A method for preventing roll marks from producing medium-high carbon hot-rolled strip steel

A hot-rolled strip steel, medium-high carbon technology, applied to the driving device of metal rolling mill, metal rolling, metal rolling, etc., can solve the problem that the roll cannot be completely prevented from being damaged, and achieve the purpose of preventing strip steel roll marks, preventing The effect of excessive cooling

Active Publication Date: 2020-10-09
湖南华菱涟源钢铁有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process, to adjust the flow of cooling water in the finishing mill, needs to collect process parameters in time and give feedback, and only for the adjustment of cooling water flow in the finishing mill, it cannot completely prevent the damage of the rolls, and then in the strip roller print

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preventing roll marks from producing medium-high carbon hot-rolled strip steel
  • A method for preventing roll marks from producing medium-high carbon hot-rolled strip steel
  • A method for preventing roll marks from producing medium-high carbon hot-rolled strip steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0036]An embodiment of the present invention, a method for preventing roll marks from being produced on medium-high carbon hot-rolled steel strip, comprises the following steps:

[0037] S01: Obtain the values ​​of the finishing temperature of hot rolling, the thickness and width of strip steel 1 after hot rolling;

[0038] S02: According to the hot-rolling finishing temperature, the thickness and width of the strip 1 after hot rolling, separately control the closing or opening of each water cooling device in the finishing mill, and control the strip 1 in the seventh finishing mill F7 Maximum threading speed in the frame.

[0039] According to the order of the finishing mills biting the steel, the finishing mills successively include the first finishing mill F1, the second finishing mill F2, the third finishing mill F3, the fourth finishing mill F4, the fifth finishing mill F5, and the sixth finishing mill F6, the seventh finishing mill F7;

[0040] Wherein, the weight perce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of manufacturing of steel and discloses a method for preventing generation of roll marks of hot rolled steel strips with a medium and high content of carbon. The method comprises the steps of obtaining hot rolling final rolling temperature and values of the thickness and width of the steel strips after hot rolling; according to the hot rolling final rolling temperature and the values of the thickness and width of the steel strips after hot rolling, separately controlling closing or opening of each water cooling device in a finishing rolling unit alone and controlling the maximum strip passing speed of the steel strips in a rack of a seventh finishing rolling machine. By comprehensively controlling closing or opening of each water cooling devicein the finishing rolling unit, controlling the strip passing speed of the rack of the seventh finishing rolling machine and controlling the diameter of a working roller of the rack of the seventh finishing rolling machine, the generation of the roll marks on the steel strips can be effectively controlled.

Description

technical field [0001] The invention belongs to the technical field of iron and steel manufacturing, and in particular relates to a method for preventing roll marks from occurring on medium-high carbon hot-rolled strip steel. Background technique [0002] In the rolling production process of hot-rolled steel coils, after the slab is heated by the heating furnace, it is descaled by the rough descaling machine and rolled by the rough rolling mill to form an intermediate billet with good surface quality. scale mill, and then enter the finishing mill, where the strips are gradually thinned and rolled into target thickness strips in each finishing mill. According to the traditional control method, the thinned strips will encounter roll gap spray water, Longitudinal water spraying and cooling water cooling between the stands, the temperature of the head of the strip gradually decreases after encountering water; the head of the strip is cooled by water between the F1-F5 stands of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/22B21B37/74B21B37/16B21B37/22B21B45/02
CPCB21B1/22B21B37/165B21B37/22B21B37/74B21B45/0218B21B2001/225B21B2275/02
Inventor 刘浩曾斌李光辉汪净刘旭辉罗钢黄建波
Owner 湖南华菱涟源钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com