Polypropylene material having scratch resistance and indentation resistance and preparation method thereof

A polypropylene material and anti-indentation technology, which is applied in the field of polypropylene material with anti-scratch and anti-indentation properties and its preparation field, can solve the problems of aging resistance, easy bridging, and no cutting, etc., and achieve easy production, The surface friction coefficient is reduced and the method is simple and feasible

Inactive Publication Date: 2018-12-28
江苏兆维塑料科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the mica powder has a flake structure, it is easy to bridge in the actual processing process, and there will be a phenomenon that the material will not be cut.
In addition, in order to maintain the flaky structure of mica powder, manufacturers on the market usually use wet processing methods to obtain mica powder by grinding. Such powder contains a large amount of metal ions and is not resistant to aging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Provide a polypropylene material with anti-scratch and anti-indentation properties, including the following components: polypropylene, talc powder, toughening agent, high-density polyethylene HDPE, silicone masterbatch, antioxidant, polytetrafluoroethylene Vinyl fluoride, additives. The toughening agent is polyolefin elastomer POE, the silicone masterbatch can also be called scratch-resistant agent, the auxiliary agent is black masterbatch, and polytetrafluoroethylene is also an anti-indentation agent. The content of each component of the polypropylene material with anti-scratch and anti-indentation properties is: 57-78 parts of polypropylene, 10-20 parts of talcum powder, 30 parts of polyolefin elastomer POE, 70 parts of high-density polyethylene HDPE 0-3 parts of anti-scratch agent, 0.2 parts of first antioxidant, 0.1 part of second antioxidant, 0.1 part of third antioxidant, 1.5 parts of black masterbatch, 0.3-2 parts of anti-indentation agent. Specifically: the con...

Embodiment 2

[0025] Provide a polypropylene material with anti-scratch and anti-indentation properties, the content of each component is: polypropylene 780kg, talc powder 150kg, polyolefin elastomer POE 30kg, high-density polyethylene HDPE 70kg, scratch-resistant agent 20kg , 2kg of the first antioxidant, 1kg of the second antioxidant, 1kg of the third antioxidant, 10kg of black masterbatch, and 5kg of anti-indentation agent. The raw materials and properties of the components and the preparation method of the polypropylene material are the same as those in Example 1.

Embodiment 3

[0027] Provide a polypropylene material with anti-scratch and anti-indentation properties. The content of each component is: polypropylene 670kg, talcum powder 200kg, polyolefin elastomer POE 30kg, high-density polyethylene HDPE 70kg, scratch-resistant agent 30kg , 2kg of the first antioxidant, 1kg of the second antioxidant, 1kg of the third antioxidant, 10kg of black masterbatch, and 5kg of anti-indentation agent. The raw materials and properties of the components and the preparation method of the polypropylene material are the same as those in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polypropylene material having scratch resistance and indentation resistance and a preparation method thereof. The polypropylene material includes polypropylene, talcum powder, toughening agent, high density polyethylene (HDPE), silicone masterbatch, antioxidant, polytetrafluoroethylene and auxiliary agent. The preparation method includes evenly mixing the components to obtain the polypropylene material. According to the polypropylene material having scratch resistance and indentation resistance and the preparation method thereof, the indentation resistance of the polypropylene material is effectively improved, the surface friction coefficient of the polypropylene is reduced, the scratch resistance is improved, the method is simple and feasible, and the polypropylene material is easy to produce.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polypropylene material with anti-scratch and anti-indentation properties and a preparation method thereof. Background technique [0002] With the increasing development and growth of the automobile industry, lightweight and replacing steel with plastic have become the main theme of the automobile industry. Modified polypropylene has been widely used in the interior and exterior decoration of automobiles, and the requirements for the appearance and performance of automobile interior and exterior decoration materials have also been continuously improved. [0003] Polypropylene interior and exterior trims are prone to collisions during use, assembly, and transportation, resulting in color differences at the collision parts and affecting product appearance. At present, the surface can be smoothed and the surface friction coefficient can be reduced by adding amides or pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L23/08C08L23/06C08L83/04C08L27/18C08K5/134C08K5/526
CPCC08L23/12C08L23/14C08L2205/035C08L2207/062C08L23/0815C08L23/06C08L83/04C08L27/18C08K5/1345C08K5/526
Inventor 赵振华章立清章立军饶福康叶辉
Owner 江苏兆维塑料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap