High-performance repairing adhesive tape for photovoltaic module back panel and preparation method

A technology for repairing tapes and photovoltaic modules, applied in photovoltaic modules, photovoltaic power generation, adhesive products, etc., can solve problems such as backplane yellowing, high cost, and functional failure, and achieve small peeling force attenuation and high bonding strength , Improve the effect of weather resistance

Inactive Publication Date: 2018-03-27
CYBRID TECHNOLOGIES INC
View PDF10 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after a period of use outdoors, the backsheet of solar modules will gradually age and crack, such as yellowing, pinholes, pulverization, micro-cracking, and cracking, which cannot meet the safety requirements of the module during operation; at the same time , during the transportation and installation of solar modules, some of the backplanes of the modules will be damaged and scratched, which will also lead to safety and functional failures during the operation of the modules
[0003] At present, no suitable repair method has been found for the damaged parts of the solar backplane. Only the damaged components can be replaced completely. This method can only replace a small number of components. If a large number of components are replaced, the cost will be extremely high, and it is difficult to recycle old components. , It is also easy to cause environmental pollution; in view of this background, it is of great significance to develop a repair tape that can be applied on-site, environmentally friendly, free of waste, and low in cost, so that damaged components can operate normally within the warranty period

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance repairing adhesive tape for photovoltaic module back panel and preparation method
  • High-performance repairing adhesive tape for photovoltaic module back panel and preparation method
  • High-performance repairing adhesive tape for photovoltaic module back panel and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Such as figure 1 As shown, a high-performance repair tape for a photovoltaic module backplane in this embodiment includes a substrate layer 1, a functional adhesive layer 2, and a release material layer 3 arranged in sequence from top to bottom, and the substrate layer 1 is 300 μm The composite polyester film consists of a core layer in the middle and a weather-resistant polymer film pasted on one side of the core layer. The core layer is a polyester film, and the weather-resistant polymer film is a fluorine film. The fluorine film is a 50 μm polyester film. Vinylidene fluoride (PVDF). The functional adhesive layer 2 includes acrylic pressure-sensitive adhesive, the added curing agent is epoxy curing agent, the tackifying resin is rosin, the antioxidant is aromatic amine antioxidant, and the ultraviolet absorber is salicylate ultraviolet absorber.

[0036] According to the preparation method of any one of the above-mentioned high-performance repair tapes for photovolta...

Embodiment 2

[0041] Such as figure 1 As shown, a high-performance repair tape for a photovoltaic module backplane in this embodiment includes a substrate layer 1, a functional adhesive layer 2, and a release material layer 3 arranged in sequence from top to bottom, and the substrate layer 1 is 300 μm The composite polyester film consists of a core layer in the middle and a weather-resistant polymer film pasted on both sides of the core layer. The core layer is a polyester film, and the weather-resistant polymer film is a fluorine film. The fluorine film is a 50 μm polyester film Vinylidene fluoride (PVDF). The functional adhesive layer 2 includes acrylic pressure-sensitive adhesive, the added curing agent is epoxy curing agent, the tackifying resin is rosin, the antioxidant is aromatic amine antioxidant, and the ultraviolet absorber is salicylate ultraviolet absorber.

[0042] According to the preparation method of any one of the above-mentioned high-performance repair tapes for photovolt...

Embodiment 3

[0047] Such as figure 1 As shown, a high-performance repair tape for a photovoltaic module backplane in this embodiment includes a substrate layer 1, a functional adhesive layer 2, and a release material layer 3 arranged in sequence from top to bottom, and the substrate layer 1 is 250 μm Composite polyester film, including a core layer in the middle, a weather-resistant polymer film pasted on one side of the core layer, and a polymer weather-resistant coating directly coated on the other side of the core layer. The core layer is a polyamide film, which is weather-resistant The permanent polymer film is a 50μm UV-resistant polyolefin film, and the polymer weather-resistant coating is formed by curing fluorocarbon resin to the surface of the core layer through a curing agent. The functional adhesive layer 2 is composed of acrylic pressure-sensitive adhesive and thermosetting structural adhesive. The added curing agent is epoxy curing agent and isocyanate curing agent. The tackif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
solid containing ratioaaaaaaaaaa
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance repairing adhesive tape for a photovoltaic module back panel. The high-performance repairing adhesive tape comprises a base material layer, a functional adhesive layer and a release material layer which are arranged in sequence from top to bottom, wherein the base material layer is composed of a polyester thin film type material; the functional adhesive layer is composed of a high-weather-resistance adhesive. According to the high-performance repairing adhesive tape for the photovoltaic module back panel and the preparation method, disclosed by the invention, the weather-resistance base material layer is selected so that the effects of water resistance, insulation, ultraviolet radiation resistance and the like can be realized and the effect of anindependent back panel is realized; the high-weather-resistance adhesive is selected for the functional adhesive layer, so that the weather resistance, high temperature resistance and yellowing resistance of the adhesive tape can be improved; the adhesive tape has great bonding strength and is not easy to fall off; meanwhile, the adhesive tape is convenient to stick and convenient to construct.

Description

technical field [0001] The invention relates to the technical field of adhesive tapes, in particular to a high-performance repair adhesive tape for a backplane of a photovoltaic module and a preparation method thereof. Background technique [0002] The solar backsheet is located on the back of the solar panel, which protects and supports the solar cells in the module, and has reliable insulation and water resistance. However, after a period of use outdoors, the backsheet of solar modules will gradually age and crack, such as yellowing, pinholes, pulverization, micro-cracking, and cracking, which cannot meet the safety requirements of the module during operation; at the same time , During the transportation and installation of solar modules, some of the backplanes of the modules will be damaged and scratched, which will also lead to safety and functional failures during the operation of the modules. [0003] At present, no suitable repair method has been found for the damage...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/25C09J7/24C09J7/29C09J7/38C09J7/50C09J107/00C09J123/22C09J133/00C09J175/04C09J183/04C08J7/043
CPCC09J7/255C09J11/04C09J11/06C09J11/08C09J107/00C09J123/22C09J175/04C09J183/04C08L2205/03C09J2477/006C09J2467/006C09J2423/006C09J2427/006C09J7/29C09J7/30C09J133/04C09J7/50C09J2475/00C09J2483/00C08J7/0427C08J7/043C08F220/1808C08F220/1804C08L45/00C08L93/04C08L23/22C08L33/04C08K3/34C08K2003/2241C08K2003/265C08K2003/3045C08L2201/08C09D127/18C09D183/08C09J2203/322C09J2423/046C09J2423/106C09J2433/00C09D175/04C08G18/7621C08G2170/40C08G18/6254H02S40/00C09D133/066C08L2203/204C08G77/24Y02E10/50C09J2301/122C09J2301/312C09J2301/302C09D4/00C09J4/00C09D127/16B32B2255/10B32B2405/00B32B2264/104B32B2457/12B32B27/34B32B2255/26B32B27/36B32B2307/712B32B2307/71B32B2264/102B32B27/304B32B27/322B32B27/08B32B27/32B32B27/20B32B27/38C08L33/08C08K3/36C08F220/14C08F220/06C08F220/20C08K3/346C08L27/18C08K3/22C08L83/08C09J7/243C09D7/61C09D7/63C09J7/38C08J2323/06C08J2323/12C09J133/08C08J2367/00C08J2377/00H01L31/186C09J2301/16C09J2301/408
Inventor 周琪权李晓旭陈洪野芋野昌三吴小平
Owner CYBRID TECHNOLOGIES INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com