Stone adhesive and preparation method thereof

A technology for adhesives and stone materials, applied in the direction of adhesives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc., can solve the problem of inability to cover dark traces, yellow edges at the joint, and poor bond strength Large and other problems, to achieve the effect of easy operation, no yellowing, and high bonding strength

Inactive Publication Date: 2019-08-27
浙江久而久化学有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The stone glue in the prior art often has the following disadvantages: 1. The dark traces at the cracks cannot be covered when the cracks are repaired, and the aesthetics after repairing the light-colored stones is poor; 2. After the adhesive is placed for a long time, the bonding 3. The bonding strength is not large, and it is often necessary to rely on the bottom plate to increase the strength during the stone repair process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stone adhesive and preparation method thereof
  • Stone adhesive and preparation method thereof
  • Stone adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The preparation methods of each sample in Example 1 to Example 18 are as follows:

[0044] (1) Weigh α-ethyl cyanoacrylate, pyrogallic acid ester compounds (pyro gallic acid propyl ester or pyro gallic acid ethyl ester) and titanium dioxide according to the ratio of preparation;

[0045] (2) Weigh 10% from the weighed ethyl α-cyanoacrylate into a three-necked flask, then put the titanium dioxide into it, and stir to fully dissolve it in the ethyl α-cyanoacrylate;

[0046] (3) Add the remaining 90% ethyl cyanoacrylate and pyrogallic acid ester compound (pyro gallic acid propyl ester or pyro gallic acid ethyl ester), and stir at the reaction temperature of 40~60℃ for 24h , Get the required stone adhesive sample.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a stone adhesive. The stone adhesive is characterized in that alpha-ethyl cyanoacrylate is taken as a main body, and components also comprise a pyrogallic acid ester compound and titanium dioxide, wherein the mass of pyrogallic acid esters accounts for 500-800 ppm of the mass of the alpha-ethyl cyanoacrylate; the mass of the titanium dioxide accounts for 500-1000 ppm of themass of the alpha-ethyl cyanoacrylate. Compared with the prior art, the stone adhesive has the advantages that 1, the stone adhesive can permeate into marble gaps due to small viscosity and good permeability; 2, the dried stone adhesive is large in bonding strength and good in stability; 3, the stone adhesive does not yellow either after being placed for a long time; 4, a preparation technology is simple and easy to operate.

Description

Technical field [0001] The invention relates to the technical field of α-ethyl cyanoacrylate adhesives, in particular to a stone adhesive and a preparation method thereof. Background technique [0002] In 1947, A·E·Ardis first synthesized α-cyanoacrylate and obtained a patent. In the 1950s, Eastman Kodak researchers accidentally discovered the adhesive properties of α-cyanoacrylate and officially launched the world's first α-adhesive. Subsequently, Japan, West Germany and other countries have also been put into production. my country began to research and produce in the 1960s. The α-adhesive has developed rapidly once it came out. It has fast curing speed, convenient use, strong adhesion, and wide range of bonding materials. For bonding steel, non-ferrous metals, rubber, leather, plastics, ceramics, glass, wood, stone, etc., it is widely used in electrical, instrumentation, machinery, electronics, optical instruments, medical, light industry and civil industries. [0003] Stone gl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/04C09J11/06C09J11/04
CPCC09J4/00C09J11/04C09J11/06
Inventor 宋宏骞汪荣利杨晔
Owner 浙江久而久化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap