Graphene polyurethane sponge and application thereof

A technology of polyurethane sponge and graphene, which is applied in electrical components, magnetic field/electric field shielding, etc., can solve the problems of frequency bandwidth of only 2.62GHz, decrease of wave-absorbing performance, and affect waterproof effect, etc., so as to improve wave-absorbing performance and service life , reduce reflectivity, solve the effects of shedding and water absorption

Inactive Publication Date: 2019-03-29
BEIJING SCITECH GRAPHENE TECH CO LTD
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN104163919A discloses a polyaniline / graphene oxide / ferric oxide absorbing material and a preparation method thereof. The material has a minimum reflection loss value of -46.5dB within 2-18GHz, but the frequency band where the reflection loss value is lower than -10dB Only 2.62GHz wide
However, polyurethane wave-absorbing sponges used in rainy seasons and outdoors need to have high-efficiency waterproof ability, otherwise the waterproof effect will be affected and the wave-absorbing performance will be reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene polyurethane sponge and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0044] Preparation of graphene dispersion:

[0045] Preparation of secondary expanded graphite: Put 5g of graphite into a 500mL three-necked flask, immerse the three-necked flask in the ice-water mixture, then add 45mL of concentrated nitric acid and 87.5mL of concentrated sulfuric acid, and slowly add 55g of potassium chlorate to the three-necked flask Medium (adding time is at least more than 15 minutes. Note: Chlorine dioxide will be produced when potassium chlorate is added, and an explosion will occur when the concentration is high), this process is stirred for 72 hours, and the treated graphite is washed into neutrality with a large amount of water, and dried Finally, the powder is obtained; then the oxidized graphite is placed in a tube furnace, and the expansion time is 30 seconds to 5 minutes and the temperature is 1000-1300°C, and the high temperature reduction is carried out to obtain the primary expanded graphite, and the primary expanded graphite is treated by th...

Embodiment 1

[0048] The graphene dispersion was prepared in the same manner as in Preparation Example 1 except that N,N-dimethylcyclohexylamine was used as the dispersion medium.

[0049] Graphene polyurethane sponge is formed by foaming the following raw materials, and the parts by weight of each component are:

[0050] 100 parts of polyether 560D, 0.15 part of catalyst A1, 0.34 part of catalyst stannous octoate, 1.2 parts of silicone oil L580, 3 parts of water, 10 parts of graphene N,N-dimethylcyclohexylamine dispersion (the content of graphene is 10%), 5 parts of N,N-dimethylcyclohexylamine dispersion of hydroxyl iron powder (5% content of hydroxyl iron powder), and 48.3 parts of toluene diisocyanate TDI-80.

[0051] The foaming method is as follows:

[0052] Control the ambient temperature at 21°C, weigh the above polyether, catalyst, water, foam stabilizer, graphene dispersion and hydroxyl iron powder dispersion according to the formula, add them to the material bucket, and mix and s...

Embodiment 2

[0054] A graphene dispersion was prepared in the same manner as in Preparation Example 1 except that bis(2-dimethylaminoethyl) ether was used as the dispersion medium.

[0055] Graphene polyurethane sponge is formed by foaming the following raw materials, and the parts by weight of each component are:

[0056] Bis(2-dimethylaminoethyl) ether dispersion (( The content of graphene is 10%), 10 parts of triethylamine dispersion liquid of hydroxyl iron powder (the content of hydroxyl iron powder is 8%), and 30 parts of hexamethylene diisocyanate.

[0057] The foaming method is as follows:

[0058] Control the ambient temperature at 20°C, weigh the above polyether, catalyst, foam stabilizer, water, silicone oil, graphene dispersion, and hydroxyl iron powder dispersion according to the formula and add them to the material bucket, and use a mixer (speed 1000rad / min) Mix and stir for 30s, let it stand for 4min, then weigh the toluene diisocyanate and pour it into the material mixing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
optical bandwidthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a graphene polyurethane sponge and an application thereof. The graphene polyurethane sponge is prepared from a composition comprising polyether polyol, an amine-based catalyst, a tin-based catalyst, a foam stabilizer, water, a graphene dispersion, a carbonyl iron powder dispersion and an isocyanate. The graphene polyurethane sponge is a superhydrophobic sponge, and has a high mechanical strength and a large specific surface area, so multiple scattering of electromagnetic waves inside the sponge is highly benefited, thereby the loss of electromagnetic waves is reduced,and the total reflectivity of electromagnetic waves is reduced.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a graphene polyurethane sponge and an application thereof. Background technique [0002] Due to its unique properties such as surface effect, quantum size effect, and Hall effect, and its low density and easy processing, graphene has attracted much attention in the field of microwave-absorbing materials. Graphene has obvious defects and residual oxygen-containing functional groups, which not only improve the impedance matching characteristics, promote the timely conversion of energy from adjacent states to the Fermi level, but also generate defect polarization relaxation and functional group electronic dipole polarization. Relaxation, these are conducive to the absorption of electromagnetic waves. At present, there are many reports on the preparation of multi-component composite materials by combining magnetic materials, conductive polymers and graphene as electromag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08K3/04C08K3/18H05K9/00C08G101/00
CPCC08G18/48C08K3/18C08K3/042C08G2110/0083H05K9/0081
Inventor 朱英孔壮
Owner BEIJING SCITECH GRAPHENE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap