Corrosion-resisting steel with yield strength of 450 MPa for coal open-boxcar and manufacturing method thereof

Abstract

The invention discloses a corrosion-resisting steel with yield strength of 450 MPa for a coal open-boxcar and a manufacturing method thereof. The corrosion-resisting steel is prepared from 0.034%-0.069% of C, 0.21%-0.29% of Si, 0.45%-1.0% of Mn, less than or equal to 0.018% of P, less than or equal to 0.006% of S, 0.015%-0.045% of Als, 0.35%-0.89% of Cr, 0.11%-0.19% of Ni, 0.25%-0.38% of Cu, 0.012%-0.021% of Ti, 0.041%-0.089% of Sb, 0.028%-0.069% of Sn, 0-0.19% of Mo, 0-0.0019% of B, 0.0008%-0.0030% of Ca, and the balance Fe and inevitable impurities. The method includes steps of heating a plate blank being 135-170 mm thick to the temperature of 1228-1249 DEG C, rough rolling the plate blank at the temperature greater than 1100 DEG C, finish rolling the plate blank at the temperature of 1000-1100 DEG C, carrying out final rolling on the plate blank at the temperature of 830-895 DEG C, and coiling the plate at the temperature of 580-650 DEG C. The steel plate has excellent resistance tosulfuric acid and chloride ion corrosion.

Description

technical field [0001] The invention belongs to the field of steel for railway vehicles, and relates to a corrosion-resistant steel suitable for use in a corrosion environment containing acidic medium and chloride ions and a manufacturing method thereof. Background technique [0002] Ordinary steel gondola cars are usually only subject to atmospheric corrosion, while coal transport gondola cars are attacked by a rather harsh corrosive environment. First of all, coal contains sulfides that have a strong chemical corrosion effect on steel; moreover, because water is used to shock coal during mining, the coal contains water, and when coal is transported in winter, certain salts must be added to prevent freezing. In order to lower the freezing point, this brings extremely corrosive chloride ions. [0003] At present, the manufacturing materials used for coal transport gondolas are aluminum alloy, stainless steel or traditional weathering steel. Although aluminum alloy and stai...

AI Technical Summary

Problems solved by technology

[0010] Aiming at the technical problems existing in the production of steel for coal-carrying gondolas at present, for example: the use of aluminum alloy and stainless steel is relatively expensive, the welding and formability are not good, and the corrosion resistance of the existing steel cannot meet the requirements, so the present invention is proposed Technical solutions

Images