A method for preparing diamond film on stainless steel surface with Cr/Craln as transition layer

A diamond thin film, stainless steel technology, applied in coating, metal material coating process, vacuum evaporation coating and other directions, can solve the problems of difficult to form diamond thin film, unable to reach the critical carbon concentration of diamond nucleation, thin film falling off, etc., to achieve excellent The effect of membrane-based binding

Active Publication Date: 2021-11-02
ZHEJIANG UNIV OF TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the direct deposition of diamond films on the surface of stainless steel has the following problems: (1) Carbon has a high diffusion rate in stainless steel. When the carbon in the CVD atmosphere reaches the stainless steel surface, it will quickly diffuse into the stainless steel, resulting in the inability to achieve diamond nucleation. The required critical carbon concentration makes it difficult to form diamond films
(2) The graphite catalysis of Fe and Ni elements in stainless steel will preferentially form a loose graphite layer on the surface of the sample, causing the film to fall off
(3) There is a huge difference in thermal expansion coefficient between the stainless steel and the diamond film, so that during the CVD cooling process, a huge thermal stress is formed between the diamond film and the stainless steel, causing the film to fall off
However, since the hardness of the CrN transition layer is 18GPa, which is much lower than that of diamond, the hardness of the entire film is low, which affects the performance and life of the film.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing diamond film on stainless steel surface with Cr/Craln as transition layer
  • A method for preparing diamond film on stainless steel surface with Cr/Craln as transition layer
  • A method for preparing diamond film on stainless steel surface with Cr/Craln as transition layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Grind 3Cr13 stainless steel with 600#, 800#, 1200#, 1500#, 2000# sandpaper in sequence, then ultrasonically shake the polished samples with acetone and absolute ethanol for 20 minutes, dry them quickly with a hair dryer, and put them into PVD Cr / CrAlN transition layer deposition is carried out in the equipment. The purity of the Cr target and the Al target used in the deposition process are both 99.999%, and the target base distance is 70 mm. The process parameters for depositing the Cr layer are: vacuum degree 1×10 –3 Pa, the Ar gas flow is 20 sccm, the working pressure is 0.8 Pa, the Cr target power is 100 W, the substrate temperature is 300 °C, and the deposition time is 20 min. The process parameters for preparing the CrAlN layer are: Ar gas flow rate is 20 sccm, N 2 The gas flow rate is 5 sccm, the working pressure is 1 Pa, the Al target power is 120 W, the Cr target power is 100 W, the substrate temperature is 300 °C, and the deposition time is 60 min; In an a...

Embodiment 2

[0034] Grind 3Cr13 stainless steel with 600#, 800#, 1200#, 1500#, 2000# sandpaper in sequence, then ultrasonically shake the polished samples with acetone and absolute ethanol for 20 minutes, dry them quickly with a hair dryer, and put them into PVD equipment The deposition of Cr / CrAlN transition layer is carried out in the middle. During the deposition process, the purity of both Cr and Al targets was 99.999%, and the target-base distance was 70 mm. The process parameters for depositing the Cr layer are: vacuum degree 0.8×10 –3 Pa, the Ar gas flow rate is 20 sccm, the working pressure is 0.8 Pa, the Cr target power is 100 W, and the deposition time is 40 min. The process parameters for preparing the CrAlN layer are: Ar gas flow rate is 20 sccm, N 2 The gas flow rate is 5 sccm, the working pressure is 1.0 Pa, the Al target power is 180 W, the Cr target power is 100 W, the substrate temperature is 300 °C, and the deposition time is 120 min; In an acetone solution containing ...

Embodiment 3

[0037] Grind the 3Cr13 stainless steel with 600#, 800#, 1200#, 1500#, 2000# sandpaper in sequence, ultrasonically shake the polished samples with acetone and absolute ethanol for 20 minutes, dry them quickly with a hair dryer, and put them into the PVD equipment A Cr / CrAlN transition layer deposition is performed. The purity of the Cr and Al targets used in the deposition process is both 99.999%, and the target base distance is 70 mm. The process parameters for depositing the Cr layer are: the degree of vacuum is 0.7×10 –3 Pa, the Ar gas flow rate is 20 sccm, the working pressure is 0.8 Pa, the Cr target power is 100 W, and the deposition time is 10 min. The process parameters for preparing the CrAlN layer are: Ar gas flow rate is 20 sccm, N 2 The gas flow is 5 sccm, the working pressure is 1 Pa, the Al target power is 30 W, the Cr target power is 100 W, the substrate temperature is 300 °C, and the deposition time is 20 min. Then the sample of the Cr / CrAlN film transition ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a diamond film on the surface of stainless steel with Cr / CrAlN as a transition layer, which is characterized in that it comprises the following steps: S1: pretreatment of stainless steel samples: sanding the stainless steel samples with acetone and absolute ethanol Ultrasonic treatment, drying and standby; S2: Deposit Cr / CrAlN transition layer on the surface of stainless steel: put the stainless steel sample in the S1 step into the sample stage of the magnetron sputtering equipment, install the Cr and Al targets on the target holder, and place the Cr / CrAlN transition layer on the stainless steel Deposit a Cr film and a CrAlN film on the surface of the substrate to obtain a stainless steel sample containing a Cr / CrAlN transition layer; S3: Prepare a diamond film on the stainless steel surface: perform ultrasonic seeding on the stainless steel sample containing a Cr / CrAlN transition layer in step S2, and use a hot wire HFCVD is used to deposit diamond films to realize the preparation of diamond films on the surface of stainless steel containing Cr / CrAlN as a transition layer. Adopting the technology of the invention, the binding force between the diamond film and the stainless steel is high, and the film does not fall off under the action of a load of 150 kg on a Rockwell hardness tester.

Description

technical field [0001] The invention belongs to the field of diamond film preparation, and in particular relates to a method for preparing a diamond film on a stainless steel surface with Cr / CrAlN as a transition layer, which has good bonding force and high hardness of the entire film. Background technique [0002] Diamond is an allotrope of carbon and the hardest natural substance in nature. In a diamond crystal each carbon atom is sp 3 The hybrid orbital forms covalent bonds with the other 4 carbon atoms to form a regular tetrahedron. The C–C bond in diamond is very strong, all valence electrons participate in the formation of covalent bonds, and there are no free electrons. This special structure endows diamond with excellent properties, such as high strength, high hardness, and good chemical stability. properties, high thermal conductivity and good biocompatibility. Stainless steel is an important metal material with good mechanical properties and good corrosion resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C16/27C23C16/02C23C14/35C23C14/16C23C14/06
CPCC23C14/0036C23C14/0641C23C14/165C23C14/352C23C16/0272C23C16/0281C23C16/271
Inventor 李晓李传星胡晓君陈成克蒋梅燕刘成吕枫
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap