Anti-seismic epoxy dipping glue and preparation method thereof

A technology of impregnating glue and epoxy, which is applied in the direction of epoxy resin glue, modified epoxy resin adhesive, adhesive, etc., and can solve the problems of air bubble construction performance, impact resistance peeling ability and fatigue resistance inspection, etc. , to achieve the effect of good construction performance, low cost and good applicability

Active Publication Date: 2015-01-21
苏州市姑苏新型建材有限公司
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the Chinese invention patent CN101654606A discloses an epoxy adhesive, which is mainly used for impregnation and bonding of carbon fiber composite materials in the reinforcement of concrete structures, which solves the problem of bubbles in the production process of the glue and the construction performance during use, but has not been passed. Impact peeling ability and fatigue resistance test

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] An anti-shock epoxy impregnating glue, which includes component A and component B, the mixing ratio of component A and component B by weight is 3:1, and the ingredients contained in each of the two components are as follows:

[0053] .

[0054] The preparation method of above-mentioned anti-seismic epoxy impregnation glue is as follows:

[0055] (1) Preparation of component A: Weigh the raw materials according to the above ratio, first mix 75.0 parts of E-51 liquid epoxy resin, 5.0 parts of ARZ-2000 type epoxy acrylic resin, 15.0 parts of hydrogenated bisphenol A diglycidol Add ether, 5.0 parts of PS-121 polysulfide rubber, 5.0 parts of 692 type benzyl glycidyl ether, 0.1 part of TH-1135 type anti-aging agent, 0.5 parts of tert-butyl peroxybenzoate and 1.0 parts of A200 gas phase white carbon black into the hydraulic pressure In the dispersing machine, stir at medium speed (600rpm) for 1h, then add 1.0 parts of BYK-R605, stir at high speed (1200rpm) for 0.25h, and fi...

Embodiment 2

[0060] An anti-shock epoxy impregnating glue, which includes component A and component B, the mixing ratio of component A and component B by weight is 3:1, and the ingredients contained in each of the two components are as follows:

[0061] .

[0062] The preparation method of above-mentioned anti-seismic epoxy impregnation glue is as follows:

[0063] (1) Preparation of component A: Weigh the raw materials according to the above ratio, first mix 75.0 parts of E-51 liquid epoxy resin, 20.0 parts of ARZ-2000 type epoxy acrylic resin, 20.0 parts of hydrogenated bisphenol A diglycidol Add ether, 3.0 parts of 692 type benzyl glycidyl ether, 5.0 parts of PS-121 polysulfide rubber, 0.5 parts of TH-1135, 0.1 parts of tert-butyl peroxybenzoate and 6.0 parts of A200 gas phase silica into the hydraulic disperser Stir at medium speed (600rpm) for 1h, then add 0.1 part of BYK-R606, stir at high speed (1200rpm) for 0.25h, and finally grind three times with a three-roller machine, then p...

Embodiment 3

[0068] An anti-shock epoxy impregnating glue, which includes component A and component B, the mixing ratio of component A and component B by weight is 3:1, and the ingredients contained in each of the two components are as follows:

[0069] .

[0070] The preparation method of above-mentioned anti-seismic epoxy impregnation glue is as follows:

[0071] (1) Preparation of component A: Weigh the raw materials according to the above ratio, first mix 50.0 parts of E-51 liquid epoxy resin, 20.0 parts of ARZ-2000 type epoxy acrylic resin, 20.0 parts of hydrogenated bisphenol A diglycidol Ether, 10.0 parts PS-121 polysulfide rubber, 5.0 parts polyether resin, 5.0 parts 692 type benzyl glycidyl ether, 0.4 parts TH-1135, 0.8 parts tert-butyl peroxybenzoate and 5.0 parts A200 fumed silica Add it into a hydraulic disperser, stir at medium speed (600rpm) for 1 hour, then add 0.5 parts of BYK-R605, stir at high speed (1200rpm) for 0.25 hours, and finally grind it three times with a thre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses anti-seismic epoxy dipping glue and a preparation method thereof. To be specific, the dipping glue comprises a component A and a component B in a weight part ratio of 3 to 1; the component A comprises 50.0-75.0 parts of bisphenol A epoxy resin, 5.0-20.0 parts of epoxy acrylate, 10.0-20.0 parts of hydrogenated bisphenol A epoxy resin, 2.0-8.0 parts of diluents, 5.0-15.0 parts of toughening agents, 1.0-6.0 parts of a thixotropic agent, 0.1-0.5 parts of an anti-aging agent, 0.5-1.0 part of peroxides, and 0.1-1.0 part of rheological additives; the component B comprises 20.0-40.0 parts of an aliphatic amine curing agent, 40.0-60.0 parts of an alicyclic amine curing agent, 0.5-2.0 parts of accelerants, 1.0-4.0 parts of coupling agents and 1.0-15.0 parts of a thixotropic agent. The dipping glue is prepared by respectively preparing the component A and the component B, and mixing the components A and B, and is mainly used for gluing carbon fiber composite materials used for reinforcing buildings in areas with the seismic fortification intensity of not less than level 7; the intensity index of the dipping glue is in line with performance indexes in Engineering Structure Strengthening Material Security Identification Technical Specification of GB50728-2011.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to an anti-seismic epoxy impregnated glue and a preparation method thereof. Background technique [0002] With the development of my country's economic construction and the continuous development of the construction industry, people pay more and more attention to the safety of building structures. In recent years, there have been many catastrophic earthquakes at home and abroad. Many buildings and bridges collapsed or were severely damaged in the earthquakes, causing a large number of casualties and bringing huge economic losses to the country. Therefore, the requirements for the anti-seismic grade of buildings and the reinforcement materials used for anti-seismic are also getting higher and higher. [0003] At present, the reinforcement methods of reinforced concrete seismic structures commonly used in engineering mainly include the reinforcement method of e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J163/02C09J163/10C09J11/08C09J11/06C09J11/04
Inventor 陈晓龙朱华张晓华
Owner 苏州市姑苏新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com