Plasma nonmetal ceramic alloy technology

A technology of ceramic alloy and plasma, which is applied in the direction of metal material coating process, coating, solid diffusion coating, etc., can solve the problems of large damage to operators, environmental pollution by ammonia gas, and shape deformation, etc., to improve service life, Reduce the temperature of the production environment and improve the effect of wear resistance

Pending Publication Date: 2019-10-25
南京朗仕億等离子体制造科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The plasma non-metallic ceramic alloy technology proposed by the present invention completely solves the problem that the shape deformation of small, light and thin parts caused by excessive production temperature, the working gas ammonia polluted the environment by production and use, and the problems of great harm to operators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A plasma non-metallic ceramic alloy technology for surface modification of small, light and thin parts, including the following steps:

[0048] (1) Clamping

[0049] 1.1. Place the processed parts in a vacuum container to clamp and fix them;

[0050] 1.2. Check whether the furnace door sealing ring is normal, wipe the furnace door sealing ring and the observation window with acetone, close and lock the furnace door;

[0051] (2) Operation process

[0052] Stage 1. Work preparation: vacuuming, furnace heating, high-frequency preheating

[0053] 2.1. Turn on the power supply of the control cabinet and turn on the cooling water pump;

[0054] 2.2. Confirm that the air valve is opened clockwise and closed counterclockwise, turn on the rotary vane pump, and turn on the Roots pump if the vacuum degree is within 1000Pa;

[0055] 2.3. When the vacuum drops to 100Pa-150Pa, turn on the heating power supply, and the current is 5±1A;

[0056] 2.4. When the vacuum reaches 50-10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a plasma nonmetal ceramic alloy technology which is used for performing surface modification on small, light and thin parts. The plasma nonmetal ceramic alloy technology is characterized by comprising the following steps: controlling the temperature of processing parts in a vacuum container to be lower than 200 DEG C, and using nitrogen gas, silane and borane to perform ionpermeation on processing surfaces of the parts. The plasma nonmetal ceramic alloy technology reduces a production environment temperature, can perform surface modification on small, light and thin parts, does not cause outlines of the parts to deform, improves surface hardness of the small, light and thin parts, improves wear resistance, reduces abrasion between friction pairs, and prolongs the service lives of the parts.

Description

technical field [0001] The invention relates to the technical field of heat treatment and infiltration on the surface of small, light and thin parts, in particular to a plasma non-metallic ceramic alloy technology. Background technique [0002] The traditional surface heat treatment infiltration process for small, light and thin parts has the following defects: (1) High nitriding temperature is easy to cause shape deformation for small, light and thin parts; [0003] (2) The ammonia gas used in the nitriding process pollutes the environment and causes great harm to operators. Contents of the invention [0004] The plasma non-metallic ceramic alloy technology proposed by the invention completely solves the problems that the shape deformation of small, light and thin parts caused by excessive production temperature, the production and use of working gas ammonia pollute the environment, and cause great harm to operators. [0005] The purpose of the present invention is achie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C8/36
CPCC23C8/36
Inventor 朱刚聂毅东吴立南
Owner 南京朗仕億等离子体制造科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com