A sic whisker with c-alpo 4 Preparation method of powder synergistically modified mullite coating

A synergistic modification and mullite technology, which is applied in the field of high-temperature anti-oxidation/anti-corrosion coating preparation, can solve the difficulties in the preparation of large components and special-shaped parts, the precise control of difficult coating thickness, and the poor bonding force between the coating and the substrate and other problems, to achieve the effect of improving easy cracking, improving dynamic erosion resistance, and low preparation cost

Active Publication Date: 2021-08-24
CENT SOUTH UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, the existing preparation processes such as electron beam physical vapor deposition and atmospheric plasma spraying have the problems of expensive equipment and high production cost; while the coating prepared by sol-gel combined with dipping-pulling method will have coatings at the corners Uneven fine distribution and poor bonding between the coating and the substrate make it difficult to achieve precise control of the coating thickness. The most important thing is that it is difficult to meet the preparation of large components and special-shaped parts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A sic whisker with c-alpo <sub>4</sub> Preparation method of powder synergistically modified mullite coating
  • A sic whisker with c-alpo <sub>4</sub> Preparation method of powder synergistically modified mullite coating
  • A sic whisker with c-alpo <sub>4</sub> Preparation method of powder synergistically modified mullite coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Step 1 Preparation of mullite precursor gel by sol-gel method

[0044] Dissolve 20.83g of tetraethyl orthosilicate and 112.53g of aluminum nitrate nonahydrate in 100ml of absolute ethanol, add 3.60g of glacial acetic acid, heat and react in a water bath at 60°C for 4 hours, then raise the temperature to 80°C for 16 hours in a water bath to obtain a mullite precursor to obtain a milky white mullite precursor gel A;

[0045] Step 2 Preparation of mullite powder by sol-gel method

[0046] Dissolve 20.83g of tetraethyl orthosilicate and 112.53g of aluminum nitrate nonahydrate in 100ml of ethanol, add 3.60g of glacial acetic acid, heat and react in a water bath at 60°C for 4 hours, then raise the temperature to 80°C for 16 hours in a water bath to obtain the mullite precursor gel. Gel and gel are dried at 60-80°C for 72 hours, then ball-milled at 200r / min for 2 hours, then put into a muffle furnace, set the heating rate at 5°C / min, kept at 1300°C for 2 hours, and then coole...

Embodiment 2

[0054] Step 1 Preparation of mullite precursor gel by sol-gel method

[0055] Dissolve 20.83g of tetraethyl orthosilicate and 112.53g of aluminum nitrate nonahydrate in 100ml of absolute ethanol, add 3.60g of glacial acetic acid, heat and react in a water bath at 60°C for 4 hours, then raise the temperature to 80°C for 16 hours in a water bath to obtain a mullite precursor to obtain a milky white mullite precursor gel A;

[0056] Step 2 Preparation of mullite powder by sol-gel method

[0057] Dissolve 20.83g of tetraethyl orthosilicate and 112.53g of aluminum nitrate nonahydrate in 100ml of ethanol, add 3.60g of glacial acetic acid, heat and react in a water bath at 60°C for 4 hours, then raise the temperature to 80°C for 16 hours in a water bath to obtain the mullite precursor gel. Gel and gel are dried at 60-80°C for 72 hours, then ball-milled at 200r / min for 2 hours, then put into a muffle furnace, set the heating rate at 5°C / min, kept at 1300°C for 2 hours, and then coole...

Embodiment 3

[0065] Step 1 Preparation of mullite precursor gel by sol-gel method

[0066] Dissolve 20.83g of tetraethyl orthosilicate and 112.53g of aluminum nitrate nonahydrate in 100ml of absolute ethanol, add 3.60g of glacial acetic acid, heat and react in a water bath at 60°C for 4 hours, then raise the temperature to 80°C for 16 hours in a water bath to obtain a mullite precursor The gel was left to age in a sealed environment at room temperature for 4 to 6 months to obtain a milky white mullite precursor gel A.

[0067] Step 2 Preparation of mullite powder by sol-gel method

[0068] Dissolve 20.83g of tetraethyl orthosilicate and 112.53g of aluminum nitrate nonahydrate in 100ml of ethanol, add 3.60g of glacial acetic acid, heat and react in a water bath at 60°C for 4 hours, then raise the temperature to 80°C for 16 hours in a water bath to obtain the mullite precursor gel. Gel and gel are dried at 60-80°C for 72 hours, then ball-milled at 200r / min for 2 hours, then put into a muffl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a kind of SiC whisker and C-AlPO 4 The preparation method of powder synergistically modified mullite coating, selects C / SiC composite material as the substrate, prepares SiC inner coating by chemical vapor deposition method, and then uses sol- Preparation of SiC Whiskers and C‑AlPO by Gel Combined with Air Spray Process 4 Powder synergistic modification of mullite coating precursor, and finally SiC whiskers and C-AlPO can be obtained by sintering 4 Powder synergistic modification of mullite coatings. This method improves the shortcomings of the coating prepared by the traditional sol-gel process, such as easy cracking, uneven distribution, and low bonding strength, and can meet the control of micron-level coating thickness. It has the advantages of simple preparation process, low preparation cost and high preparation efficiency. , can meet many advantages such as the preparation of large-scale components and heterogeneous components, is convenient for large-scale industrial application, and has broad development prospects.

Description

technical field [0001] The invention relates to a SiC whisker and C-AlPO 4 The invention discloses a method for preparing a powder synergistically modified mullite coating, which belongs to the technical field of high-temperature anti-oxidation / anti-corrosion coating preparation. Background technique [0002] C / SiC composite materials have certain oxidation resistance and good mechanical properties, showing the characteristics of low density, high strength, high toughness, high temperature resistance, ablation resistance, erosion resistance, high hardness and high wear resistance. C / SiC composite materials have broad application prospects in high-performance weaponry, aerospace, energy technology, chemical industry, transportation industry and other fields. However, since the carbon fiber and matrix carbon start to oxidize above 400°C, the SiC matrix starts to oxidize to SiO at a temperature above 1200°C 2 film, SiO 2 The film will react with the water vapor in the enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/185C04B35/81C04B35/622C04B35/624C04B35/626C04B41/89
Inventor 李杨肖鹏陈鹏举李专
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap