Method for preparing polyisocyanate by photochemical reaction and method for preparing waterborne polyurethane resin

A polyisocyanate, reaction technology, applied in the field of water-based polyurethane resin, can solve the problems of high chlorine content of polyisocyanate, yellow color and other problems, achieve the effect of improving yellowing resistance, reducing violent fluctuations, and improving yellowing resistance

Active Publication Date: 2021-09-07
WANHUA CHEM GRP CO LTD +1
View PDF25 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above prior art prepares polyisocyanate, although many methods for reducing the chromaticity and chlorine content of isocyanate are mentioned, but it is not clear which type of impurity causes the chlorine content of polyisocyanate to be high or the color is yellow, which affects the reality. There is some uncertainty in the application process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing polyisocyanate by photochemical reaction and method for preparing waterborne polyurethane resin
  • Method for preparing polyisocyanate by photochemical reaction and method for preparing waterborne polyurethane resin

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0098] a) using the heater disclosed in Example 1 of Chinese patent application CN105214568A, a diamine H 12 MDA is gasified and heated to 355 deg.] C, under nitrogen protection, and gaseous phosgene is heated to 355 deg.] C via a respective feed line continuously added phosgenation reactor; absolute pressure of the reaction is 0.05MPa, the reaction temperature is 360 deg.] C; wherein, H 12 MDA feeding amount is 800Kg / h, the feed amount of the gaseous phosgene was 3000Kg / h; using o-dichlorobenzene solution through a gas injection means for absorbing the reaction mixture obtained after the flash gas (contact time of approximately 10s) was cooled to 100 ℃, to give product containing H 12 MDI, crude product phosgene and a solution of o-dichlorobenzene; o-dichlorobenzene solution absorption -35 ℃ the absorber off-gas entering the exhaust gas after the reaction to give the o-dichlorobenzene solution of phosgene.

[0099] b) step a) obtained crude product is treated to remove phosge...

preparation example 2

[0107] Step a) the phosgenation reaction is a liquid phase phosgenation, with reference to China Patent Document CN103319372B reactor disclosed in the following steps are performed:

[0108] 1) The cold reaction: the H 12 MDA o-dichlorobenzene as a solvent configured content of 15% by mass solution, and preheated to 40 ℃, liquid phase and the liquid phosgene -5 ℃ simultaneously introduced into the reaction vessel containing a solution of o-dichlorobenzene phosgenation; wherein, H 12 MDA in feed rate is 400Kg / h, cool the reaction of phosgene feed rate of 1500kg / h, cool the reaction temperature is controlled at 60 ℃, residence time of 5min;

[0109] 2) thermal reaction: temperature was controlled at 155 deg.] C, and a residence time of 2h, the reaction was carried out in o-dichlorobenzene and the presence of excess phosgene to give the product containing H 12 MDI, phosgene and o-dichlorobenzene solution of the reaction liquid (crude product);

[0110] O-dichlorobenzene solution ...

preparation example 3

[0118] Step a) using the phosgenation of a salt phosgenation reactor tank embodiments with reference to Chinese Patent Document CN105218422B Example 1 disclosed in the following steps are performed:

[0119] 1) In the salt-forming reaction kettle was added after previously 1000Kg o-dichlorobenzene as the reaction solvent, and stirring the circulating pump, the compressed gas is hydrogen chloride at a rate of 50mol / min into the reactor via a pre-mixer, stirring 15min, the H 12 MDA and o-dichlorobenzene by heating a mixture of starting material to a preheater 30 ℃, after sufficient contact to 335Kg / h and the flow rate of hydrogen chloride gas into a salt; using external circulating cooling water for cooling, removing part of the reaction heat, cycling liquid flow 5m 3 Left / h, the reaction solution temperature was maintained at 30-45 ℃, the feed 3h, stopping H 12 O-dichlorobenzene with MDA feed mixture, continuing to pass HCl gas 30min.

[0120] 2) step 1) obtained H 12 MDA hyd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of water-based polyurethane resins, and in particular relates to a method for preparing polyisocyanates by photochemical reaction and a method for preparing water-based polyurethane resins. The method for preparing water-based polyurethane resins comprises the following steps: The raw materials of chain extender and hydrophilic agent are polymerized to obtain water-based polyurethane resin; wherein, the content of benzophenone impurities in the polyisocyanate is ≤0.045wt%. By controlling the content of benzophenone impurities in the polyisocyanate preparation process, the invention can effectively improve the anti-yellowing performance of the product, and also reduce the harm of unqualified downstream products caused by the presence of such impurities in the product.

Description

Technical field [0001] The present invention belongs to the technical field of aqueous polyurethane resin, in particular, to a method of preparing a photochemical reaction of a polyisocyanate and a method for preparation of an aqueous polyurethane resin. Background technique [0002] Polyurethane is one of the outstanding integrated performance of synthetic resin. Due to its monomeric synthetic varieties, mild reaction conditions, specific, controllable, and a large adjustment margin formulation characteristics and microstructure of polymer materials, can be widely used in coatings, adhesives, foams, elastomers and synthetic fibers , has become clothing, food, shelter, one of the essential materials firms; and, which itself has become a multi-species, multi-series family of materials, polyurethane formed a complete industrial system, which is the other resins not available. [0003] With the strengthening of environmental awareness and environmental regulations, environmentally f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C263/10C07C265/14C08G18/75
CPCC07C263/10C08G18/758C07C2601/14C07C265/14
Inventor 华卫琦俞勇尚永华李建峰郭耀允王腾飞李文滨孙烨王峤刘德刚黎源
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap