatibility

Active Publication Date: 2021-06-04
HENAN NORMAL UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, transition metal-involved methods are substrate-limited and environmentally polluting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of synthetic method of [60] fullerene cyclopentanone and [60] fullereno 2-cyclohexenone compound
  • A kind of synthetic method of [60] fullerene cyclopentanone and [60] fullereno 2-cyclohexenone compound
  • A kind of synthetic method of [60] fullerene cyclopentanone and [60] fullereno 2-cyclohexenone compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Preparation of [60]fullerenocyclopentanones 2a:

[0015]

[0016] Reaction steps:

[0017] 0.05mmol C 60 , 0.015mmol catalyst 0.015mmol sodium ethoxide, 0.05mmol p-benzoquinone and 0.15mmol substrate 1a Add to a 25mL dry Shrek tube, then add dry 4mL anhydrous o-dichlorobenzene and 1mL anhydrous dichloromethane, seal the Shrek tube, ultrasonically dissolve the reactant completely, and then place it in a nitrogen atmosphere React in an oil bath at 90°C, stop the reaction after TLC detects that the reaction is complete, cool to room temperature, filter out the insoluble matter first, then spin off the organic solvent under reduced pressure, pack the column with thin-layer chromatography silica gel, load the sample by wet method, and use Carbon disulfide was eluted as an eluent to obtain the target product [60]fullerenocyclopentanone compound 2a, and the relative yield of product 2a was 56%.

[0018] 2a: 1 H NMR (400MHz, CDCl 3 / CS 2 )δ7.69(d, J=7.6Hz, 2H), 7.42...

Embodiment 2

[0023] Preparation of [60]fullerenocyclopentanone 2b:

[0024]

[0025] Reaction steps:

[0026] 0.05mmol C 60 , 0.015mmol catalyst 0.015mmol sodium ethoxide, 0.05mmol p-benzoquinone and 0.15mmol substrate 1b Add to a 25mL dry Shrek tube, then add dry 4mL anhydrous o-dichlorobenzene and 1mL anhydrous dichloromethane, seal the Shrek tube, ultrasonically dissolve the reactant completely, and then place it in a nitrogen atmosphere React in an oil bath at 90°C, stop the reaction after TLC detects that the reaction is complete, cool to room temperature, filter out the insoluble matter first, then spin off the organic solvent under reduced pressure, pack the column with thin-layer chromatography silica gel, load the sample by wet method, and use Carbon disulfide was eluted as an eluent to obtain the target product [60]fullerenocyclopentanone compound 2b, and the relative yield of product 2b was 67%.

[0027] 2b: 1 H NMR (400MHz, CDCl 3 / CS 2 )δ7.60(d, J=8.4Hz, 2H), 6.93(...

Embodiment 3

[0032] Preparation of [60]fullerenocyclopentanone 2c:

[0033]

[0034] Reaction steps:

[0035] 0.05mmol C 60 , 0.015mmol catalyst 0.015mmol sodium ethoxide, 0.05mmol p-benzoquinone and 0.15mmol substrate 1c Add to a 25mL dry Shrek tube, then add dry 4mL anhydrous o-dichlorobenzene and 1mL anhydrous dichloromethane, seal the Shrek tube, ultrasonically dissolve the reactant completely, and then place it in a nitrogen atmosphere React in an oil bath at 110°C, stop the reaction after TLC detects that the reaction is complete, cool to room temperature, filter out the insoluble matter first, then spin off the organic solvent under reduced pressure, pack the column with thin-layer chromatography silica gel, load the sample by wet method, and use Carbon disulfide was eluted as an eluent to obtain the target product [60]fullerenocyclopentanone compound 2c, and the relative yield of product 2c was 45%.

[0036] 2c: 1 H NMR (400MHz, CDCl 3 / CS 2 )δ7.69(dd, J=8.8,5.2Hz,2H),7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for synthesizing [60] fullerenocyclopentanone and [60] fullereno 2-cyclohexenone compounds, belonging to the technical field of synthesis of fullerene derivatives. The main points of the technical scheme of the present invention are: with C 60 and α,β ‑Unsaturated aldehydes were used as raw materials, and the organic small molecular nitrogen heterocyclic carbene was used as a catalyst to achieve the direct acylation of [60] fullerene through the polarity inversion strategy of aldehydes to obtain the target product [60] fullerene and Cyclopentanone and [60]fullereno-2-cyclohexenones. The invention uses organic small molecular catalyst nitrogen heterocyclic carbene, no metal is involved in the reaction process, and the synthesis process is green and environmentally friendly; the substrate has a wide application range and good functional group compatibility; it has high yield and is suitable for large-scale preparation.

Description

technical field [0001] The invention belongs to the technical field of synthesis of fullerene derivatives, in particular to a method for synthesizing [60] fullerene cyclopentanone and [60] fullerene 2-cyclohexenone compounds. Background technique [0002] The wide application of fullerene derivatives in the fields of optoelectronic materials and biomedicine has made the chemical modification of fullerenes aroused extensive attention of chemists. By chemical method in C 60 The introduction of different groups on the surface to improve its physical and chemical properties such as solubility, energy level and electron affinity, and the modification of fullerenes is a current research hotspot. The traditional method of modifying fullerene is mainly cycloaddition reaction. In recent years, the method involving transition metals has shown high efficiency and attracted widespread attention. However, transition metal-involved methods are substrate-limited and pollute the environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C45/45C07C49/697C07C49/755C07C49/683
CPCC07C45/455C07C49/683C07C49/697C07C49/755C07C2603/97
Inventor 刘统信张朋玲张贵生胡贝贝
Owner HENAN NORMAL UNIV