Pouring type granulated asphalt and preparing method thereof

A pouring and asphalt technology, which is applied in building structure, building components, building insulation materials, etc., can solve the problems of high cost, poor safety, complex asphalt preparation process, etc., to save energy, reduce carbon emissions, and enrich manufacturing technology Effect

Pending Publication Date: 2019-04-16
北京紫瑞天成科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the embodiment of the present invention provides a cast-type granulated asphalt and its preparation method to solve the problem of complex asphalt preparation process, poor safety, high cost and difficulty in meeting the requirements of ordinary heavy traffic asphalt or polymer modification in the prior art. Problems with asphalt granulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pouring type granulated asphalt and preparing method thereof
  • Pouring type granulated asphalt and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The preparation method of the cast-type granulated asphalt provided in Example 1 of the present invention, the cast-type granulated asphalt is composed of the following materials in parts by weight:

[0029] 10 parts of high-quality asphalt for shell material, 70 parts of No. 70 bitumen for inner core material, 0.2 parts of sulfenamide accelerator, 8 parts of sodium thiosulfate, 1 part of paraffin oil, and 4 parts of terpene resin;

[0030] Its preparation method concrete operation is:

[0031] S1: Pre-melt the high-quality asphalt of the shell material, the temperature of the pre-melt treatment is 210°C, and heat-insulate the No. 70 bitumen of the inner core material, and set the temperature of the heat-insulation treatment to 120°C;

[0032] S2: adding the sulfenamide accelerator to the shell material high-quality asphalt for mixing, melting and stirring to obtain the first mixture, wherein the mixing and melting stirring speed is 30r / min, and the stirring time is 15m...

Embodiment 2

[0037] The preparation method of the cast-type granulated asphalt provided in Example 2 of the present invention, the cast-type granulated asphalt is composed of the following materials in parts by weight:

[0038] 5 parts of No. 10 bitumen for shell material, 80 parts of No. 90 bitumen for inner core material, 0.3 parts of thiuram accelerator, 5 parts of polycyclic aromatic hydrocarbon sodium sulfonate, 1.5 parts of rosin oil, and 3 parts of C9 petroleum resin;

[0039] Its preparation method concrete operation is:

[0040] S1: Carry out pre-melting treatment on No. 10 asphalt of the shell material, the temperature of the pre-melting treatment is 200°C, and heat preservation treatment of No. 90 pitch of the inner core material, and the temperature of the heat preservation treatment is set to 110°C;

[0041] S2: adding the thiuram accelerator to the shell material No. 10 asphalt for mixing, melting and stirring to obtain the first mixture, wherein the speed of mixing, melting ...

Embodiment 3

[0046] The preparation method of the cast-type granulated asphalt provided in Example 3 of the present invention, the cast-type granulated asphalt is composed of the following materials in parts by weight:

[0047] 15 parts of No. 30 bitumen for shell material, 60 parts of No. 110 bitumen for inner core material, 0.4 part of octadecanoic acid, 7 parts of sodium sulfoaluminate, 1.5 parts of rosin oil, and 3 parts of C9 petroleum resin;

[0048] Its preparation method concrete operation is:

[0049] S1: Carry out pre-melting treatment on asphalt No. 30 of the shell material, the temperature of the pre-melting treatment is 190 ° C, and heat preservation treatment of No. 110 bitumen of the inner core material, and the temperature of the heat preservation treatment is set to 100 ° C;

[0050] S2: Add octadecanoic acid to shell material No. 30 asphalt for mixing, melting and stirring to obtain the first mixture, wherein the speed of mixing, melting and stirring is 35r / min, and the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The embodiment of the invention discloses pouring type granulated asphalt and a preparing method thereof. The asphalt comprises an outer shell material, an inner core material, an accelerant, a delaying agent, a plasticizer and an adhesive. The pouring type granulated asphalt can be directly added into a mixing vat, asphalt granules are smashed and molten through high shearing force and heat of collected materials, an asphalt mixture is mixed, and the defect that liquid asphalt needs to be transported by heat insulation vehicles and needs to be stored at a high temperature after reaching the site is avoided; the liquid asphalt can be stored and transported at a normal temperature, energy is saved, the circular economy is developed, and the environment harmonious development is protected.

Description

technical field [0001] The embodiment of the present invention relates to the technical field of asphalt granulation manufacturing, in particular to a pouring granulated asphalt and a preparation method thereof. Background technique [0002] Crude oil undergoes deep processing in petrochemical refineries, and light components go downstream to produce high value-added products. Heavy component bitumen raw materials also play a vital role in the infrastructure construction process. Asphalt raw materials require high temperatures during storage and transportation. Components such as polycyclic aromatic hydrocarbons that are volatile for a long time are harmful to health. The development of a kind of asphalt that can be stored and transported at room temperature is an important measure for the coordinated development of energy conservation, development of circular economy, and environmental protection. [0003] In the process of asphalt road construction, heavy traffic asphalt a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08J3/12
CPCC08J3/126C08J2395/00C08J2495/00
Inventor 于小桥倪腾亚汪海胡晓亮于越梁清源
Owner 北京紫瑞天成科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products