A technology of nonlinear optics and boronite, which is applied in the field of nonlinear optical devices containing boronite crystals, and can solve problems such as the difficulty of deep ultraviolet nonlinear optical crystals

Active Publication Date: 2021-05-11
FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, from a structural point of view, the UV absorption edge and nonlinear coefficient of the crystal are usually contradictory, and it is extremely difficult to obtain a deep ultraviolet nonlinear optical crystal with excellent performance through structural design and optimization.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nonlinear Optical Devices Containing Peroborite Crystals
  • Nonlinear Optical Devices Containing Peroborite Crystals
  • Nonlinear Optical Devices Containing Peroborite Crystals

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] Embodiment 1 molten salt method grows boborite crystal

[0067] (1) Pre-calcined boronite: using analytically pure MgCl 2 、H 3 BO 3 As the initial raw material, according to Mg 3 B 7 o 13 Cl stoichiometry, MgCl 2 and H 3 BO 3 Excess 1wt% and 3wt% respectively carry out weighing, mixing, grinding, tabletting, and then put into a furnace, and pre-fire at 800-900° C. for two hours.

[0068] (2) crystal growth: adopt molten salt method to grow boborite crystal, comprise the following steps: pre-burned boborite and flux (flux is MgCl 2 and H 3 BO 3 According to the mixture of 1:1 in molar ratio, to ensure that the impurity phase is not introduced), weigh and mix according to the molar ratio of 1:1, put it into a platinum crucible, put the crucible into the center of the molten salt furnace, and cover the furnace cover; The temperature was raised to 1200°C at a rate of 50°C per hour, melted, and kept for two days, then lowered to room temperature at a rate of 50°C ...

Embodiment 2

[0069] Embodiment 2 molten salt method grows boborite crystal

[0070] (1) Pre-calcined boronite: using analytically pure MgO, MgCl 2 、H 3 BO 3 As the initial raw material, according to Mg 3 B 7 o 13 Cl stoichiometric ratio, MgO, MgCl 2 and H 3 BO 3 Weigh, where MgCl 2 and H 3 BO 3 Excessive 3wt% and 5wt%, respectively, mixed, ground, pressed into a furnace, and pre-fired at 800-900°C for two hours.

[0071] (2) crystal growth: adopt molten salt method to grow boborite crystal, comprise the following steps: pre-burned boborite and flux (flux is MgCl 2 and H 3 BO 3 According to the molar ratio of 3:1 mixture), weigh and mix according to the molar ratio of 1:2, put it into a platinum crucible, put the crucible in the center of the molten salt furnace, and cover the furnace cover; heat up at a rate of 50°C per hour Melt at 1180°C, keep warm for two days, then cool down to room temperature at a rate of 50°C per hour, wash with water, and obtain boronite crystals.

Embodiment 3

[0072] Embodiment 3 molten salt method grows boborite crystal

[0073] (1) Pre-calcined boronite: using analytically pure MgCl 2 、H 3 BO 3 As the initial raw material, according to Mg 3 B 7 o 13 Cl stoichiometric ratio, MgCl 2 and B 2 o 3 Weigh, where MgCl 2 Excess 2wt%, after mixing, grinding and tableting, put into furnace, and pre-fire at 800-900°C for two hours.

[0074] (2) crystal growth: adopt molten salt method to grow boborite crystal, comprise the following steps: pre-burned boborite and flux (flux is MgCl 2 and H 3 BO 3 According to the molar ratio of 3:1 mixture), weigh and mix according to the molar ratio of 1:4, put it into a platinum crucible, put the crucible in the center of the molten salt furnace, cover the furnace cover; heat up at a rate of 50 ° C per hour Melt at 1150°C, keep warm for two days, then cool down to room temperature at a rate of 50°C per hour, wash with water, and obtain boronite crystals.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
remanent polarizationaaaaaaaaaa
Login to view more

Abstract

The present invention provides a nonlinear optical device, the nonlinear optical device comprises a boronite crystal, wherein the boronite crystal is periodically polarized. The nonlinear optical device is a device that passes at least one beam of incident electromagnetic radiation through at least one boborite crystal to generate at least one beam of output radiation with a frequency different from that of the incident electromagnetic radiation. The wavelength range of the incident electromagnetic radiation is 0.155-4.0 μm. Peroborite crystal is a kind of photoelectric information functional crystal with ferroelectricity and deep ultraviolet nonlinearity. The nonlinear optical device made of peroborite crystal adopts quasi-phase matching technology (the quasi-phase matching is to use periodic pole In this way, the periodic inversion of the ferroelectric domain is realized by applying a pulse voltage to the boraxite crystal), and the output of deep ultraviolet electromagnetic radiation can be realized.

Description

technical field [0001] The invention relates to a nonlinear optical device, in particular to a 3 B 7 o 13 Cl) Nonlinear optical devices of crystals. Background technique [0002] With the development of modern laser technology, the laser wavelengths that can be directly obtained by using laser crystals are limited, and it is impossible to achieve full-band laser output. From ultraviolet to infrared spectral regions, there are still blank bands, especially in the deep ultraviolet region. Due to its unique nonlinear effects, such as frequency doubling, sum frequency, difference frequency, and parametric amplification, nonlinear optical crystals can effectively broaden the wavelength range of laser light. Using the nonlinear effect of crystals can be used to make a variety of nonlinear optical devices such as second harmonic generators, up-down frequency converters, and optical parametric oscillators. The electromagnetic radiation generated by the laser can be converted in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G02F1/355G02F1/35C30B29/10C30B9/12
CPCC30B9/12C30B29/10G02F1/353G02F1/3534G02F1/3551
Inventor 龙西法王祖建
Owner FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap