A high-strength expansion sleeve and its manufacturing method

A technology of expansion casing and manufacturing method, which is applied in the direction of casing, manufacturing tools, drill pipes, etc., can solve the problems of low strength and poor plasticity, and achieve improved pressure resistance, high strength and elongation, and easy mass production The effect of implementation

Active Publication Date: 2021-08-13
BAOSHAN IRON & STEEL CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] One of the objectives of the present invention is to provide a high-strength expansion sleeve, which has high strength and elongation, so as to solve the problems of low strength and poor plasticity of the expansion sleeve in the prior art, and improve The pressure resistance of the expansion casing used in the downhole meets the demand for high-strength expansion casing in the field of oilfield production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength expansion sleeve and its manufacturing method
  • A high-strength expansion sleeve and its manufacturing method
  • A high-strength expansion sleeve and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5 and comparative example 1-4

[0042] Table 1-1 and Table 1-2 list the mass percent of each chemical element in the high-strength expansion sleeves of Examples 1-5 and Comparative Examples 1-4.

[0043] Table 1-1. (wt%, the balance is Fe and unavoidable impurities other than P, S, N)

[0044] serial number C mn Si P S Cr Mo V Ac1 Ac1+30 Ac3 Ac3-30 Example 1 0.1 3 0.2 0.009 0.002 / / 0.05 697 727 860 830 Example 2 0.12 4 0.1 0.010 0.001 0.2 0.2 0.07 686 716 858 828 Example 3 0.14 5 0.3 0.010 0.003 0.5 0.5 0.1 687 717 874 844 Example 4 0.18 6 0.4 0.012 0.005 / / 0.15 670 700 857 827 Example 5 0.20 4 0.25 0.013 0.002 / / 0.2 687 717 851 821 Comparative example 1 0.1 1.5

0.2 0.009 0.002 / / 0.05 713 743 860 830 Comparative example 2 0.3

4 0.1 0.010 0.001 0.2 0.2 0.07 686 716 817 787 Comparative example 3 0.05

5 0.3 0.010 0.003 / 0.5 / 678 708...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength expansion sleeve, the mass percentage of chemical elements is: C: 0.1-0.2%, Si: 0.1-0.4%, Mn: 3-6%, V: 0.05-0.2%, Ca: 0.0005 ‑0.005%, Ti: 0.01‑0.04%, Al: 0.01‑0.05%, and at least one of Cr≤0.5%, Mo≤0.5%, Nb≤0.04%, and the balance is Fe and other unavoidable impurities. The invention also discloses a method for manufacturing the high-strength expansion sleeve, which includes the steps: (1) producing a tube blank through smelting and continuous casting; (2) piercing and continuous rolling the tube blank; (3) heat treatment: The steel pipe is heated to the austenitizing temperature Ac1+30°C to Ac3‑30°C, water quenched after holding for 30‑60min; then tempered in the range of 650‑720°C, holding time for 50‑80min; then heat sizing.

Description

technical field [0001] The invention relates to a casing and a manufacturing method thereof, in particular to an expansion casing and a manufacturing method thereof. Background technique [0002] The expansion casing is a special kind of petroleum-specific pipe. In addition to having good expansion performance, it must also ensure that the mechanical properties of the corresponding steel grade casing in the American Petroleum Institute (API) standard are met after expansion, so as to meet the engineering application requirements. However, the mechanical properties of the expansion sleeve in the current prior art limit its expansion rate. When the expansion rate exceeds 20%, the expansion sleeve is prone to the problem of uneven wall thickness, resulting in local wall thickness reduction of the expansion sleeve. , thereby reducing the mechanical properties of the entire tube of the expansion sleeve, so obtaining an expansion sleeve with a high elongation rate is the main tech...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C38/14C22C38/06C22C38/38C22C38/24C22C38/22C22C38/26C22C38/28C21D9/08C21D1/18E21B17/00
CPCC21D1/18C21D9/08C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C22C38/22C22C38/24C22C38/26C22C38/28C22C38/38E21B17/00
Inventor 董晓明张忠铧高展
Owner BAOSHAN IRON & STEEL CO LTD