Manufacturing method of novel chemical fiber blended yarn

A technology of chemical fibers and production methods, applied in the direction of yarn, textiles and papermaking, etc., to achieve strong adsorption, good thermal insulation performance, and good warmth retention

Inactive Publication Date: 2019-09-27
沛县谦和纺织有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention proposes a method for making a novel chemical fiber blended yarn, which solves the problems of warmth retention and air permeability of clothing fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A method for making a novel chemical fiber blended yarn, comprising the following raw materials in parts by weight:

[0037] 30 parts of cotton fiber;

[0038] 15 parts of chemical fiber;

[0039] 15 parts of bamboo fiber;

[0040] Activated carbon fiber 5 parts;

[0041] In an embodiment, the chemical fiber is acrylic fiber, polyester fiber and viscose fiber;

[0042] Its preparation method is as follows:

[0043] Step 1: Remove impurities from cotton fiber, activated carbon fiber, chemical fiber and bamboo fiber; first ginn cotton fiber and chemical fiber several times; It is used to remove sand, small impurities and short fluff; finally, the activated carbon fiber and bamboo fiber are filtered through a screen to remove impurities.

[0044] Step 2: Loosen the cotton fiber, chemical fiber, activated carbon fiber and bamboo fiber, and remove the horizontal connection between fibers.

[0045] Step 3: Open the cotton fiber, chemical fiber, bamboo fiber and activate...

Embodiment 2

[0054] A method for making a novel chemical fiber blended yarn, comprising the following raw materials in parts by weight:

[0055] 40 parts of cotton fiber;

[0056] 20 parts of chemical fiber;

[0057] 20 parts of bamboo fiber;

[0058] Activated carbon fiber 5 parts;

[0059] In an embodiment, the chemical fiber is polyester, polyester fiber and viscose fiber;

[0060] Its preparation method is as follows:

[0061] Step 1: Remove impurities from cotton fiber, activated carbon fiber, chemical fiber and bamboo fiber; first ginn cotton fiber and chemical fiber several times; It is used to remove sand, small impurities and short fluff; finally, the activated carbon fiber and bamboo fiber are filtered through a screen to remove impurities.

[0062] Step 2: Loosen the cotton fiber, chemical fiber, activated carbon fiber and bamboo fiber, and remove the horizontal connection between fibers.

[0063] Step 3: Open the cotton fiber, chemical fiber, bamboo fiber and activated ca...

Embodiment 3

[0072] A method for making a novel chemical fiber blended yarn, comprising the following raw materials in parts by weight:

[0073] 30 parts of cotton fiber;

[0074] 20 parts of chemical fiber;

[0075] 16 parts of bamboo fiber;

[0076] 3 parts activated carbon fiber;

[0077] In this embodiment, the chemical fiber is polyester, polypropylene fiber and viscose fiber;

[0078] Its preparation method is as follows:

[0079] Step 1: Remove impurities from cotton fiber, activated carbon fiber, chemical fiber and bamboo fiber; first ginn cotton fiber and chemical fiber several times; It is used to remove sand, small impurities and short fluff; finally, the activated carbon fiber and bamboo fiber are filtered through a screen to remove impurities.

[0080] Step 2: Loosen the cotton fiber, chemical fiber, activated carbon fiber and bamboo fiber, and remove the horizontal connection between fibers.

[0081] Step 3: Open the cotton fiber, chemical fiber, bamboo fiber and activa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of blended yarns and particularly relates to a manufacturing method of a novel chemical fiber blended yarn. The problems of high thickness and poor heat preservation performance and gas permeability of an existing garment fabric are solved. The following scheme is proposed. The method comprises the steps that cotton fibers, activated carbon fibers, chemical fibers and raw bamboo fibers are subjected to impurity removal, released and subjected to opening, the cotton fibers, activated carbon fibers and raw bamboo fibers are conveyed to a carding machine for carding, the chemical fibers are heated, mix-fused and prepared into a spinning solution, and through spinning, composite fibers are prepared; the cotton fibers, activated carbon fibers and raw bamboo fibers are convoyed into a combing machine; the cotton fibers, activated carbon fibers, raw bamboo fibers and composite fibers after being combed are evenly mixed and drafted; the drafted fibers are twisted and coiled to prepare a finished blended yarn product, and the prepared finished product is proper in thickness and good in heat preservation performance and gas permeability.

Description

technical field [0001] The invention relates to the technical field of blended yarns, in particular to a method for making novel chemical fiber blended yarns. Background technique [0002] With the development and progress of science and technology, people's requirements for low-clothing are getting higher and higher, especially for people in cold regions, who have higher requirements for the warmth retention of clothing fabrics; in cold regions, cotton-padded clothes are generally used for outdoor activities Ways to keep warm, or wear down jackets, but with the improvement of people's aesthetic concept and the requirements for portability during the journey, there is an increasing demand for light and thin fabric products. Although down jackets can be made very light, they are relatively bulky and bloated when worn, so they are not suitable for outdoor sports such as mountain climbing. Although fur clothes have good thermal performance, fur clothes are relatively heavy and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04D02G3/44
CPCD02G3/04D02G3/44D02G3/443D10B2101/12D10B2201/02D10B2201/22D10B2201/24D10B2321/022D10B2321/10D10B2331/04D10B2501/00D10B2501/04
Inventor 李桂花
Owner 沛县谦和纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com