Novel plant fiber flame retardant adhesive and preparation method thereof

A plant fiber, adhesive technology, applied in the direction of aldehyde/ketone condensation polymer adhesive, adhesive type, starch adhesive, etc., can solve the problem of poor fire resistance, difficult to achieve fire resistance, safety performance and decoration effect, impact and other issues, to achieve durable fire resistance, improve weather resistance and coloring effect, and enhance the effect of compression resistance

Active Publication Date: 2018-12-07
中山市富门木制品有限公司
View PDF11 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wood is an indispensable material for modern decoration and decoration projects. The amount of wood used in modern decoration projects is increasing, and the quality requirements are getting higher and higher. It is difficult for ordinary wood to achieve fire resistance, safety performance and decorative effects.
At present, the adhesives used in flame-retardant solid wood multi-layer decorative panels have poor fire resistance, and generally contain formaldehyde solvents, which will affect the human body or the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel plant fiber flame retardant adhesive and preparation method thereof
  • Novel plant fiber flame retardant adhesive and preparation method thereof
  • Novel plant fiber flame retardant adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A new flame-retardant adhesive for plant fibers, comprising the following components: 4g of trisodium phosphate, 50g of magnesium sulfate solution, 2g of calcium hydroxide, 3g of emulsifier, 60g of starch glue, 25g of phenolic resin, 3g of tartaric acid, 1g of boric acid, oxidized Magnesium 110g, silica 3g and lithopone 2g.

[0022] The preparation method of the starch glue is as follows: starch and water are heated and gelatinized at a mass ratio of 0.12-0.2:1.

[0023] The concentration of the magnesium sulfate solution is 17-25 ° of Baume.

[0024] The emulsifier is fatty alcohol polyoxyethylene ether, preferably OS-15.

[0025] A preparation method of the above-mentioned plant fiber novel flame-retardant adhesive, comprising the following steps:

[0026] Step 1. Heat starch and water at a mass ratio of 0.12-0.2:1 to 70-90°C for gelatinization, then cool to room temperature to prepare starch glue;

[0027] Step 2, stirring and mixing lithopone, trisodium phosphate...

Embodiment 2

[0030] A new type of flame-retardant adhesive for plant fibers, comprising the following components: 3g of trisodium phosphate, 50g of magnesium sulfate solution, 5g of calcium hydroxide, 4g of emulsifier, 75g of starch glue, 28g of phenolic resin, 4g of tartaric acid, 3g of boric acid, oxidized Magnesium 118g, silica 4g and lithopone 3g.

[0031] The preparation method of the starch glue is as follows: starch and water are heated and gelatinized at a mass ratio of 0.12-0.2:1.

[0032] The concentration of the magnesium sulfate solution is 17-25 ° of Baume.

[0033] The emulsifier is fatty alcohol polyoxyethylene ether, preferably OS-15.

[0034] A preparation method of the above-mentioned plant fiber novel flame-retardant adhesive, comprising the following steps:

[0035] Step 1. Heat starch and water at a mass ratio of 0.12-0.2:1 to 70-90°C for gelatinization, then cool to room temperature to prepare starch glue;

[0036] Step 2, stirring and mixing lithopone, trisodium p...

Embodiment 3

[0039] A new type of plant fiber flame retardant adhesive, comprising the following components: 2g of trisodium phosphate, 35g of magnesium sulfate solution, 4g of calcium hydroxide, 2g of emulsifier, 22g of starch glue, 12g of phenolic resin, 2g of tartaric acid, 2g of boric acid, oxidation Magnesium 105g, silica 2g and lithopone 1g.

[0040] The preparation method of the starch glue is as follows: starch and water are heated and gelatinized at a mass ratio of 0.12-0.2:1.

[0041] The concentration of the magnesium sulfate solution is 17-25 ° of Baume.

[0042] The emulsifier is fatty alcohol polyoxyethylene ether, preferably OS-15.

[0043] A preparation method of the above-mentioned plant fiber novel flame-retardant adhesive, comprising the following steps:

[0044] Step 1. Heat starch and water at a mass ratio of 0.12-0.2:1 to 70-90°C for gelatinization, then cool to room temperature to prepare starch glue;

[0045] Step 2, stirring and mixing lithopone, trisodium phosp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a novel plant fiber flame retardant adhesive and a preparation method thereof. The novel plant fiber flame retardant adhesive comprises the following components in parts by weight: 1-4 parts of trisodium phosphate, 30-75 parts of magnesium sulfate solution, 1-5 parts of calcium hydroxide, 1-4 parts of an emulsifier, 20-80 parts of starch glue, 10-30 parts of phenolic resin,2-4 parts of tartaric acid, 1-3 parts of boric acid, 105-118 parts of magnesia, 2-5 parts of silica and 1-3 parts of a colorant; The concentration of the magnesium sulfate solution is 17-25 degree Be,and that preparation method of the starch glue comprise the following step of: heating and gelatinizing starch and water according to the mas ratio of 0.12-0.2: 1. The novel plant fiber flame retardant adhesive of the invention has durable and excellent fire resistance, water resistance and environmental protection performance. The novel plant fiber flame retardant adhesive does not contain harmful substances such as formaldehyde, benzene and the like, and is energy-saving, environment-friendly and safe.

Description

technical field [0001] The invention relates to the field of flame-retardant adhesives, in particular to a novel flame-retardant adhesive for plant fibers and a preparation method thereof. Background technique [0002] Wood is an indispensable material for modern decoration and decoration projects. The amount of wood used in modern decoration projects is increasing, and the quality requirements are getting higher and higher. It is difficult for ordinary wood to achieve fire resistance, safety performance and decorative effects. At present, the adhesives used in flame-retardant solid wood multi-layer decorative boards have poor fireproof performance, and generally contain formaldehyde solvent, which will affect the human body or the environment. Contents of the invention [0003] In order to solve the above problems, the present invention provides a new type of flame-retardant adhesive for plant fibers, which is safe and environmentally friendly, and has durable fireproof p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/02C09J161/06C09J11/06C09J11/04
CPCC08K2003/222C08K2003/3045C08K2003/324C08L2201/02C08L2201/08C08L2205/03C09J11/04C09J11/06C09J103/02C08L61/06C08K13/02C08K3/22C08K3/32C08K3/30C08K3/36
Inventor 傅福信黄军定
Owner 中山市富门木制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap