Welding method of large-scale stainless steel tank under high-temperature, high-humidity and blown sand environment

A welding method and stainless steel technology, applied in welding equipment, welding/welding/cutting items, arc welding equipment, etc., can solve the problems of inconvenient welding of large stainless steel tanks, long welding stress release time, wet weld bead, etc., to achieve The welding quality is good, the design is strict, and the effect of avoiding welding deformation

Inactive Publication Date: 2018-12-07
MCC5 GROUP CORP SHANGHAI
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Usually, the welding stress of the tank will be released after the welding construction is completed, but the welding stress release time of the large stainless steel tank under the environment of high temperature, high humidity and wind and sand is longer than that of the normal welding, and the welding deformation will be caused after the release. The welding deformation of the tank has clear requirements in the specification API650, and the deformation must be within the range
However, in a high-humidity environment, the tank wall is deformed due to wet weld bead or rain during welding, so how to control the welding deformation in tank construction is a difficult problem
[0004] Therefore there is above-mentioned inconvenience and problem in the welding mode of known large-scale stainless steel tank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The welding method of the large-scale stainless steel tank tank under high temperature, high humidity, sandstorm environment of the present invention, comprises the following steps:

[0034] a. Preparations before welding construction, including the following steps:

[0035] (1) Welder assessment: Welders who participate in welding must have a certificate of qualification for large-scale stainless steel tank welding projects. They must pass the on-site assessment in accordance with the requirements of the Saudi SABIC standard and obtain a welder qualification certificate before they can engage in welding within the scope of the qualified examination items. Work;

[0036] (2) Prepare welding process card

[0037] Welding procedure card: Welding procedure assessment shall be carried out on site according to the relevant regulations of Saudi Arabian SABIC and American standard ASME, and the welding procedure card shall be prepared according to the selection of procedure a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a welding method of a large-scale stainless steel tank under a high-temperature, high-humidity and blown sand environment. The welding method is characteristics by comprising the following steps that a, preparatory work before welding construction is carried out; b, welding measure regulations are carried out; and c, welding environment regulations are carried out. Comparedwith usual welding, the welding method of the large-scale stainless steel tank under the high-temperature, high-humidity and blown sand environment has the characteristics of longer welding stress relief time under the high-temperature, high-humidity and blown sand environment, the welding method of the large-scale stainless steel tank under the high-temperature, high-humidity and blown sand environment has the advantages that welding technical measures are designed closely, the operability is high, a welding stress relief method after the tank welding construction completed is buffered successfully, and welding deformation caused after release is avoided, and the welding quality of a tank meets standards of Saudi SABIC and America ASME.

Description

technical field [0001] The invention relates to tank welding in the field of petrochemical industry, in particular to a welding method for large stainless steel tanks under high temperature, high humidity and windy sand environment. Background technique [0002] The large-scale stainless steel tank project in Saudi Arabia with 20,000 cubic meters, tank diameter of 38m, tank height of 24.55m, and tank wall height of 19.1m is located on the sandy soil of the Persian Gulf seaside. High difficulty. During the welding construction process of the tank, the American ASME standard and the Saudi SABIC standard are combined and mutually complementary for inspection and acceptance. [0003] Usually, the welding stress of the tank will be released after the welding construction is completed, but the welding stress release time of the large stainless steel tank under the environment of high temperature, high humidity and wind and sand is longer than that of the normal welding, and the w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K9/00B23K9/235B23K101/12B23K103/04
CPCB23K9/00B23K9/235
Inventor 廖兴银唐敏任鸿赵洪浩卢伟张昊
Owner MCC5 GROUP CORP SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products