Method for forming thin-walled sheet metal parts

A forming method and technology of sheet metal parts, which are applied in the field of sheet metal forming, can solve the problems of increased resistance to movement of guide rails, failure to meet the use requirements, and inability to guarantee the size of the part surface, so as to ensure the size of the surface and save knocking Process, the effect of reducing labor intensity

Active Publication Date: 2020-06-19
CHINA HANGFA GUIZHOU LIYANG AVIATION POWER CO LTD
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the processing of the part, the part is released from the mold by tapping from one end (see the schematic diagram of the fitting of the part and the mold figure 2 ), due to the close contact between the four sides of the part and the mold, the surface size of the part cannot be guaranteed, which increases the movement resistance of the guide rail and cannot meet the use requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for forming thin-walled sheet metal parts
  • Method for forming thin-walled sheet metal parts
  • Method for forming thin-walled sheet metal parts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The technical scheme of the present invention will be further described below in conjunction with the accompanying drawings, but the required protection scope is not limited to the description;

[0030] Such as figure 1 and Figure 7 Shown is the final size drawing of the parts processed by the present invention and the schematic diagram of the position of each bending section. The thin-walled sheet metal part includes a first side, a second side and a third side connected in sequence, the length of the first side is greater than the third side, and the first side and the third side are perpendicular to the second side side, and the first side and the third side are located on the same side of the second side, the first S-shaped curved section 1 is arranged on the first side, and the second S-shaped curved section 4 is arranged on the third side, The first side is connected to the second side through the first right-angle bending section 2, the second side is connecte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a shaping mold and method of thin-wall sheet metal parts. The mold consists of three sets of sub molds including a first bending mold, a second bending mold and a third bendingmold (wherein each set of sub mold consists of a female mold and a male mold). When spare parts are processed, the three sets of sub molds are bent according to the sequence of the mold 1, the mold 2and the mold 3, and the bending positions are shown as the figure 3. The specific processing technology of the spare parts comprises the steps of performing blanking, performing bending for the firsttime,...performing bending for the second time,...and performing bending. The mold disclosed by the invention is simple to operate, the profile size of the spare parts can be guaranteed, the labor intensity of workers can be reduced, and the production efficiency of the spare parts can be improved.

Description

technical field [0001] The invention belongs to the field of mechanical processing, and in particular relates to sheet metal forming of a "ji"-shaped thin-walled part. Background technique [0002] "Ji"-shaped guide rail groove (for the structural diagram of the parts, see figure 1 ) The material is 0Cr17Ni7Al, the thickness of the material is t1.0, and the length of the groove of the part is L=618.5 +0.5 mm. At present, the molding process used for this type of parts is: after two extrusion and bending moldings, the parts are separated from the molding die; blanking-initial bending...-bending-...knocking repair-correction. During the processing of the part, the part is released from the mold by tapping from one end (see the schematic diagram of the fitting of the part and the mold figure 2 ), due to the close contact between the four sides of the part and the mold, the surface size of the part cannot be guaranteed, which increases the movement resistance of the guide ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21D5/00B21D37/10B23K26/00B23K26/38
CPCB21D5/00B21D37/10B23K26/0093B23K26/38
Inventor 武国栋文金龙申静芳李立新刘兴红方志忠黄顺殷炳开邱树彬井启芳张顺
Owner CHINA HANGFA GUIZHOU LIYANG AVIATION POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products