Water-based anti-scratch matte oil
An anti-scratch, dumb oil technology, applied in the direction of anti-corrosion coatings, coatings, polycarbonate coatings, etc., can solve the problems affecting the surface damage of electronic products, poor film adhesion performance, poor wear resistance, etc., to achieve Enhanced protective effect, good impact resistance and transparency, and the effect of reducing friction damage
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0012] see figure 1 , a water-based anti-scratch dumb oil, comprising the following components by weight percentage: polycarbonate 75%, organic leveling agent 0.9%, ceramic dispersion 3.5%, polyester polyurethane 13.5%, film-forming aid 3% agent, 0.4% substrate wetting agent, 0.4% surfactant, 1.2% mineral oil defoamer, 1.1% aziridine curing agent, and 1% de-watered;
[0013] Its usage is as follows:
[0014] The first step, polycarbonate 75%, silicone leveling agent 0.9%, ceramic dispersion 3.5%, polyester polyurethane 13.5%, film-forming aid 3%, substrate wetting agent 0.4%, surface active Agent 0.4%, mineral oil defoamer 1.2%, aziridine curing agent 1.1%, and the ratio of 1% deionized water mixed to obtain the mixture;
[0015] In the second step, the mixture obtained in the first step is evenly coated on the film;
[0016] The second step, after the above steps are completed, dry and solidify, and take it out to obtain the finished product of the matte oil protective fil...
Embodiment 2
[0018] A water-based anti-scratch dumb oil, comprising the following components by weight percentage: polycarbonate 80%, organic silicon leveling agent 0.5%, ceramic dispersion 3%, polyester polyurethane 11.5%, film-forming aid 2%, substrate wetting agent 0.2%, surfactant 0.3%, mineral oil defoamer 1%, aziridine curing agent 1%, and 0.5% deionized water;
[0019] Its usage is as follows:
[0020] The first step, polycarbonate 80%, organic leveling agent 0.5%, ceramic dispersion 3%, polyester polyurethane 11.5%, film-forming aid 2%, substrate wetting agent 0.2%, surface active 0.3% of antifoaming agent, 1% of mineral oil defoamer, 1% of aziridine curing agent, and 0.5% of deionized water are mixed to obtain the mixture;
[0021] In the second step, the mixture obtained in the first step is evenly coated on the film;
[0022] The third step, after the above steps are completed, dry and solidify, and take it out to obtain the finished product of the matte oil protective film. ...
Embodiment 3
[0024] A water-based anti-scratch dumb oil, comprising the following components by weight percentage: polycarbonate 85%, organic leveling agent 0.1%, ceramic dispersion 1%, polyester polyurethane 10%, film-forming aid 1%, substrate wetting agent 0.1%, surfactant 0.1%, mineral oil defoamer 0.5%, aziridine curing agent 1.5%, and 0.7% deionized water;
[0025] Its usage is as follows:
[0026] The first step, polycarbonate 85%, organic leveling agent 0.1%, ceramic dispersion 1%, polyester polyurethane 10%, film-forming aid 1%, substrate wetting agent 0.1%, surface active 0.1% of agent, 0.5% of mineral oil defoamer, 1.5% of aziridine curing agent, and 0.7% of deionized water are mixed to obtain the mixture;
[0027] In the second step, the mixture obtained in the first step is evenly coated on the film;
[0028] The second step, after the above steps are completed, dry and solidify, and take it out to obtain the finished product of the matte oil protective film.