An ag with visible light response 2 znsns 4 /mo structured photoanode and its preparation method and application
A structured light and visible light technology, applied in chemical instruments and methods, electrodes, chemical/physical processes, etc., to achieve excellent photoelectric conversion efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0054] Example 1 Ag 2 ZnSnS 4 Preparation of / Mo structured photoanode
[0055] (1) Ultrasonic cleaning of molybdenum mesh:
[0056] First use 5mol / L concentrated hydrochloric acid and 5mol / L concentrated sodium hydroxide solution to ultrasonically clean for 1.0 hours (frequency 40KHz), then use acetone, deionized water and ethanol to ultrasonically clean for 1.0 hour (frequency 40KHz), after ultrasonic cleaning The surface of molybdenum mesh presents a metallic luster.
[0057] (2) Deposit metal Ag:
[0058] First configure 100ml of 0.01mol / L silver nitrate solution, and then deposit metallic silver on the molybdenum grid by controlling the deposition voltage and deposition charge. The deposition voltage is 0.0V Vs SCE (calomel electrode), and the deposition charge is 0.8C / cm 2 , to obtain the Ag / Mo precursor.
[0059] (3) Deposit metal Sn:
[0060] First configure the 0.02mol / L stannous chloride solution of 100ml, then deposit metal tin on the Ag / Mo net by control...
Embodiment 2
[0065] Example 2 Ag with different Zn / Sn / Ag deposition charges 2 ZnSnS 4 Preparation of / Mo structured photoanode This example prepares Ag with different Zn / Sn / Ag deposition charges 2 ZnSnS 4 / Mo structure photoanode, prepared 2 kinds of photoanodes altogether, its preparation method is the same as embodiment 1, difference is: the first kind is to deposit these three kinds of metal elements in step (2)(3)(4) in embodiment 1 The simultaneous reduction of charge is: 0.4C / cm 2 (Ag), 0.8C / cm 2 (Sn), 0.8C / cm 2 (Zn); the second is to increase the amount of these three kinds of metal element deposition charge in step (2) (3) (4) in embodiment 1 while being: 1.2C / cm 2 (Ag), 2.4C / cm 2 (Sn), 2.4C / cm 2 (Zn). However, these two Ag 2 ZnSnS 4 The ratio of deposited charges in the Zn / Sn / Ag precursor in the / Mo structured photoanode remains 2.0:2.0:1.0.
[0066] Schematic diagram of a synthetic photoanode:
[0067] Embodiment 1 and 2 prepare Ag 2 ZnSnS 4 The specific steps o...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com