High-extinction low-VOC (volatile organic compound) nano matte assistant and preparation method thereof
A technology of matting additives and nano-modifiers, applied in electrophoretic coatings, coatings, etc., can solve the problems of increasing the hardness and fullness of the paint film, poor scratch resistance and rough surface of the paint film, etc., to achieve Increase hardness and fullness, not easy to agglomerate, strong matting effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0020] Example 1
[0021] This specific embodiment is a formulation of a nano matte additive with high matting properties and low VOC. The raw materials of the additive include: 1 part of vinyl triethoxysilane, 100 parts of nano alumina, 1 part of citric acid, and 100 parts of deionized water. .
[0022] The above formula is processed, and the processing steps are: add nano alumina and vinyl triethoxy silane to deionized water according to the raw material ratio, and stir evenly at 1000 RPM for pre-dispersion, and then use The nano sand mill grinds it to the nano-primary particle size, then adds citric acid to it to adjust the pH value to 6-7, and reacts at 1000RPM for 0.5 hours to obtain a high matte low VOC nano matte Additive sample 1.
Example Embodiment
[0023] Example 2
[0024] This specific embodiment is a formulation of a nano matte additive with high matting properties and low VOC. The raw materials of the additive include: 10 parts of 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, nano-nitriding 80 parts of aluminum, 5 parts of acetic acid, and 70 parts of deionized water.
[0025] The above formula is processed, and the processing steps are as follows: add nano aluminum nitride and 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane to deionized water according to the ratio of raw materials, and Stir uniformly at a rotation speed of 800RPM for pre-dispersion, then grind it to a nanometer primary particle size with a nano sand mill, then add acetic acid to it to adjust its pH to 6-7, and react at a rotation speed of 800RPM After 3 hours, sample 2 of nano matt additive with high matt property and low VOC was obtained.
Example Embodiment
[0026] Example 3
[0027] This specific embodiment is a formulation of a nano matte additive with high matting properties and low VOC. The raw materials of the additive include: 20 parts of bis(acetylacetonyl) ethoxy isopropoxy titanate, 50 parts of nano silica, 10 parts of oxalic acid, 50 parts of deionized water.
[0028] The above formula is processed, and the processing steps are as follows: add nano silica and bis(acetylacetonyl) ethoxy isopropoxy titanate to deionized water according to the ratio of raw materials, and rotate at 500 RPM Stir uniformly for pre-dispersion, and then grind it to a nanometer primary particle size with a nano sand mill, then add oxalic acid to adjust its pH to 6-7, and react at 500 RPM for 6 hours. Sample 3 of nano matte additives with high extinction and low VOC was obtained.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap