Phosphor, method for preparing phosphor, optoelectronic component, and method for producing optoelectronic component

A technology of optoelectronic devices and fluorescent materials, applied in the manufacturing process of optoelectronic devices, the field of optoelectronic devices

Active Publication Date: 2019-06-28
EVERLIGHT ELECTRONICS
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are no relevant reports on fluorescent materials that can generate a wider red visible-near-infrared spectrum and have higher rad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphor, method for preparing phosphor, optoelectronic component, and method for producing optoelectronic component
  • Phosphor, method for preparing phosphor, optoelectronic component, and method for producing optoelectronic component
  • Phosphor, method for preparing phosphor, optoelectronic component, and method for producing optoelectronic component

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0091] This embodiment provides a group of fluorescent materials whose general formula is La 3 Ga 1-y Ge 5 o 16 :yCr 3+ , where 0

[0092] La 3 Ga 0.995 Ge 5 o 16 :0.005Cr 3+

[0093] La 3 Ga 0.99 Ge 5 o 16 :0.01Cr 3+

[0094] La 3 Ga 0.97 Ge 5 o 16 :0.03Cr 3+

[0095] La 3 Ga 0.95 Ge 5 o 16 :0.05Cr 3+

[0096] La 3 Ga 0.93 Ge 5 o 16 :0.07Cr 3+

[0097] La 3 Ga 0.91 Ge 5 o 16 :0.09Cr 3+

[0098] La 3 Ga 0.89 Ge 5 o 16 :0.11Cr 3+

[0099] La 3 Ga 0.87 Ge 5 o 16 :0.13Cr 3+

[0100] The preparation method of this group of fluorescent materials is: according to the stoichiometric ratio in the molecular formula of the fluorescent materials, accurately weigh the raw material La 2 o 3 , Ga 2 o 3 、GeO 2 and Cr 2 o 3 ;Put the weighed raw materials into an agate mortar and grind to mix evenly, then transfer the resulting mixture to an alumina crucibl...

Embodiment 2

[0105] This embodiment provides a fluorescent material with a molecular formula of La 2.97 Ga 0.99 Ge 5 o 16 :0.03Gd 3+ ,0.01Cr 3+ , the preparation method of the fluorescent material is as follows:

[0106] Accurately weigh the raw material La according to the stoichiometric ratio in the molecular formula of the fluorescent material 2 o 3 , Ga 2 o 3 、GeO 2 、Gd 2 o 3 and Cr 2 o 3 , put the weighed raw material into an agate mortar and grind it to mix evenly, then transfer the mixture to an alumina crucible, and place it in a tube furnace for sintering in an air atmosphere, controlling the sintering temperature to 1300°C The sintering time is about 6 hours, and after being cooled in the furnace, it is ground into powder to obtain fluorescent materials.

[0107] Such as Figure 5 As shown, the XRD diffraction pattern of the fluorescent material is compared with the standard X-ray diffraction pattern, and all the diffraction peaks of the fluorescent material are co...

Embodiment 3

[0111] This embodiment provides a fluorescent material whose molecular formula is La 2.97 Ga 0.99 Ge 5 o 16 :0.03Yb 3+ ,0.01Cr 3+ , the preparation method of the fluorescent material is as follows:

[0112] Accurately weigh the raw material La according to the stoichiometric ratio in the molecular formula of the fluorescent material 2 o 3 , Ga 2 o 3 、GeO 2 , Yb 2 o 3 and Cr 2 o 3 , put the weighed raw material into an agate mortar and grind it to mix evenly, then transfer the mixture to an alumina crucible, and place it in a tube furnace for sintering in an air atmosphere, controlling the sintering temperature to 1300°C The sintering time is about 6 hours, and after being cooled in the furnace, it is ground into powder to obtain fluorescent materials.

[0113] Such as Figure 7 As shown, the XRD diffraction pattern of the fluorescent material is compared with the standard X-ray diffraction pattern, and all the diffraction peaks of the fluorescent material are co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a phosphor, a method for preparing the phosphor, an optoelectronic component, and a method for producing the optoelectronic component. The phosphor has the following general formula: LaGaGeO: 3xA, yCr, 5zB, where x, y, and z do not equal to 0 simultaneously; A represents at least one of Gd and Yb; B represents at least one of Sn, Nb, and Ta. For the phosphor, its emission spectrum is within a red visible light region and a near-infrared region when excited by blue visible light, purple visible light or ultraviolet light; and it has a wide reflection spectrum and a high radiant flux. Therefore, it can be used in optoelectronic components such as LEDs to meet requirements of current medical testing, food composition analysis, security cameras, iris/facial recognition, virtual reality, gaming notebook and light detection and ranging applications.

Description

technical field [0001] The present invention relates to a fluorescent material and its preparation method, an optoelectronic device and a method for manufacturing the optoelectronic device, in particular to a fluorescent material with high radiation flux and wide emission wavelength in the red visible light-near infrared region and its preparation process, An optoelectronic device provided with the fluorescent material and a manufacturing process of the optoelectronic device. Background technique [0002] Visible light is the part of the electromagnetic spectrum that the human eye can perceive, and infrared light is electromagnetic waves (light) with longer wavelengths than visible light. Studies have shown that infrared light is able to "penetrate" into human skin, being absorbed by the epidermis, dermis and subcutaneous tissue. At the same time, the spectrum that some human organs can absorb is in the visible light range of the electromagnetic spectrum, while the reflecte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K11/80H01L33/50
CPCC09K11/7707C09K11/7708C09K11/7775C09K11/7776H01L33/486H01L33/501H01L33/502C09K11/62C09K11/66C09K11/77C09K11/7766H01L33/005H01L2933/0041
Inventor 韦拉马尼·拉金德伦方牧怀刘如熹张合吕侊懋林晏申康桀侑盖伯瑞尔尼科洛·德·古斯曼胡淑芬
Owner EVERLIGHT ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap