A preparation process and technology for rubber stoppers, which are applied in the field of preparation of silicone-free rubber stoppers, can solve the problems of uniform coating on the surface of unfavorable rubber stoppers, the film is easy to fall off, and the adhesion of the film material is not strong. Good aging performance, excellent chemical corrosion resistance and temperature resistance, the effect of solving friction and bottle mouth jam
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] Example 1 The preparation process of the silicone-free rubber stopper includes the steps of mixing rubber, rubber sheeting, compression vulcanization forming, slitting, cleaning and drying, and packaging. It also includes sequential coating of polydimethylmethylmethacrylate on the surface of the rubber stopper after cleaning and drying. Base siloxane prepolymer solution and polyvinylidene fluoride resin dispersion and coating drying and curing steps;
[0023] Among them, the main components of the polydimethylsiloxane prepolymer solution are end-capped polydimethylsiloxane prepolymer, silane crosslinking agent and organic solvent;
[0024] The main composition of the polyvinylidene fluoride resin dispersion is a polyvinylidene fluoride resin emulsion with a solid content of 5 to 15% and a silicone rubber catalyst.
[0025] The composition of the polydimethylsiloxane prepolymer solution is 100 parts of the hydroxy-terminated polydimethylsiloxane of the rubber ...
Example Embodiment
[0027] Example 2-3
Example Embodiment
[0028] The difference between Example 2 and Example 1 is that it includes 1 part of blocked polydimethylsiloxane prepolymer, 0.5 part of silane crosslinking agent and 100 parts of organic solvent A in parts by weight, and polyvinylidene fluoride resin is dispersed. The weight percentage of the silicone rubber catalyst in the liquid is 0.001%; the main composition of the polyvinylidene fluoride resin dispersion liquid is a polyvinylidene fluoride resin emulsion with a solid content of 15% and a silicone rubber catalyst. The silicone rubber in the polyvinylidene fluoride resin dispersion liquid The weight percentage of the catalyst is 0.001%.
[0029] The drying temperature of the coating is 160°C, and the coating curing includes two steps of room temperature curing and high temperature curing in sequence. The room temperature curing time is 36h, the high temperature curing temperature is 200°C, and the high temperature curing time is 5-10 minutes. The organic solvent A is aceton...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap