Method for improving toughness of high-carbon equivalent steel plate welding heat affected zone through rare earth

A welding heat-affected zone and high carbon equivalent technology, which is applied in the direction of improving process efficiency and manufacturing converters, can solve problems such as easy aggregation and growth, and achieve the effect of inhibiting grain growth and improving performance

Active Publication Date: 2019-06-11
UNIV OF SCI & TECH BEIJING +1
View PDF16 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, Ti- and Ca-containing oxide inclusions are easy to aggregate and grow in molten steel, and the particle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving toughness of high-carbon equivalent steel plate welding heat affected zone through rare earth
  • Method for improving toughness of high-carbon equivalent steel plate welding heat affected zone through rare earth
  • Method for improving toughness of high-carbon equivalent steel plate welding heat affected zone through rare earth

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0032] The present invention will be further described below in conjunction with the embodiments.

[0033] The invention discloses a method for improving the toughness of the welding heat affected zone of a high carbon equivalent steel plate by using rare earth. Among them, the refining outside the furnace adopts the LF+vacuum degassing / RH process route, and adding rare earth alloys during the RH refining process, thereby newly forming fine and dispersed Ce inclusions containing rare earths and original inclusions modified by rare earths in the molten steel . These inclusions inhibit the growth of pre-austenite grains in the heat-affected zone during the welding process. At the same time, the addition of rare earth also delays the transformation of bainite in the heat-affected zone and inhibits the formation of upper bainite, thereby greatly increasing the height The toughness of the heat-affected zone of carbon equivalent thick plate welding.

[0034] Research on improving the i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for improving toughness of a high-carbon equivalent steel plate welding heat affected zone through rare earth, and belongs to the technical field of high-strength steel plates for welding. The method sequentially comprises the converter smelting step, LF refining step, RH refining step, continuous casting step, hot rolling step and thermal treatment step. According to the method, a certain amount of rare earth Ce alloy is added into molten steel during the RH refining process, inclusions in molten steel are modified into rare earth inclusions through rare earth, tiny new rare earth inclusions are generated in molten steel, and dispersed distribution of the rare earth inclusions is controlled; the tiny dispersed distribution rare earth Ce inclusions and original inclusions modified by rare earth newly generated in molten steel inhibit original austenite grains in the heat affected zone from growing during the welding process; and bainite transformationof the welding heat affected zone is delayed through addition of rare earth, formation of bainite is inhibited, and toughness of the high-carbon equivalent steel plate welding heat affected zone is greatly improved.

Description

technical field [0001] The invention belongs to the technical field of high-strength steel plates for welding, and in particular relates to a method for improving the toughness of welding heat-affected zones of high-carbon equivalent steel plates by using rare earth. Background technique [0002] The large-scale and high-rise development of steel for construction machinery and steel for building components requires steel plates to have higher strength and good welding performance. However, as the strength of the steel plate increases, its weldability decreases significantly, and the sensitivity to weld cracks increases. Especially for thick plates with high carbon equivalent, with the increase of welding heat energy, the grain size of prior austenite in the welding heat-affected zone increases significantly, forming a coarse-grained heat-affected zone, and the post-weld heat-affected zone is easy to form upper bainite structure, significantly reducing the toughness of the w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/10C21C7/064C21C5/28C21D1/18C21D8/02C22C38/38C22C38/28C22C38/26C22C38/24C22C38/22C22C38/06C22C38/02
CPCY02P10/20
Inventor 史成斌李晶陆斌智建国耿如明
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap