A kind of biomass nanofiber membrane, its preparation method and application

A nanofiber membrane, nanofiber technology, applied in electrochemical generators, structural parts, electrical components, etc., can solve the problems of loose connection of nanofibers and reduced mechanical properties of diaphragms

Active Publication Date: 2020-10-27
UNIV OF SCI & TECH OF CHINA
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these improved methods lead to loose connections between nanofibers with the formation of pores in the separator, thereby reducing the mechanical properties of the separator.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of biomass nanofiber membrane, its preparation method and application
  • A kind of biomass nanofiber membrane, its preparation method and application
  • A kind of biomass nanofiber membrane, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0051] The present invention also provides a kind of preparation method of biomass nanofiber membrane, comprises the following steps:

[0052] S1, providing biomass nanofiber slurry;

[0053] S2. Reacting the biomass nanofiber slurry with a modifier, the modifier being one or more of acrylonitrile and isoacrylonitrile, to obtain biomass nanofibers modified with cyano groups;

[0054] S3. Papermaking the biomass nanofibers modified with cyano groups to obtain a biomass nanofiber separator.

[0055] The biomass nanofiber membrane prepared by the method of the invention has good mechanical properties, and excellent electrochemical properties such as ion conductivity.

[0056] In the embodiment of the present invention, a biomass nanofiber slurry is firstly prepared. Specifically, the biomass nanofiber and dispersion liquid can be mixed and beaten to obtain a biomass nanofiber slurry. The biomass nanofibers can be selected from one or more of cellulose nanofibers and chitin nano...

Embodiment 1

[0067] 1) Disperse 3 g of dried chitin flakes in 1 L of deionized water to obtain a suspension; then add acetic acid solution to adjust the pH value of the resulting suspension to 3, and stir at room temperature for 12 hours. The suspension of 0.3wt.% chitin flakes was ground with a beater at a speed of 20000r / min for 1 hour to obtain chitin nanofiber slurry.

[0068]2) Pour 1L of the resulting chitin nanofiber slurry into a 3L beaker, add 12g of sodium hydroxide, stir evenly, add 2L of acetone, and finally add about 180mL of acrylonitrile to make the concentration of acrylonitrile in the entire mixed solution 1mol / L. (The solvent is acetone, the concentration is 1M), and stirred at room temperature for 5 hours. Then filter and wash twice with acetone and deionized water, respectively, to obtain 3 g of cyano-modified chitin nanofibers (referred to as CCN-1M).

[0069] figure 1 Infrared test graphs of chitin nanofibers modified with different concentrations of cyano groups, ...

Embodiment 2～3

[0076] Prepare according to step 1) and step 2) in Example 1, the difference is that the concentrations of acrylonitrile added in step 2) are 3M and 5M respectively, and cyano-modified chitin nanofibers CCN-3M and CCN are respectively obtained. -5M (cyano substitution degrees are 0.235, 0.234, respectively). Infrared spectrum see figure 1 , after the comparison of the infrared spectra before and after modification, the infrared absorption peak of the cyano group can be clearly seen, which proves that the cyano group is indeed grafted onto the fiber.

[0077] Correspondingly, according to step 3) in Example 1, cyano-modified chitin nanofiber membranes CCN-3M and CCN-5M were respectively prepared.

[0078] Carry out performance test according to the test method of embodiment 1, tensile performance test result sees image 3 , the tensile strength of the separators modified with different concentrations of acrylonitrile were all greater than 120MPa. For ionic conductivity test ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a biomass nanofiber membrane, its preparation method and application. The biomass nanofiber membrane includes a biomass nanofiber film layer with a dense structure, which is made of biomass nanofibers chemically modified with cyano groups. become. In the present invention, due to the modification of the cyano group, the surface of the biomass nanofiber membrane can combine with the liquid electrolyte to form a gel state, through which lithium ions can be transported, so that the transmission of lithium ions does not depend on the strength of the membrane. aperture. The biomass nanofiber separator provided by the invention has good compactness, high ion conductivity, good electrolyte wettability and high ion transfer number. The present invention avoids the complicated steps that the biomass nanofiber separator needs to achieve high porosity by forming pores to improve the lithium ion conductivity of the separator. The biomass nanofiber separator provided by the application has good mechanical properties and realizes a dense bio The material nanofiber separator also has a breakthrough in excellent electrochemical performance.

Description

technical field [0001] The invention relates to the technical field of lithium batteries, in particular to a biomass nanofiber separator, its preparation method and application. Background technique [0002] Lithium batteries include lithium metal batteries and lithium ion batteries. At present, lithium ion batteries (LIB) are power / energy storage batteries with relatively excellent comprehensive performance. With the increasing demand for high-performance portable electronic products and electric vehicles, the requirements for energy density, cycle life and safety of lithium-ion batteries will increase significantly. Lithium-ion batteries are mainly composed of positive electrodes, separators, electrolytes and negative electrodes; during charging and discharging, Li + Intercalation and deintercalation back and forth between two electrodes. Among them, as a key component of lithium-ion batteries, the separator plays the role of isolating the positive and negative electrode...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/16H01M2/14H01M10/0525H01M50/403H01M50/426H01M50/446H01M50/449H01M50/489
CPCH01M10/0525H01M50/4295H01M50/44H01M50/403H01M50/449Y02E60/10
Inventor 姚宏斌沈豹张天文
Owner UNIV OF SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap