A kind of cement quick-setting agent and its preparation method and application, a kind of cement stone

A technology of quick-setting agent and cement stone, applied to cement quick-setting agent and its preparation, cement stone. It can solve the problems of difficult high-temperature extraction and low strength of heavy oil

Active Publication Date: 2021-07-06
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thermal recovery wells have the characteristics of low-temperature cementing (22-45°C) and high-temperature mining (higher than 270°C). High-temperature mining must use high-temperature-resistant cement when cementing wells, and accelerators need to be added to the cement slurry for low-temperature well cementing. , but the early strength of the cement in the prior art is low after thickening, which brings certain difficulties to the high-temperature exploitation of heavy oil. research focus

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cement quick-setting agent and its preparation method and application, a kind of cement stone
  • A kind of cement quick-setting agent and its preparation method and application, a kind of cement stone
  • A kind of cement quick-setting agent and its preparation method and application, a kind of cement stone

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The present invention also provides the preparation method of the above-mentioned cement quick-setting agent, comprising the following steps: mixing polyaluminum chloride, calcium chloride, sodium oxalate, calcium aluminate, calcium formate, sodium sulfate, dispersant and nano-silicon in sequence , to obtain cement quick-setting agent.

[0033] In the present invention, the mixing time is preferably 0.5-2 hours.

[0034] The present invention also provides the application of the above-mentioned cement quick-setting agent in cement stone.

[0035] The present invention also provides a cement stone, which comprises the above-mentioned cement quick-setting agent, water and cement. In the present invention, the added amount of the cement quick-setting agent is preferably 0.5-2% of the cement mass.

[0036] In the present invention, there is no special limitation on the source of the cement, and commercially available products well known to those skilled in the art can be ...

Embodiment 1

[0039] A cement quick-setting agent, comprising the following components in mass percent: 2% polyaluminium chloride; 25% calcium chloride; 20% sodium oxalate; 5% calcium aluminate; 10% calcium formate; 15% sodium sulfate; Agent 5%; nano-silicon 15%;

[0040] The above-mentioned cement quick-setting agent, 800G grade cement and water are mixed, and the cement quick-setting agent is 2% of the mass of the 800G grade cement to obtain cement stone.

[0041] figure 1 For the cement stone that embodiment 1 makes under certain temperature and pressure, the curve graph of grout consistency changing with time, from figure 1 It can be seen that the cement slurry can thicken in a short time (2h).

Embodiment 2

[0043] A cement quick-setting agent, comprising the following components in mass percent: 8% polyaluminum chloride; 23% calcium chloride; 18% sodium oxalate; 8% calcium aluminate; 8% calcium formate; 13% sodium sulfate; Agent 9%; nano-silicon 13%. ;

[0044] Mix the above-mentioned cement quick-setting agent, 800G grade cement and water, and arrange them according to different proportions to obtain cement stone.

[0045] Table 1 Different content of cement quick-setting agent, at different temperatures for 1.90g / cm 3 Experimental data on the influence of density cement slurry thickening time (min)

[0046]

[0047]

[0048]From the experimental data in Table 1, it can be obtained that the cement slurry prepared in this example, within the range of 32-52 °C, the thickening time shortens continuously with the increase of temperature and addition amount. When the addition amount is 2%, the cement The thickening time of the slurry is 56-137 minutes.

[0049] figure 2 T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a cement quick-setting agent, a preparation method and application thereof, and a cement stone, which belong to the field of heavy oil production cementing. The cement quick-setting agent provided by the invention comprises the following components in mass percent: 5-10% of polyaluminum chloride; 20-25% of calcium chloride; 15-20% of sodium oxalate; 5-10% of calcium aluminate; formic acid Calcium 5-10%; sodium sulfate 10-15%; dispersant 5-10%; nano-silicon 10-15%. The cement quick-setting agent provided by the invention adopts specific components and contents, has low-temperature quick-setting, high early strength, and does not decline in strength under high temperature. The result of embodiment shows, the cement quick-setting agent provided by the present invention, in the scope of 32~52 ℃, when adding amount is 2%, the thickening time of cement slurry is 56~137min; The strength is 8.1MPa for 8h; 26.9MPa for 24h.

Description

technical field [0001] The invention relates to the field of well cementing in heavy oil production, in particular to a cement quick-setting agent, a preparation method and application thereof, and a cement stone. Background technique [0002] About half of the world's proven oil reserves are heavy oil, and countries such as Canada, the United States, and Venezuela have all carried out thermal recovery of heavy oil. Our country is also rich in heavy oil resources, and since the 1970s, we have been committed to the research and practice of heavy oil recovery technology. A large number of heavy oil reservoirs have been discovered in Liaohe, Shengli, Tuha, Karamay and other oilfields, and the production is close to 10-15% of the production capacity of each oilfield. The rational development of these oilfields is of great significance to the stable and increased production of the above-mentioned oilfields. [0003] Liaohe Oilfield is rich in heavy oil, and the current annual ou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B24/06C04B103/12
CPCC04B28/00C04B40/0039C04B2103/12C04B22/12C04B22/124C04B24/06C04B22/08C04B24/04C04B22/147C04B2103/408C04B22/02
Inventor 魏继军李连江孙宝玉吕海丹马志贺张璞乔张莉刘奇张阔
Owner BC P INC CHINA NAT PETROLEUM CORP