Aluminum silicon alloy partition plate, phosphating treatment method and compressor

A phosphating, aluminum-silicon alloy technology, applied in the field of compressors, can solve problems such as poor wear resistance of partitions, and achieve the effects of weight reduction, cost reduction, and good phosphating effect

Active Publication Date: 2019-08-27
ZHUHAI LANDA COMPRESSOR +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the defect of poor wear resistance of existing partitions, the present invention proposes an aluminum-silicon alloy partition, a phosphating treatment method and a compressor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum silicon alloy partition plate, phosphating treatment method and compressor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The invention proposes that the separator adopts an aluminum-silicon alloy material, and the surface of the separator is coated with a phosphating film after phosphating treatment. The aluminum-silicon alloy material of the separator contains 17-32% Si, 5-10% Cu, 2-5% Zn, 0.6-2% Mn, 1-2% Mg, 0.7-1.5% Fe, 0.1% RE, and the remainder All are Al. Compared with the general aluminum alloy composition, the aluminum-silicon alloy material composition of the separator eliminates the addition of heavy metal antimony. Although heavy metal elements can increase the hardness and strength of the alloy, the element is poisonous and expensive. The removal of heavy metal elements can reduce it on the one hand. Cost, on the other hand, can reduce the harm to the environment and the human body, making the material more environmentally friendly. Preferably, the content of Zn and Mg in the aluminum-silicon alloy material of the separator is increased, which effectively promotes the formatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum silicon alloy partition plate, a phosphating treatment method and a compressor. The partition plate adopts an an aluminum silicon alloy material, and the partitionplate is coated with a phosphating film after the surface of the partition plate is subjected to phosphating treatment. The wear resistance of the partition plate can be significantly improved, the requirement on the wear resistance of the partition plate under the unlimited working condition of the compressor is met, and the process cost of the partition plate is lower.

Description

Technical field [0001] The invention relates to the technical field of compressors, in particular to aluminum-silicon alloy separators, phosphating treatment methods and compressors. Background technique [0002] Compared with cast iron, conventional aluminum alloys are weaker in strength, hardness and wear resistance, and generally cannot be directly applied to the diaphragm of the compressor. The existing solution is to passivate, oxidize or phosphatize aluminum alloy separators to improve the strength and wear resistance of the separators. Although the cost of phosphating treatment is much lower than that of passivation treatment and oxidation treatment, and the phosphating film formed after phosphating treatment has better wear resistance, passivation treatment and oxidation treatment are used most in actual production, and phosphating treatment is very Rare, the main reason is that aluminum is mainly used in conventional aluminum alloys, and other alloying elements are gene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C30/06C23C22/08F04C29/00F04C29/12
CPCC22C21/02C22C30/02C22C30/06C23C22/08F04C29/00F04C29/12
Inventor 郑慧芸贾波廖熠沈慧
Owner ZHUHAI LANDA COMPRESSOR
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com