Expanding type smoke-suppression flame retardant for waterborne coating and preparation method thereof

A technology of water-based coatings and flame retardants, applied in the preparation of intumescent smoke-suppressing flame retardants for water-based coatings, in the field of intumescent smoke-suppressing flame retardants for water-based coatings, can solve the problem of hindering evacuation and rescue operations and affecting victims And the health and life safety of disaster relief personnel, to achieve good isolation of combustion gas, good foaming, and improve the effect of environmental protection

Active Publication Date: 2019-03-01
中创(重庆)防火材料有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the expansion process of flame-retardant coatings, with the release of a large amount of non-combustible gases, the coating layer is also heated to release a large amount of smoke and toxic gases, including smoke particles, CO, etc., which seriously affect the health and safety of victims and rescuers. Safety of life, hindering evacuation and rescue operations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Expanding type smoke-suppression flame retardant for waterborne coating and preparation method thereof
  • Expanding type smoke-suppression flame retardant for waterborne coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The intumescent smoke-suppressing flame retardant for water-based coatings of this embodiment consists of water and the following components in parts by weight: 24 parts of boric acid, 36 parts of polyphosphate amine, 20 parts of phosphoguanidinourea, 36 parts of pentaerythritol, and 30 parts of melamine parts, 1.4 parts of sulfonated carbon, 3.6 parts of zinc borate, and 2.4 parts of ammonium octamolybdate.

[0035] Using the above-mentioned intumescent smoke-suppressing flame retardant to prepare intumescent water-based fire-proof and flame-retardant coatings for wood materials, it also includes water and the following components in parts by weight: 200 parts of melamine-modified urea-formaldehyde resin emulsion, ethylene-vinyl acetate copolymer emulsion 110 parts, 18 parts of paint additives, 36 parts of pigment and filler titanium dioxide; the solid content of the paint is 50%.

[0036] Wherein, the coating aid is composed of film-forming aids, dispersants, defoamer...

Embodiment 2

[0047] The intumescent smoke-suppressing flame retardant for water-based coatings of this embodiment consists of water and the following components in parts by weight: 22 parts of boric acid, 38 parts of polyphosphate amine, 22 parts of phosphoguanidinourea, 38 parts of pentaerythritol, and 32 parts of melamine. parts, 1.3 parts of sulfonated carbon, 4.0 parts of zinc borate, and 2.0 parts of ammonium octamolybdate.

[0048] Using the above-mentioned intumescent smoke-suppressing flame retardant to prepare intumescent water-based fire-proof and flame-retardant coatings for wood materials, it also includes water and the following components in parts by weight: 200 parts of melamine-modified urea-formaldehyde resin emulsion, ethylene-vinyl acetate copolymer emulsion 115 parts, 16 parts of paint additives, 34 parts of pigment and filler titanium dioxide; the solid content of the paint is 51%.

[0049] Wherein, the coating aid is composed of film-forming aids, dispersants, defoame...

Embodiment 3

[0060] The intumescent smoke-suppressing flame retardant for water-based coatings of this embodiment consists of water and the following components in parts by weight: 20 parts of boric acid, 38 parts of polyphosphate amine, 24 parts of phosphoguanidinourea, 40 parts of pentaerythritol, and 30 parts of melamine -34 parts, 1.2 parts of sulfonated carbon, 3.8 parts of zinc borate, 2.2 parts of ammonium octamolybdate.

[0061] Using the above-mentioned intumescent smoke-suppressing flame retardant to prepare intumescent water-based fire-proof and flame-retardant coatings for wood materials, it also includes water and the following components in parts by weight: 200 parts of melamine-modified urea-formaldehyde resin emulsion, ethylene-vinyl acetate copolymer emulsion 120 parts, 20 parts of paint additives, 38 parts of pigment and filler titanium dioxide; the solid content of the paint is 52%.

[0062] Wherein, the coating aid is composed of film-forming aids, dispersants, defoamer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an expanding type smoke-suppression flame retardant for waterborne coating and a preparation method thereof. The smoke-suppression flame retardant is prepared from the following components in parts by weight: 20 to 24 parts of boric acid, 36 to 38 parts of amine polyphosphate, 20 to 24 parts of amidinourea phosphate, 36 to 40 parts of pentaerythritol, 30 to 34 parts of melamine, 1.0 to 1.4 parts of sulfonated carbon, 3.6 to 4.0 parts of zinc borate and 2.0 to 2.4 parts of ammonium octamolybdate. The expanding type smoke-suppression flame retardant provided by the invention is used for preparing waterborne fireproofing flame-retarding coating for surface coating of a wood material; the combustion of the wood material can be greatly delayed in a heating process and fire spreading is inhibited; the waterborne fireproofing flame-retarding coating for the wood material, which is prepared from the expanding type smoke-suppression flame retardant, has the advantages that good smoke-suppression performance is realized; the smoke generation time can be delayed and the release amount of smoke and the generation of toxic gas are reduced; and more safe time and space are provided for escaping and rescuing of people under a fire condition.

Description

technical field [0001] The invention belongs to the technical field of water-based paints, in particular to an intumescent smoke-suppressing flame retardant for water-based paints, and also relates to a preparation method of the intumescent smoke-suppressing flame retardants for water-based paints. Background technique [0002] Wood materials have the advantages of environmental protection, non-toxicity, strong processability and renewable, and are widely used in furniture, construction and interior decoration and other fields. However, untreated wood materials are not fire-resistant, flammable and have fire spread, which will increase the fire risk in the place of use, and there is a serious safety hazard. In order to effectively reduce the occurrence of fires, the country has formulated a series of laws, regulations and safety standards, requiring materials and products used in buildings, indoors or public places to reach the corresponding flame retardant level, which requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/18C09D161/32C09D123/08C09D7/61
CPCC08K2003/323C08K2003/387C08L2201/02C09D5/185C09D161/32C09D7/61C08L23/0853C08K13/02C08K3/32C08K3/38C08K5/053C08K5/34922C08K3/04C08K3/24C08K5/29
Inventor 李竑靓
Owner 中创(重庆)防火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com