A kind of one-component aqueous acrylic acid dispersion and preparation method thereof

A water-based acrylic and dispersion technology, applied in the direction of coating, etc., can solve the problems of construction inconvenience and achieve the effect of improving gloss, hardness and weather resistance

Active Publication Date: 2021-05-14
湖北双键精细化工有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Water-based hydroxyacrylic dispersion cannot be used as a one-component self-drying coating due to the limitation of the synthesis process. It needs to be combined with an isocyanate curing agent to make a two-component coating. It brings some inconvenience to the construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The preparation method of the one-component aqueous acrylic acid dispersion provided in this embodiment is as follows:

[0029] (1), weigh each component according to the following parts by mass:

[0030] 280 parts of isopropanol

[0031] The first mixed solution: (200 parts of methyl methacrylate; 50 parts of styrene; 50 parts of cyclohexyl methacrylate; 70 parts of butyl methacrylate; 5 parts of butyl acrylate; 5 parts of isooctyl acrylate; 100 parts of isobornyl acrylate; 2 parts of vinyltrimethoxysilane; 3 parts of pentaerythritol tetraacrylate; 4.8 parts of azobisisobutyronitrile)

[0032] The second mixed solution (15 parts of acrylic acid; 80 parts of methyl methacrylate; 10 parts of butyl acrylate; 15 parts of butyl methacrylate; 1 part of pentaerythritol tetraacrylate; 1.6 parts of azobisisobutyronitrile)

[0033] Dimethylethanolamine 16.8 parts

[0034] 720 parts of deionized water

[0035] (2), firstly add the solvent isopropanol into the four-necked flas...

Embodiment 2

[0046] The preparation method of the one-component aqueous acrylic acid dispersion provided in this embodiment is as follows:

[0047] (1), weigh each component according to the following parts by mass:

[0048] 300 parts of isopropanol

[0049] The first mixed solution: (220 parts of methyl methacrylate; 45 parts of styrene; 40 parts of cyclohexyl methacrylate; 80 parts of butyl methacrylate; 10 parts of butyl acrylate; 3 parts of isooctyl acrylate; 80 parts of isobornyl acrylate; 3 parts of vinyltrimethoxysilane; 3.5 parts of pentaerythritol tetraacrylate; 5.5 parts of azobisisobutyronitrile)

[0050] The second mixed solution (17 parts of acrylic acid; 85 parts of methyl methacrylate; 12 parts of butyl acrylate; 13 parts of butyl methacrylate; 1.5 parts of pentaerythritol tetraacrylate; 2 parts of azobisisobutyronitrile)

[0051] 18 parts of triethylamine

[0052] 700 parts of deionized water

[0053] (2), firstly add the solvent isopropanol into the four-necked flask of ...

Embodiment 3

[0060] The preparation method of the one-component aqueous acrylic acid dispersion provided in this embodiment is as follows:

[0061] (1), weigh each component according to the following parts by mass:

[0062] 290 parts of isopropanol

[0063] The first mixed solution: (180 parts of methyl methacrylate; 40 parts of styrene; 45 parts of cyclohexyl methacrylate; 70 parts of butyl methacrylate; 8 parts of butyl acrylate; 1 part of isooctyl acrylate; 120 parts of isobornyl acrylate; 1 part of vinyltrimethoxysilane; 2.5 parts of pentaerythritol tetraacrylate; 4.5 parts of benzoyl peroxide)

[0064] The second mixed solution (16 parts of acrylic acid; 75 parts of methyl methacrylate; 8 parts of butyl acrylate; 16 parts of butyl methacrylate; 0.5 parts of pentaerythritol tetraacrylate; 1.5 parts of benzoyl peroxide)

[0065] Dimethylethanolamine 16.8 parts

[0066] 700 parts of deionized water

[0067] (2), firstly add the solvent isopropanol into the four-necked flask of the r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-performance one-component water-based acrylic dispersion and a preparation method thereof. The provided one-component water-based acrylic dispersion comprises the following components: isopropanol, (meth)acrylate, vinyl Monomer, Acrylic and / or Methacrylic Acid, Pentaerythritol Tetraacrylate, Initiator, Neutralizer, Deionized Water. The one-component water-based acrylic dispersion provided by the present invention is easy to use and operate. Compared with the two-component paint, the link of paint mixing is omitted. Good, high hardness, good water resistance, good weather resistance and so on. More importantly, the VOC (volatile organic compound) of the one-component water-based acrylic dispersion provided by the present invention can reach 0, which is very environmentally friendly.

Description

technical field [0001] The invention relates to a high-performance water-based acrylic dispersion, in particular to a single-component water-based acrylic dispersion, which belongs to the technical field of water-based coatings. Background technique [0002] In the social environment with increasingly stringent environmental protection requirements, it has long been the general trend for water-based paints to replace oil-based paints. Water-based hydroxyacrylic secondary dispersions have developed rapidly in recent years and are widely used in the field of industrial coatings. The hydroxyl group in the water-based hydroxyacrylic secondary dispersion and the isocyanate group in the isocyanate curing agent can react and cross-link to form a network structure. The water-based two-component coating made of the two has high gloss, high fullness, high Hardness, excellent chemical resistance, good water resistance, good weather resistance, etc., are widely used in industrial coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/14C08F220/18C08F212/08C08F230/08C08F222/14C08F220/06C09D133/12
CPCC08F220/14C09D143/04C08F220/18C08F220/1804C08F212/08C08F230/08C08F222/104C08F220/06
Inventor 高州柴广刘志鸿田军马世凯胡勇军董威游仁国雷木生
Owner 湖北双键精细化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com