A production process of high-performance tool and die flat steel

A production process and tooling technology, which is applied in the field of high-performance tooling flat steel production process, can solve problems such as low yield rate, performance and parameters not meeting practical requirements, and difficult control of composition ratio, so as to achieve low cost, Easy processing and good product quality

Active Publication Date: 2020-05-19
四川丰元机械制造有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the common production process, a variety of ingredients need to be used, so the ratio of each ingredient is difficult to control
Often the properties and parameters of mold steel after processing and forming cannot meet the practical requirements, resulting in problems such as low yield
In the prior art, it is difficult to effectively solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production process of high-performance tool and die flat steel
  • A production process of high-performance tool and die flat steel
  • A production process of high-performance tool and die flat steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be further described in detail in conjunction with specific embodiments below.

[0029] The technical solution adopted in the present invention is: a production process of high-performance tool and die flat steel, comprising the following steps:

[0030] Step 1. Send the scrap steel and pig iron into the electric arc furnace. After melting, heat up to ≥1580°C. During the oxidation period, the amount of C removal is guaranteed to be ≥0.20%. The rate of C removal is 0.01% / min-0.03% / min. 0.10%;

[0031] Step 2: Send the molten steel into the LF furnace, adjust the slag, add C powder, Fe-Si powder and Si-Ca powder for reduction, fine-tune the composition after the temperature is ≥1580°C, and keep the slag in the furnace for ≥20 minutes after it turns white , after the ingredients are qualified and the temperature reaches 1670°C-1690°C, it will be released from the furnace;

[0032] Step 3. After pouring out 70%-80% of the slag, the molten steel ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Brinell hardnessaaaaaaaaaa
Brinell hardnessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-performance tool mold flat steel. The high-performance tool mold flat steel comprises, by weight percentage, 0.35%-0.40% of C, 0.70%-1.0% of Si, 0.30%-0.60% of Mn, smallerthan or equal to 0.010% of P, smaller than or equal to 0.005% of S, 5.20%-5.70% of Cr, 0.40%-0.60% of Ni, 1.30%-1.50% of Mo, 0.90%-1.20% of V, smaller than or equal to 0.10% of Cu, smaller than or equal to 0.010% of the combination of As, Sn, Pb, Sb and Bi and the balance Fe and inevitable impurity elements. The yield of the produced tool and mold flat steel is high, the inherent purity degree ishigh, few impurities exist, the organization is uniform, various mechanical properties are high, the energy is saved, and the cost is reduced.

Description

technical field [0001] The invention belongs to the field of alloy steel processing, and in particular relates to a production process of high-performance tool and mold flat steel. Background technique [0002] Die steel is a type of steel used to make molds such as cold stamping dies, hot forging dies, and die-casting dies. Its performance is mainly affected by material and heat treatment. It has very high requirements on the purity, cracks and mechanical properties of steel, and the harmful impurities such as P, S, H, O, N, As, Sn must also be strictly controlled. At present, in the common production process, multiple ingredients need to be used, so the ratio of each ingredient is difficult to control. Often the properties and parameters of mold steel after processing cannot meet the practical requirements, resulting in problems such as low yield. In the prior art, it is difficult to effectively solve the above problems. Contents of the invention [0003] The technic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/42C22C38/44C22C38/46C22C38/60C21C7/00C21C7/06C21C7/10C21D8/00C22C33/04
CPCY02P10/20
Inventor 余佑祥黄生权崔建强苏雄杰唐政良王洪祥鲁友名
Owner 四川丰元机械制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com