Plant fiber slurry as well as preparation method and application thereof

A plant fiber and slurry technology, applied in decorative arts, decorative structures, etc., can solve the problems of brittleness and brittleness, can not withstand vibration, unfavorable handling, etc., and achieve the effects of easy storage, safe raw materials, and unbreakable strength.

Inactive Publication Date: 2020-01-03
李如勇
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Clay sculpture is made of clay. Although it is easy to shape, it is brittle and fragile after molding. It cannot withstand vibration and is not conducive to moving.
At present, in the prior art, there is no method of using plant fiber and glutinous rice as raw material for clay sculpture creation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] (1) In parts by weight, crush 62 parts of wheat straw into 0.5 cm particles, soak in 40 parts of clear water, ferment for 3 days, and grind into fiber pulp; (2) Fiber pulp obtained in step (1) Carry out infrared sterilization to obtain aseptic fiber pulp; (3) in parts by weight, peel 35 parts of glutinous rice and leave the glutinous rice heart, grind it into a size of 100 mesh glutinous rice flour, sieve, add 60 parts of clear water and boil to make glutinous rice paste; (4) In parts by weight, add 1 part of bleaching agent to 100 parts of sterile fiber pulp for bleaching; (5) In parts by weight, add 45 parts of glutinous rice paste to 55 parts of sterile fiber pulp after bleaching Stir evenly with 1 part of water-soluble color paste to obtain plant fiber slurry.

[0018] Shape the skeleton with iron wire to form the skeleton of the bottle, fill and cover the skeleton with plant fiber slurry, trim the shape precisely, let it dry naturally, and paint it to get the clay ...

Embodiment 2

[0020] (1) In parts by weight, crush 60 parts of wheat straw into 0.5 cm particles, soak in 30 parts of clear water, ferment for 3 days, and grind into fiber pulp; (2) Fiber pulp obtained in step (1) Carry out infrared sterilization to obtain sterile fiber pulp; (3) in parts by weight, peel 25 parts of glutinous rice and leave the glutinous rice heart, grind it into a size of 100 mesh glutinous rice flour, sieve, add 50 parts of clear water and boil to make glutinous rice paste; (4) in parts by weight, add 1.5 parts of bleaching agent in 100 parts of sterile fiber pulp, and bleach; (5) in parts by weight, add 45 parts of sterile fiber pulp after bleaching to 55 parts of glutinous rice paste Stir evenly with 1 part of water-soluble color paste to obtain plant fiber slurry.

[0021] Shape the skeleton with iron wire to form the skeleton of the rose, fill and cover the skeleton with plant fiber slurry, trim the shape precisely, let it dry naturally, and paint it to get the clay s...

Embodiment 3

[0023] In parts by weight, 65 parts of wheat straw are crushed into 0.5 cm particles, soaked in 50 parts of clear water, fermented for 3 days, and ground into fiber pulp; (2) The fiber pulp obtained in step (1) is subjected to infrared sterilization , to obtain aseptic fiber slurry; (3) in parts by weight, 35 parts of glutinous rice peeled to stay glutinous rice heart, ground into a size of 100 mesh glutinous rice flour, sieved, add 60 parts of clear water to boil glutinous rice paste; (4) In parts by weight, 2 parts of bleaching agents are added to 100 parts of sterile fiber pulp for bleaching; (5) In parts by weight, 65 parts of sterile fiber pulp after bleaching are added to 35 parts of glutinous rice paste and 1 part of The water-soluble color paste is evenly stirred to obtain plant fiber paste.

[0024] Shape the skeleton with iron wire to form the skeleton of the rabbit, fill and cover the skeleton with plant fiber slurry, trim the shape precisely, let it dry naturally, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses plant fiber slurry as well as a preparation method and application thereof, and relates to the technical field of plant fiber slurry preparation. The preparation method comprises the following steps: (1) crushing a plant fiber raw material to form particles, putting the particles into clear water for soaking, performing fermentation, and performing grinding to form fiber slurry; (2) performing infrared sterilization on the fiber slurry obtained in the step (1) to obtain sterile fiber slurry; (3) peeling glutinous rice to obtain peeled glutinous rice, performing grindingto form glutinous rice flour, performing sieving, adding clear water, and performing boiling to form glutinous rice paste; (4) adding a bleaching agent into the sterile fiber slurry, and performing bleaching; and (5) adding the glutinous rice paste and water-soluble color paste into the bleached sterile fiber slurry, and performing uniform stirring to obtain the plant fiber slurry. The raw materials used in the plant fiber slurry are safe, environmentally friendly and low in price, the preparation method is simple, and artistic works prepared by using the plant fiber slurry do not need to bebaked after being shaped, have larger strength and are not easy to break after natural air-drying, and are easier to preserve.

Description

technical field [0001] The invention relates to the technical field of preparation of plant fiber slurry. Background technique [0002] Straw is the remaining stems and leaves of crops such as rice, wheat, and corn after they are matured and threshed. Among them, the straw of rice is often called straw, and the straw of wheat is called straw. Due to the popularization of coal, electricity and natural gas and the abundance of various industrial products in China in the past two decades, the demand for straw in rural areas has decreased, and the disposal of a large amount of straw has become a serious social problem. Although it is prohibited by law, farmers in many places still directly Burning straw in the field, causing air pollution, fire and other consequences. There is a large amount of plant fiber in the straw, which is also wasted by burning and other treatments. [0003] Clay sculpture, commonly known as "color sculpture", is an ancient and common folk art in Chines...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L99/00B44C3/04
CPCB44C3/04C08L97/02C08L99/00
Inventor 李如勇
Owner 李如勇
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com